The deposition of amorphous indium zinc oxide (IZO) thin films on glass substrates with n-type carrier concentrations between 10 14 and 3 × 10 20 cm −3 by sputtering from single targets near room temperature was investigated as a function of power and process pressure. The resistivity of the films with In/Zn of ∼0.7 could be controlled between 5 × 10 −3 and 10 4 Ω cm by varying the power during deposition. The corresponding electron mobilities were 4–18 cm 2 V −1 s −1.The surface root-mean-square roughness was <1 nm under all conditions for film thicknesses of 200 nm. Thin film transistors with 1 μm gate length were fabricated on these IZO layers, showing enhancement mode operation with good pitch-off characteristics, threshold voltage 2.5 V and a maximum transconductance of 6 mS/mm. These films look promising for transparent thin film transistor applications.