Facile fabrication of Alkaline treatment and tantalum composite coating on SLA surface to increase antimicrobial and biocompatibility for titanium implant

In order to achieve both antibacterial and biological activity on the SLA (sandblasted large-grit acid-etched) surface, this study utilized alkali treatment and magnetron sputtering to create a layer of AT + Ta (alkali treatment and tantalum) composite coating on the SLA surface to enhance biocompatibility and antibacterial properties. The AT + Ta coating successfully maintained the hierarchical porous structure of alkali treatment while also improving antibacterial properties. The physical and chemical properties, antibacterial properties, and biocompatibility of the AT + Ta coating were systematically investigated. The results suggest that AT + Ta coating could be an effective approach for enhancing the surface properties of SLA implant.

Evaluation of UV photofunctionalization effect on ultrastructural properties of SLA titanium disks: An in vitro study.

The success rate of dental implants diminishes over time; the lack of osseointegration and infection are the major causes of most implant failures. One of the effective methods to improve the surface properties is to irradiate ultraviolet (UV) light. This study investigated the effect of UV photofunctionalization on the ultrasuperficial properties of sandblasted, large-grit, acid-etched (SLA) titanium discs. In this in vitro study, 24 sandblasted and acid-etched titanium discs, with a lifespan of more than four weeks, were categorized into three groups (n=8): control, ultraviolet C (UVC), and ultraviolet B (UVB). Then, they were exposed to a UV light source for 48 hours at a 1-cm distance. In addition to measuring the contact angle between the liquid and the disc surface in each of the three groups, the atomic concentrations of carbon, oxygen, and nitrogen atoms were measured at three different sites on each disc. One-way ANOVA and post hoc Tukey tests were used to analyze data. The mean concentration of carbon atoms significantly differed in the control, UVC, and UVB groups (P<0.001). The mean concentrations of nitrogen atoms differed significantly between the three groups (P<0.001). However, the mean concentrations of oxygen atoms were not significantly different between the three groups. In examining the contact angle, wettability was higher in the UVC group than in the UVB group and higher in the UBV group than in the control group. Photofunctionalization with UV light significantly decreased carbon and nitrogen concentrations on the surface of titanium implants, indicating that the implant's superficial hydrocarbons were eliminated. It was observed that UVC photofunctionalization was more effective than UVB photofunctionalization in reducing superficial contamination and improving wettability.

Comparison of Osseointegration in Novel Laser-Textured and SLA Implants.

Osseointegration is defined as the direct structural and functional connection between neo-formed bone and dental implants. Among the parameters suggested to predominantly influencing the establishment of a successful osseointegration is the quality of the implant surface, which may enhance the strength and speed of this biomechanical process. The purpose of this study was to evaluate the ability of a novel laser-treated surface, compared to sandblasted, large-grit, acid-etched (SLA) surfaces, to enhance and accelerate implant integration in delayed implant placement.Methods: Thirty patients with two missing posterior teeth were enrolled in this study. Each patient received, at a randomly allocated site, an implant with a conventional SLA surface, and at a second site, an implant with laser-textured surface. A total of 60 tissue-level implants were subsequently placed. Implant stability (ISQ) was measured using resonance frequency analysis (RFA). ISQ was assessed at baseline (T0), 8 weeks (T1), and 12 weeks (T2) following implant placement. Results: There was a statistical difference in implant stability between laser-textured and SLA group at 12 weeks postoperatively. Implant stabilization showed a successful osseointegration with both surface types. Both laser and SLA surface treatments had positive impacts on implant stabilization following delayed placement. Laser-treated surfaces presented higher values of osseointegration at 3 months postoperatively.

Surface Modifications of Commercial Dental Implant Systems: An Overview.

The aim of this review was to perform a comprehensive overview of evidence pertaining to the influence of various surface modifications on the surface roughness, bone implant contact, and the success and complication rates of the implants. Modified sandblasted, large-grit, acid-etched (SLA) implants (SLActive implants) have a higher implant stability quotient compared with conventional SLA implants. Also, when compared between the implant surfaces from various manufacturers, Biomet 3i Nanotite implants were shown to have a relatively higher implant stability quotient compared to Straumann implants as well as the Biomet Osseotite implants. Only one study reports the insertion torque values as obtained by the various implant surfaces, with the findings being statistically similar for all the types, and a higher mean value for Biomet 3i Nanotite implants. Among SLA and SLActive surfaces, the latter was found to have a lower marginal bone loss, and among Astratech implants, the marginal bone loss levels were similar for Osseospeed and Tioblast surfaces. When Osseospeed, TiUnite and SLActive surfaces were compared, Osseospeed was found to have the minimum bone loss while TiUnite was found to have the highest. The bone implant contact percentages are similar and satisfactory for most of the implant surface modifications that are available currently. Upon assessing the recent literature on the survival rates for implants with various surface modifications, it was found that among Nobel Biocare implants, the survival rate was higher for TiUnite implants, compared with the turned surfaces. Surprisingly, among the Straumann implant surfaces, the survival rates were found to be higher for the SLA implants when compared to the modified SLA implants. Only one of the included studies evaluated the survival rate for Astratech implant surfaces and found a 100% survival rate for both the Osseospeed and Tioblast surface implants. Therefore, major advancements have been made in developing novel surfaces of dental implants. The numerous innovations set the stage for rehabilitating patients with high success and predictable survival rates even in challenging conditions.

Effects of Ultraviolet Treatment and Alendronate Immersion on Osseointegration of Dental Implants and Mucosal Attachment of Dental Implant Abutments.

To evaluate the effects of ultraviolet (UV) treatment and alendronate immersion on the osseointegration of dental implants and mucosal attachment of dental implant abutments using a mongrel dog model. A total of 48 sandblasted, large-grit, acid-etched (SLA) titanium dental implants and 48 machined surface healing abutments in four male mongrel dogs were prepared. Implants and healing abutments were divided into four groups (n = 12 per group). The control (CON) group did not undergo additional surface treatments. The UV group was treated with UV for 15 minutes, and the alendronate-immersed (AN) group was soaked in 10-3 M alendronate for 24 hours. The UV treatment and alendronate soaking (UVAN) group was treated with alendronate, followed by UV irradiation. All implants were placed in the mandible of mongrel dogs, and the animals were sacrificed at 4 and 8 weeks postoperatively. Bone-to-implant contact (BIC), bone density, and connective tissue attachment were measured. In cortical bone, the UV group exhibited significantly higher BIC compared to the CON and AN groups (P < .05). In contrast, the AN and UVAN groups did not have significantly higher BIC. In the trabecular bone, there was no statistical difference between the groups. No significant increase in bone density and connective tissue attachment was shown in any group. UV treatment of SLA surface implants significantly increased osseointegration in cortical bone. The alendronate immersion did not increase osseointegration, and there was no synergic effect with UV treatment. Further, UV treatment and alendronate immersion of machined healing abutments did not significantly increase connective tissue attachment.

Comparison of three-dimensional digital analyses and two-dimensional histomorphometric analyses of the bone-implant interface.

Histological analysis is considered to be the gold standard method of evaluating osseointegration around a bone-implant. However, this method requires invasive specimen preparation and is capable of representing only one plane. By comparison, micro-computed tomography (μCT) is a fast and convenient method that offers three-dimensional information but is hampered by problems related to resolution and artifacts, making it a supplementary method for osseointegration analysis. To verify the reliability of μCT for osseointegration evaluation, this animal model study compared bone-to-implant contact (BIC) ratios obtained by the gold standard histomorphometric method with those obtained by the μCT method, using a rabbit tibia implant model. A sandblasted, large-grit, acid-etched (SLA) implant and a machined surface implant were inserted into each tibia of two rabbits (giving eight implants in total). Bone-implant specimens were analyzed using μCT with a spiral scan technique (SkyScan 1275) and histological sections were prepared thereafter. Three-dimensional (3D) reconstructed μCT data and four two-dimensional (2D) μCT sections, including one section corresponding to the histologic section and three additional sections rotated 45°, 90°, and 135°, were used to calculate the BIC ratio. The Pearson’s test was used for correlation analysis at a significance level of 0.05. The histomorphometric BIC and the 2D-μCT BIC showed strong correlation (r = 0.762, P = 0.046), whereas the histomorphometric BIC and 3D-μCT BIC did not (r = -0.375, P = 0.385). However, the mean BIC value of three or four 2D-μCT sections showed a strong correlation with the 3D-μCT BIC (three sections: r = 0.781, P = 0.038; four sections: r = 0.804, P = 0.029). The results of this animal model study indicate that μCT can be used to complement the histomorphometric method in bone-implant interface analyses. With the limitations of this study, 3D-μCT analysis may even have a superior aspect in that it eliminates random variables that arise as a consequence of the selected cutting direction.

Dental implants with electrochemical nanopattern formation to increase osseointegration

An electrochemical nanopattern formation (ENF) surface treatment was developed to overcome the limitations of conventional surface treatments. This study aimed to evaluate the cytocompatibility and preclinical efficacy of the newly developed ENF surfaces in comparison to conventional surfaces. The cytocompatibility of human mesenchymal stem cells, degree of bone formation, bone-to-implant contact (BIC) ratio, and implant stability quotient (ISQ) were investigated using rabbit and beagle models. Overall, the ENF surfaces showed greater cytocompatibility than other surfaces. The ISQs of implants in rabbit tibias showed that ENF surfaces provided greater stability than other surfaces. In contrast, the ISQs of implants in beagle mandibles were similar for ENF and sandblasted large-grit acid-etched (SLA) surfaces. In the rabbit model, the degree of bone formation and BIC ratio were significantly higher for ENF surfaces than for other surfaces. However, the removal torque (RT) during implant removal was significantly higher for SLA surfaces than ENF surfaces. Thus, it was confirmed that ENF-treated dental implants can replace conventional implants, but further research is required to improve the surface roughness to increase the RT.

The Effect of Microcosm Biofilm Decontamination on Surface Topography, Chemistry, and Biocompatibility Dynamics of Implant Titanium Surfaces.

Since the inception of dental implants, a steadily increasing prevalence of peri-implantitis has been documented. Irrespective of the treatment protocol applied for the management of peri-implantitis, this biofilm-associated pathology, continues to be a clinical challenge yielding unpredictable and variable levels of resolution, and in some cases resulting in implant loss. This paper investigated the effect of microcosm biofilm in vitro decontamination on surface topography, wettability, chemistry, and biocompatibility, following decontamination protocols applied to previously infected implant titanium (Ti) surfaces, both micro-rough -Sandblasted, Large-grit, Acid-etched (SLA)-and smooth surfaces -Machined (M). Microcosm biofilms were grown on SLA and M Ti discs. These were treated with TiBrushes (TiB), combination of TiB and photodynamic therapy (PDT), combination of TiB and 0.2%CHX/1%NaClO, plus or minus Ultraviolet-C (UV-C) radiation. Surface topography was evaluated by Scanning Electron Microscopy (SEM) and Laser Surface Profilometry. Surface function was analysed through wettability analysis. Surface chemistry evaluation of the discs was performed under SEM/Energy-dispersive X-ray spectroscopy (EDX) and X-ray photoelectron spectroscopy (XPS). Biocompatibility was tested with the cytocompatibility assay using human osteoblast-like osteosarcoma cell line (MG-63) cells. Elemental analysis of the discs disclosed chemical surface alterations resulting from the different treatment modalities. Titanium, carbon, oxygen, sodium, aluminium, silver, were identified by EDX as the main components of all the discs. Based on the data drawn from this study, we have shown that following the decontamination of Ti surfaces the biomaterial surface chemistry and topography was altered. The type of treatment and Ti surface had a significant effect on cytocompatibility (p = 0.0001). Although, no treatment modality hindered the titanium surface biocompatibility, parameters such as the use of chemical agents and micro-rough surfaces had a higher cytotoxic effect in MG-63 cells. The use of smooth surfaces, and photofunctionalisation of the TiO2 layer had a beneficial effect on cytocompatibility following decontamination.

Comparison of antimicrobial effect of several decontaminating methods on contaminated Titanium discs

Decontaminating the implant surface, exposed to bacterial biofilm, is a concern in the treatment of peri-implant inflammatory disease. The aim of this study was to compare the effect of several methods on reduction of the bacterial load, colonized on the surfaces of titanium discs.In this in vivo study, seven titanium discs with Sandblasted, Large-grit, acid-etched (SLA) surface were placed in the mouth of each of ten patients with chronic periodontitis by an intra-oral maxillary splint for 24 h. In each patient, the contaminated discs, except for the negative control ones, were randomly treated by one of the six antiseptic methods including sterile normal saline, plastic curette, air polisher, hydrogen peroxide, 980 nm diode laser, and Er-YAG laser. A spectrophotometer was used to measure Optical Density (OD) in case of aerobic microorganisms. Colony-Forming Units (CFUs) were used for anaerobic bacteria. Data were analyzed through Kruskal-Wallis and Mann-Whitney Tests at a significance level of α =0.05 by SPSS software.Statistical analysis showed a significant decrease in OD of aerobic bacteria among the seven groups during a 0-24 h time interval (P < 0.001). Furthermore, these tests showed a significant difference in the CFU (P < 0.001) for anaerobic bacteria after 48 h.The results of this study showed that all of the adopted methods significantly reduced microbial colonies on the surfaces of titanium discs with SLA surface. Er: YAG laser and normal saline had the highest and the lowest effects, respectively.

Secondary stability achieved in dental implants with a calcium-coated sandblasted, large-grit, acid-etched (SLA) surface and a chemically modified SLA surface placed without mechanical engagement: A preclinical study.

To assess the osseointegration of calcium-coated (CS) and chemically modified, sandblasted, large-grit, acid-etched (MS) dental implants with a lack of primary mechanical stability. Eighteen implants in CS and MS groups each were loosely placed in the mandible of six mongrel dogs and allowed to heal for 2, 4 and 8weeks. Implant stability quotient (ISQ) and implant stability test (IST) values recorded periodically and bone-to-implant contact (BIC) and the number of Haversian canals per 1mm2 measured histologically were statistically analysed (p<.05). All CS and MS implants placed survived. Compared with immediately after installation, ISQ and IST values in both groups increased significantly to over 76 at 2weeks (p<.0083) and remained stable thereafter. BIC was significantly greater at 8weeks (61.3±13.6% in CS group; 57.6±5.9% in MS group) compared to 2 and 4weeks in both groups (p<.017). There were no significant intergroup differences in ISQ, IST or BIC at different time points. Significantly more Haversian canals were observed in group CS (6.2±1.0/mm2 ) compared with group MS at 4weeks (3.7±1.8 /mm2 ; p<.05), while intergroup difference was not significant at 8weeks. Both CS and MS implants inserted without primary stability obtained osseointegration within 2weeks, and lamellar bone adjacent to the implants was first observed at 8weeks. The formation of primary osteons was more active at 4weeks in group CS than in group MS.

Comparison of Various Time-Related Modifications of Ultraviolet Photofunctionalization on SLA-Treated Titanium Surfaces.

The purpose of this study was to compare changes in the physicochemical and biologic characteristics of titanium surfaces through short-term re-hydrophobization for 24 hours and ultraviolet (UV) re-irradiation for 24 hours. Photofunctionalization was performed with four 15-W bactericidal lamps at an intensity of 5.0 mW/cm2 (wavelength = 254 ± 20 nm) on sandblasted, large-grit, acid-etched (SLA)-treated titanium surfaces, which were stored in a sterilized sealed container for 8 weeks to allow enough biologic aging. The duration of the UV irradiation was as follows: irradiation group-UV irradiated for 24 hours; re-hydrophobization group-UV irradiated for 24 hours and then stored in an ambient sterilized medium; and re-irradiation group-UV irradiated for 24 hours followed by storing for 24 hours in an ambient sterilized medium and then UV re-irradiated for 24 hours. The surface characteristics were evaluated with field emission scanning electron microscopy, x-ray photoelectron spectroscopy (XPS), and water contact angle. Cell viability and morphology were measured using fluorescence staining. Alkaline phosphatase (ALP) assay and alizarin red S staining were performed to evaluate the differentiation of osteogenic cells and the mineralization capability. Macroroughness and superimposed microroughness were observed on the disk surfaces in all groups as typically seen on SLA surfaces. The water contact angles were measured to be 1.85, 1.48, and 1.18 degrees for the irradiation group, re-hydrophobization group, and re-irradiation group, respectively, indicating superhydrophilicity. There was no difference in the surface elemental ratio or the spectra of XPS, cell viability, or ALP activity. Although the re-irradiation group had the highest total amount of calcium deposition, there was no statistical significance. Within the limitations of the study, improved superhydrophilicity and bioactivity after UV irradiation were maintained during short-term re-hydrophobization and repeated re-irradiation without changing the topography of SLA titanium surfaces.

Mechanism of Exosomes Involved in Osteoimmunity Promoting Osseointegration Around Titanium Implants With Small-Scale Topography.

Exosomes are nanoscale extracellular vesicles. Several studies have shown that exosomes participate in intercellular communication and play a key role in osseointegration. However, it is unclear whether exosomes and their contents participate in the communication between the immune and skeletal systems in the process of osseointegration. In this study, we obtained smooth titanium disks by polishing and small-scale topography titanium disks by sandblasted large-grit acid-etched (SLA) technology combined with alkali thermal reaction. After stimulating mouse RAW264.7 cells with these two kinds of titanium disks, we co-cultured the MC3T3-E1 cells and the RAW264.7 cells, obtained and identified the exosomes derived from RAW264.7 cells, and studied the effect of the osteoimmune microenvironment and the exosomes on the osseointegration of mouse MC3T3-E1 cells. Cell counting kit-8 (CCK-8), real time quantitative PCR, western blotting, alizarin red staining, and quantitative and confocal fluorescence microscopy were used to study the effects of exosomes on MC3T3-E1 cells; RNA sequencing and correlation analysis were performed. We found that the osteoimmune microenvironment could promote the osseointegration of MC3T3-E1 cells. We successfully isolated exosomes and found that RAW264.7 cell-derived exosomes can promote osteogenic differentiation and mineralization of MC3T3-E1 cells. Through RNA sequencing and gene analysis, we found differentially expressed microRNAs that targeted the signal pathways that may be related, such as mTOR, AMPK, Wnt, etc., and thus provide a reference for the mechanism of osteoimmunue regulation of implant osseointegration. The study further elucidated the mechanism of implant osseointegration and provided new insights into the effect of exosomes on implant osseointegration, and provided reference for clinical improvement of implant osseointegration and implant success rate.

Improvement of Osseointegration by Ultraviolet and/or Simvastatin Treatment on Titanium Implants with or without Bone Graft Materials.

We evaluated and compared ultraviolet (UV) treatment and simvastatin (SIM) immersion effects on the osseointegration of sandblasted, large-grit, acid-etched (SLA) titanium dental implants at two different time points in rabbit tibias, with or without xenogenic bone graft materials. The surface alteration on simvastatin treatment titanium discs was analyzed using an infrared spectrometer. Implants were categorized into four groups according to the surface treatment type. Twelve rabbits received two implants per tibia. A tibial defect model was created using a trephine bur, with implants in contact with the bone surface and bovine bone graft materials for gap filling. The rabbits were sacrificed after 2 or 4 weeks. UV treatment or SIM immersion increased the bone-to-implant contact (BIC) on nongrafted sides, and both increased the BIC and bone area (BA) on grafted sides. The application of both treatments did not result in higher BIC or BA than a single treatment. At two different time points, BIC in the nongrafted sides did not differ significantly among the UV and/or SIM treated groups, whereas BA differed significantly. UV or SIM treatment of SLA titanium implants accelerates osseointegration in tibias with or without xenogenic bone graft materials. The combination of both treatments did not show synergy.

Clinical effect evaluation of anodized and sandblasted, large-grit, acid-etched implants within 10 years: a meta-analysis

Objective: To systematically evaluate the clinical effect of anodized implants and sandblasted, large-grit, acid-etched (SLA) implants in the recent 10 years, so as to provide a reference for the selection and evaluation of implants. Methods: The data from Pubmed, Cochrane Library, Embase, CNKI, and Wanfang Data database from January 2010 to April 2020 were searched, to find clinical studies on anodized and SLA implants. According to the inclusion and exclusion criteria, literature was strictly screened, and data was extracted. Included studies were evaluated by using the methodological index for non-randomized studies (MINORS) and were analyzed by Stata14.0. The outcome of interest was cumulative survival rate (CSR) and marginal bone loss (MBL). Heterogeneity and publication bias among included literature was evaluated comprehensively. Results: A total of 22 articles, including 6 276 anodized implants, were collected for the analysis of anodized implants. Meta-analysis of proportions showed that anodized implants CSR were 98% (95%CI: 97%-98%, P<0.05) in total, at 5 years were 98% (95%CI: 98%-99%, P<0.05), and at 10 years were 97% (95%CI: 96%-98%, P<0.05). MBL change was 1.02 mm (95%CI: 0.69-1.34, P<0.05) in total. A total of 17 articles, including 4 567 SLA implants, were collected for the analysis of SLA implants. Meta-analysis of proportions showed that SLA implants CSR were 99% (95%CI: 98%-100%, P<0.05) in total, 99% at 5 years (95%CI: 98%-100%, P<0.05), and 99% at 10 years (95%CI: 97%-100%, P<0.05). MBL change was 0.69 mm (95%CI: 0.44-0.95, P<0.05) in total. The results of the above two studies were tested for bias (P>0.05), indicating no significant publication bias. Conclusions: Meta-analysis suggested that SLA implants have higher CSR and lower MBL than anodized implants.

Surface Topography of Titanium Affects Their Osteogenic Potential through DNA Methylation.

It is widely accepted that sandblasted/large-grit/acid-etched (SLA) surfaces of titanium (Ti) have a higher osteogenic potential than machined ones. However, most studies focused on differential gene expression without elucidating the underlying mechanism for this difference. The aim of this study was to evaluate how the surface roughness of dental Ti implants affects their osteogenic potential. Mouse preosteoblast MC3T3-E1 cells were seeded on machined and SLA Ti discs. The cellular activities of the discs were analyzed using confocal laser scanning microscopy, proliferation assays, and real-time polymerase chain reaction (PCR). DNA methylation was evaluated using a methylation-specific PCR. The cell morphology was slightly different between the two types of surfaces. While cellular proliferation was slightly greater on the machined surfaces, the osteogenic response of the SLA surfaces was superior, and they showed increased alkaline phosphatase (Alp) activity and higher bone marker gene expression levels (Type I collagen, Alp, and osteocalcin). The degree of DNA methylation on the Alp gene was lower on the SLA surfaces than on the machined surfaces. DNA methyltransferase inhibitor stimulated the Alp gene expression on the machined surfaces, similar to the SLA surfaces. The superior osteogenic potential of the SLA surfaces can be attributed to a different epigenetic landscape, specifically, the DNA methylation of Alp genes. This finding offers novel insights into epigenetics to supplement genetics and raises the possibility of using epidrugs as potential therapeutic targets to enhance osteogenesis on implant surfaces.

The Role and Activation Mechanism of TAZ in Hierarchical Microgroove/Nanopore Topography-Mediated Regulation of Stem Cell Differentiation.

PurposeTo investigate the role and activation mechanism of TAZ in periodontal ligament stem cells (PDLSCs) perceiving hierarchical microgroove/nanopore topography.Materials and MethodsTitanium surface with hierarchical microgroove/nanopore topography fabricated by selective laser melting combined with alkali heat treatment (SLM-AHT) was used as experimental group, smooth titanium surface (Ti) and sandblasted, large-grit, acid-etched (SLA) titanium surface were employed as control groups. Alkaline phosphatase (ALP) activity assays, qRT-PCR, Western blotting, and immunofluorescence were carried out to evaluate the effect of SLM-AHT surface on PDLSC differentiation. Moreover, TAZ activation was investigated from the perspective of nuclear localization to transcriptional activity. TAZ knockdown PDLSCs were seeded on three titanium surfaces to detect osteogenesis- and adipogenesis-related gene expression levels. Immunofluorescence and Western blotting were employed to investigate the effect of the SLM-AHT surface on actin cytoskeletal polymerization and MAPK signaling pathway. Cytochalasin D and MAPK signaling pathway inhibitors were used to determine whether actin cytoskeletal polymerization and the MAPK signaling pathway were indispensable for TAZ activation.ResultsOur results showed that SLM-AHT surface had a greater potential to promote PDLSC osteogenic differentiation while inhibiting adipogenic differentiation than the other two groups. The nuclear localization and transcriptional activity of TAZ were strongly enhanced on the SLM-AHT surface. Moreover, after TAZ knockdown, the enhanced osteogenesis and decreased adipogenesis in SLM-AHT group could not be observed. In addition, SLM-AHT surface could promote actin cytoskeletal polymerization and upregulate p-ERK and p-p38 protein levels. After treatment with cytochalasin D and MAPK signaling pathway inhibitors, differences in the TAZ subcellular localization and transcriptional activity were no longer observed among the different titanium surfaces.ConclusionOur results demonstrated that actin cytoskeletal polymerization and MAPK signaling pathway activation triggered by SLM-AHT surface were essential for TAZ activation, which played a dominant role in SLM-AHT surface-induced stem cell fate decision.

Osteoconductive and Osteoinductive Surface Modifications of Biomaterials for Bone Regeneration: A Concise Review

The main aim of bone tissue engineering is to fabricate highly biocompatible, osteoconductive and/or osteoinductive biomaterials for tissue regeneration. Bone implants should support bone growth at the implantation site via promotion of osteoblast adhesion, proliferation, and formation of bone extracellular matrix. Moreover, a very desired feature of biomaterials for clinical applications is their osteoinductivity, which means the ability of the material to induce osteogenic differentiation of mesenchymal stem cells toward bone-building cells (osteoblasts). Nevertheless, the development of completely biocompatible biomaterials with appropriate physicochemical and mechanical properties poses a great challenge for the researchers. Thus, the current trend in the engineering of biomaterials focuses on the surface modifications to improve biological properties of bone implants. This review presents the most recent findings concerning surface modifications of biomaterials to improve their osteoconductivity and osteoinductivity. The article describes two types of surface modifications: (1) Additive and (2) subtractive, indicating biological effects of the resultant surfaces in vitro and/or in vivo. The review article summarizes known additive modifications, such as plasma treatment, magnetron sputtering, and preparation of inorganic, organic, and composite coatings on the implants. It also presents some common subtractive processes applied for surface modifications of the biomaterials (i.e., acid etching, sand blasting, grit blasting, sand-blasted large-grit acid etched (SLA), anodizing, and laser methods). In summary, the article is an excellent compendium on the surface modifications and development of advanced osteoconductive and/or osteoinductive coatings on biomaterials for bone regeneration.

Evaluating protein binding specificity of titanium surfaces through mass spectrometry-based proteomics.

To evaluate whether surface characteristics of different titanium modifications may influence the composition of the salivary pellicle on each surface by analyzing the salivary proteome through mass spectrometry-based proteomics. Titanium discs with three surfaces modifications (PT (machined titanium), SLA (sandblasted/large-grit/acid-etched), and SLActive (modified SLA)) were characterized (topography, chemistry, and energy) prior to being exposed to saliva for 2h to form a protein pellicle. The resultant protein layer was retrieved and analyzed through mass spectrometry (nLC-ESI-MS/MS) to examine the surface specificity for protein binding, while the proteome profile of each surface was classified. The proteome analysis showed that the salivary pellicle composition was more complex on rough surfaces (SLA and SLActive). Although variability in protein composition was observed between surfaces, most proteins were detected on more than one surface, indicating a limited surface specificity for protein binding. Additionally, the salivary pellicle formed on the SLActive presented a larger number of proteins associated with immune response, biological adhesion, and biomineralization. Although topography, chemistry, and energy differed between the surfaces, they were not determinant to produce a salivary pellicle with high surface specificity. Also, we showed that several salivary proteins adsorbed on Ti surfaces are involved in biological functions important to the biointegration. This study sheds light on the necessity for the development of bioactive surfaces that favors the formation of a specific protein layer that can enhance tissue response to assist the biointegration of dental implants.

Bioactive Surfaces vs. Conventional Surfaces in Titanium Dental Implants: A Comparative Systematic Review.

Animal studies and the scarce clinical trials available that have been conducted suggest that bioactive surfaces on dental implants could improve the osseointegration of such implants. The purpose of this systematic review was to compare the effectiveness of osseointegration of titanium (Ti) dental implants using bioactive surfaces with that of Ti implants using conventional surfaces such as sandblasted large-grit acid-etched (SLA) or similar surfaces. Applying the guidelines of the Preferred Reporting Items for Systematic Reviews and Meta-analyses (PRISMA) statement, the MEDLINE, PubMed Central and Web of Science databases were searched for scientific articles in April 2020. The keywords used were “dental implants”, “bioactive surfaces”, “biofunctionalized surfaces”, and “osseointegration”, according to the question: “Do bioactive dental implant surfaces have greater osseointegration capacity compared with conventional implant surfaces?” Risk of bias was assessed using the Cochrane Collaboration tool. 128 studies were identified, of which only 30 met the inclusion criteria: 3 clinical trials and 27 animal studies. The average STROBE (STrengthening the Reporting of OBservational studies in Epidemiology) and ARRIVE (Animal Research: Reporting of In Vivo Experiments) scores were 15.13 ± 2.08 and 17.7±1.4, respectively. Implant stability quotient (ISQ) was reported in 3 studies; removal torque test (RTT)—in 1 study; intraoral periapical X-ray and microcomputed tomography radiological evaluation (RE)—in 4 studies; shear force (SF)—in 1 study; bone-to-implant contact (BIC)—in 12 studies; and BIC and bone area (BA) jointly—in 5 studies. All animal studies reported better bone-to-implant contact surface for bioactive surfaces as compared to control implants with a statistical significance of p < 0.05. Regarding the bioactive surfaces investigated, the best results were yielded by the one where mechanical and chemical treatment methods of the Ti surfaces were combined. Hydroxyapatite (HA) and calcium–phosphate (Ca–Ph) were the most frequently used bioactive surfaces. According to the results of this systematic review, certain bioactive surfaces have a positive effect on osseointegration, although certain coating biomolecules seem to influence early peri-implant bone formation. Further and more in-depth research in this field is required to reduce the time needed for osseointegration of dental implants.

A laminin-211-derived bioactive peptide promotes the osseointegration of a sandblasted, large-grit, acid-etched titanium implant.

Early implant loading is very important for reducing the duration of missing teeth in human patients. The laminin-derived peptide, DLTIDDSYWYRI motif (Ln2-P3), accelerates bone healing. Therefore, to investigate the hypothesis that Ln2-P3 increases the bone response to sandblasted, large-grit, acid-etched (SLA) titanium implants, the effect of the Ln2-P3 peptide on the osseointegration of SLA titanium implants was evaluated in vitro and in vivo. Human osteoblast-like cells were cultured on untreated, scrambled peptide (SP)-treated, and Ln2-P3-treated SLA titanium discs, and the cellular responses of these cells were evaluated. The Ln2-P3 treatment augmented osteoblast attachment and spreading, alkaline phosphatase activity, and the expression of osteogenic marker genes. Furthermore, the untreated and Ln2-P3-treated SLA titanium implants were inserted into the tibiae of rabbits for 9 and 11 days. Compared with the untreated implants, the Ln2-P3-treated implants showed a significantly higher bone-to-implant contact ratio at Day 9 after implantation and an increased bone area. The Ln2-P3 treatment of the SLA titanium implant surface augmented osteoblastic activity and accelerated peri-implant bone formation at the bone-implant interface. Overall, these results indicated that compared with the SLA titanium surface alone, the Ln2-P3 peptide-treated SLA titanium surface enhances initial osseointegration, thereby facilitating earlier implant loading.