Abstract
Several series of plasticized segmented polyether urethane of linear structure which can be used as the polymer base of thermoplastic materials were synthesized. The possibility of obtaining thermoplastic segmented polyurethane ureas with a softening temperature of 100 ÷120°C when using isophorone diisocyanate as the main element for building polymer chains, and DEHS as a plasticizer was proven. The original method for the purification of aromatic amine 4,4′-methylene-bis(2-chloroaniline) used in the process of synthesizing polyurethane ureas as a chain extender was developed. The polymers obtained have a uniquely low glass transition temperature close to -100°C with a plasticizer concentration of not more than 40%. The strength of these materials is more than 10 MPa at room temperature, and it is more 40 MPa at -70°C.