Slag-resistant tests were performed in fired crucibles made from raw kaolin and calcined alumina powders containing 65, 72, 78 wt% Al 2O 3 and 65 wt% Al 2O 3 + 6 wt% Cr 2O 3. The crucible tests showed that a 2-mm-wide protective layer was visible between slag and non-reaction zones in the 65 wt% Al 2O 3 crucible and that no such layer appeared in the 72 and 78 wt% Al 2O 3 crucibles. Reflected light microscopy revealed that in the 65 wt% Al 2O 3 + 6 wt% Cr 2O 3 crucible the slag zone was less fluid and the reaction zone less slag penetrative and reactive, as compared with others. The expansion or the shrinkage trend of the bauxite aggregate brick bonded with raw kaolin and calcined alumina powders after more than 3 h reheating at 1500°C depends mainly on the alumina content of the bonding matrix regardless of aggregate mix grading, and previous firing temperatures for green compacts. The continuing positive reheat linear change of bauxite-based, high-alumina, torpedo ladle brick, which promotes mortar joint tightening and retards pencilling slag attack, can be obtained by the combined action of the bonding matrix containing 65 wt% Al 2O 3 and a lower temperature firing prior to services.