γ - In 2 Se 3 thin films prepared at different annealing temperatures ranging from 100to400°C were irradiated using 90MeV Si ions with a fluence of 2×1013ions∕cm2. X-ray diffraction analysis proved that there is no considerable variation in structural properties of the films due to the swift heavy ion irradiation. However, photosensitivity and sheet resistance of the samples increased due to irradiation. It was observed that the sample, which had negative photoconductivity, exhibited positive photoconductivity, after irradiation. The negative photoconductivity was due to the combined effect of trapping of photoexcited electrons, at traps 1.42 and 1.26eV, above the valence band along with destruction of the minority carriers, created during illumination, through recombination. Photoluminescence study revealed that the emission was due to the transition to a recombination center, which was 180meV above the valence band. Optical absorption study proved that the defects present at 1.42 and 1.26eV were annealed out by the ion beam irradiation. This allowed photoexcited carriers to reach conduction band, which resulted in positive photoconductivity. Optical absorption study also revealed that the band gap of the material could be increased by ion beam irradiation. The sample prepared at 400°C had a band gap of 2eV and this increased to 2.8eV, after irradiation. The increase in optical band gap was attributed to the annihilation of localized defect bands, near the conduction and valence band edges, on irradiation. Thus, by ion beam irradiation, one could enhance photosensitivity as well as the optical band gap of γ-In2Se3, making the material suitable for applications such as window layer in solar cells.