Porous Ti6Al4V Scaffolds Research Articles

Osteogenesis of 3D printed porous Ti6Al4V implants with different pore sizes.

Selective laser melting (SLM) is one of the three-dimensional (3D) printing techniques that manufacturing versatile porous scaffolds with precise architectures for potential orthopedic application. To understand how the pore sizes of porous Ti6Al4V scaffolds affect their biological performances, we designed and fabricated porous Ti6Al4V implants with straightforward pore dimensions (500, 700, and 900 µm) via SLM, termed as p500, p700, and p900 respectively. The morphological characteristics of Ti6Al4V scaffolds were assessed showing that the actual pore sizes of these scaffolds were 401 ± 26 µm, 607 ± 24 µm, 801 ± 33 µm, respectively. The mechanical properties of Ti6Al4V scaffolds were also evaluated showing that they were comparable to that of bone tissues. Meanwhile, the effect of pore size on biological responses was systematically investigated in vitro and in vivo. It was verified that 3D printing technique was able to fabricate porous Ti6Al4V implants with proper mechanical properties analogous to human bone. The in vitro results revealed that scaffolds with appropriate pore dimension were conducive to cell adhesion, proliferation and early differentiation. Furthermore, the porous Ti6Al4V scaffolds were implanted into the rabbit femur to investigate bone regeneration performance, the in vivo experiment showed the p700 sample was in favor of bone ingrowth into implant pores and bone-implant fixation stability. Taken together, the biological performance of p700 group with actual pore size of about 600 µm was superior to other two groups. The obtained findings provide basis to individually design and fabricate suitable porous Ti6Al4V with specific geometries for orthopedic application.

Osseointegration assessment of extrusion printed Ti6Al4V scaffold towards accelerated skeletal defect healing via tissue in-growth

3D printing is an additive manufacturing technique to produce metallic components with controlled pore size, total porosity and pore-connectivity. Selective laser melting (SLM), the most widely used technique to develop such kind of metallic components for bone graft applications, requires a controlled atmosphere for reactive metal powder processing. In this study, a simple extrusion-based 3D printing technique is developed to produce porous Ti6Al4V scaffold under ambient environmental condition to overcome the existing limitation. 3D printed Ti6Al4V scaffold with pore size ~500µm and total porosity ~58% was achieved. The scaffold exhibited ~13% shrinkage after sintering, resulting in strut diameter ~348µm with persistent inter-particle voids. The compressive strength and elastic modulus values are 39.58±4.56MPa and 450±7.21MPa comparable to cancellous bone mechanical properties. In vitro cytocompatibility assessment of scaffold using mesenchymal stem cells revealed extensive cellular coverage on scaffold surface and differentiation towards bone cell lineage. In vivo studies by scaffold implantation in rabbit femur for four weeks and eight weeks exhibited the scaffold's ability to promote osseointegration and tissue integration through bone in-growth evidenced by micro-CT. Therefore, using this simple and cost-effective technique, bone graft substitute scaffolds could be developed as implant for load bearing applications.

Novel Bio-functional Magnesium Coating on Porous Ti6Al4V Orthopaedic Implants: In vitro and In vivo Study

Titanium and its alloys with various porous structures are one of the most important metals used in orthopaedic implants due to favourable properties as replacement for hard tissues. However, surface modification is critical to improve the osteointegration of titanium and its alloys. In this study, a bioactive magnesium coating was successfully fabricated on porous Ti6Al4V by means of arc ion plating, which was proved with fine grain size and high film/substrate adhesion. The surface composition and morphology were characterized by X-ray diffraction and SEM equipped with energy dispersive spectroscopy. Furthermore, the in vitro study of cytotoxicity and proliferation of MC3T3-E1 cells showed that magnesium coated porous Ti6Al4V had suitable degradation and biocompatibility. Moreover, the in vivo studies including fluorescent labelling, micro-computed tomography analysis scan and Van-Gieson staining of histological sections indicated that magnesium coated porous Ti6Al4V could significantly promote bone regeneration in rabbit femoral condylar defects after implantation for 4 and 8 weeks, and has better osteogenesis and osteointegration than the bare porous Ti6Al4V. Therefore, it is expected that this bioactive magnesium coating on porous Ti6Al4V scaffolds with improved osteointegration and osteogenesis functions can be used for orthopedic applications.

Incorporating simvastatin/poloxamer 407 hydrogel into 3D-printed porous Ti6Al4V scaffolds for the promotion of angiogenesis, osseointegration and bone ingrowth

Three-dimensional porous titanium alloys printed via electron beam melting have low stiffness similar to that of cortical bone and are promising scaffolds for orthopedic applications. However, the bio-inert nature of titanium alloy is poorly compatible with bone ingrowth. We previously observed that simvastatin/poloxamer 407 thermosensitive hydrogel induces endogenous angiogenic/osteogenic growth factors and promotes angiogenesis and osteogenesis, but the mechanical properties of this hydrogel are poor. The purpose of this study was to construct 3D-printed porous titanium scaffolds (pTi scaffolds) filled with simvastatin/hydrogel and evaluate the effects of this composite on osseointegration, bone ingrowth and neovascularization using a tibial defect rabbit model. Four and eight weeks after implantation, the bone volume, bone mineral density, mineral apposition rate, and push-in maximum force of the pTi scaffolds filled with simvastatin/hydrogel were significantly higher than those without simvastatin (p < 0.05). Moreover, filling with simvastatin/hydrogel significantly enhanced vascularization in and around the pTi scaffolds, and a significant correlation was observed between the volume of new bone and neovascularization (p < 0.01). In conclusion, incorporating simvastatin/poloxamer 407 hydrogel into pTi scaffolds significantly improves neovascularization, osseointegration and bone ingrowth.

In vitro and in vivo study of additive manufactured porous Ti6Al4V scaffolds for repairing bone defects.

Metallic implants with a low effective modulus can provide early load-bearing and reduce stress shielding, which is favorable for increasing in vivo life-span. In this research, porous Ti6Al4V scaffolds with three pore sizes (300~400, 400~500, and 500~700 μm) were manufactured by Electron Beam Melting, with an elastic modulus range of 3.7 to 1.7 GPa. Cytocompatibility in vitro and osseointegration ability in vivo of scaffolds were assessed. hBMSCs numbers increased on all porous scaffolds over time. The group with intended pore sizes of 300 to 400 μm was significantly higher than that of the other two porous scaffolds at days 5 and 7. This group also had higher ALP activity at day 7 in osteogenic differentiation experiment. The scaffold with pore size of 300 to 400 μm was implanted into a 30-mm segmental defect of goat metatarsus. In vivo evaluations indicated that the depth of bone ingrowth increased over time and no implant dislocation occurred during the experiment. Based on its better cytocompatibility and favorable bone ingrowth, the present data showed the capability of the additive manufactured porous Ti6Al4V scaffold with an intended pore size of 300 to 400 μm for large segmental bone defects.

Multi-scale porous Ti6Al4V scaffolds with enhanced strength and biocompatibility formed via dynamic freeze-casting coupled with micro-arc oxidation

Titanium implants with sufficient mechanical properties and biocompatibility have been in demand for rapid healing and successful surgery. Herein, porous Ti6Al4V scaffolds with multi-scale porosity were obtained by coupling dynamic freeze-casting with micro-arc oxidation (MAO). The fabricated scaffolds exhibited tailored pore sizes and interconnected pores. Compressive strength and elastic modulus were controlled by adjusting the porosity of the scaffolds. MAO was successfully conducted on the porous Ti6Al4V scaffolds by inhibiting gaseous emission from the electrolysis of water with the addition of ethanol to the MAO solution. Moreover, the biological response of preosteoblasts on the multi-scale porous Ti6Al4V scaffolds was enhanced owing to their porous topography and modified chemical composition.

Porous Ti6Al4V scaffolds for dental implants: Microstructure, mechanical, and corrosion behavior

Titanium and its alloys are known as one of the most significant metallic materials used in the orthopedic and dental implants due to their excellent mechanical properties, corrosion resistance, and biocompatibility. One of the main issues in dental implant is the fabrication of the biomaterials that have early and sufficiently strong bonding with the surrounding bone. In the present study, porous Ti6Al4V scaffolds were synthesized using the powder metallurgy with various amounts of magnesium. The specimens were sintered at 950 ℃, close to magnesium vaporization point, because of the remaining magnesium in the scaffolds. The microstructure and mechanical properties of the specimens were investigated. Electrochemical characterization was carried out to indicate the effect of porosity on corrosion resistance. This investigation showed that the porous Ti6Al4V scaffolds containing 5–10 volume percent of magnesium with 28–31% porosity as a semi-degradable implant could be an advanced alternative for clinical application under load-bearing conditions such as dental implants which require two factors of strength and osteointegration.

Tailored Surface Treatment of 3D Printed Porous Ti6Al4V by Microarc Oxidation for Enhanced Osseointegration via Optimized Bone In-Growth Patterns and Interlocked Bone/Implant Interface.

3D printed porous titanium (Ti) holds enormous potential for load-bearing orthopedic applications. Although the 3D printing technique has good control over the macro-sturctures of porous Ti, the surface properties that affect tissue response are beyond its control, adding the need for tailored surface treatment to improve its osseointegration capacity. Here, the one step microarc oxidation (MAO) process was applied to a 3D printed porous Ti6Al4V (Ti64) scaffold to endow the scaffold with a homogeneous layer of microporous TiO2 and significant amounts of amorphous calcium-phosphate. Following the treatment, the porous Ti64 scaffolds exhibited a drastically improved apatite forming ability, cyto-compatibility, and alkaline phosphatase activity. In vivo test in a rabbit model showed that the bone in-growth at the untreated scaffold was in a pattern of distance osteogenesis by which bone formed only at the periphery of the scaffold. In contrast, the bone in-growth at the MAO-treated scaffold exhibited a pattern of contact osteogenesis by which bone formed in situ on the entire surface of the scaffold. This pattern of bone in-growth significantly increased bone formation both in and around the scaffold possibly through enhancement of bone formation and disruption of bone remodeling. Moreover, the implant surface of the MAO-treated scaffold interlocked with the bone tissues through the fabricated microporous topographies to generate a stronger bone/implant interface. The increased osteoinetegration strength was further proven by a push out test. MAO exhibits a high efficiency in the enhancement of osteointegration of porous Ti64 via optimizing the patterns of bone in-growth and bone/implant interlocking. Therefore, post-treatment of 3D printed porous Ti64 with MAO technology might open up several possibilities for the development of bioactive customized implants in orthopedic applications.

Hierarchical Micropore/Nanorod Apatite Hybrids In-Situ Grown from 3-D Printed Macroporous Ti6Al4V Implants with Improved Bioactivity and Osseointegration

The advent of three-dimensional (3-D) printed technique provides great possibility in the fabrication of customized porous titanium (Ti) implant. However, the bioinert property of the printed Ti poses an outstanding problem. Hybrid micro-arc oxidation and hydrothermal (MAO–HT) treatment on porous metals is able to produce multi-scaled hierarchical orthopedic implant, showing great potential for surface modification of 3-D printed implant. In this study, cylindrical porous Ti6Al4V (Ti64) scaffolds with pore size of 640 µm, porosity of 73% were 3-D printed by electron beam melting process, and their surfaces were left untreated or treated by a combined MAO–HT procedure. In vitro bioactivity was tested by immersion in simulated body fluid for different time points. Then, 12 scaffolds in each group were implanted into the femoral condyles of New Zealand rabbit for 8 weeks. Osseointegration was evaluated by qualitative and quantitative histological analysis, and the bone ingrowth features were probed by sequential fluorescent labeling at 3 and 6 weeks post-surgery. Following the MAO–HT treatment, the porous Ti64 scaffold was endowed with multi-scaled micro/nano-topographies and high amounts of CaP on its surface. The treated scaffold exhibited drastically enhanced apatite forming ability compared with the untreated one. In vivo test revealed significantly that a higher amount of bone ingrowth and bone implant contact at the treated scaffold. The 2 types of scaffolds had different patterns of bone ingrowth: the treated scaffold exhibited a pattern of contact osteogenesis, by which bone formed directly on the treated implant surface, whereas bone formed distal to the implant surface of the untreated scaffold. MAO–HT treatment can significantly enhance the in vitro apatite-inducing ability and in vivo osseointegration capacity of 3-D porous Ti64 scaffold and may provide as a viable approach for the fabrication of bioactive 3-D printed porous implant for orthopedic applications.

Improved bone formation and ingrowth for additively manufactured porous Ti6Al4V bone implants with strontium laden nanotube array coating

The porous Ti6Al4V scaffolds with strontium laded nanotube arrays exhibited enhanced bone formation and ingrowth abilities.

Additive manufactured Ti6Al4V scaffolds with the RF- magnetron sputter deposited hydroxyapatite coating

Present paper reports on the results of surface modification of the additively manufactured porous Ti6Al4V scaffolds. Radio frequency (RF) magnetron sputtering was used to modify the surface of the alloy via deposition of the biocompatible hydroxyapatite (HA) coating. The surface morphology, chemical and phase composition of the HA-coated alloy were studied. It was revealed that RF magnetron sputtering allows preparing a homogeneous HA coating onto the entire surface of scaffolds.

Electrophoretic deposition of hydroxyapatite and hydroxyapatite–alginate on rapid prototyped 3D Ti6Al4V scaffolds

The advantage of using bioceramic particles coated on porous three-dimensional structures is still unexplored in the purpose of improving the osteoinduction of hybrid metallic scaffold implants in vivo. In this study, we evaluate electrophoretic deposition (EPD) to coat porous Ti6Al4V scaffolds with hydroxyapatite (HA). Scaffolds were shaped in different open structures with a horizontal shift in fiber stacking. They were produced using three-dimensional fiber deposition method and were coated by EPD with HA powder (d10 = 1.7, d50 = 5.7 and d90 = 18 µm) suspended in ethanol or butanol at different concentration, DC voltage, and time. A composite HA–alginate was also used to coat the scaffolds. Alginate was used as a binder, and the coating properties (homogeneity, thickness, cracks, continuity, etc.) were compared to coatings obtained from pure HA suspensions. Voltage and time of deposition effects were studied between 10 and 140 V and 10 and 120 s, respectively. Coating thickness and density with respect to the depth of the porous structure were studied by observing cross sections using scanning electron microscopy and image processing analysis. HA–alginate combination resulted in a homogeneous and deeper dense layer of HA. This work also points to the characteristics of HA–alginate composite as a superior alternative to pure HA coating which needs an appropriate thermal treatment for adequate substrate adhesion.

Enhanced angiogenesis and osteogenesis in critical bone defects by the controlled release of BMP-2 and VEGF: implantation of electron beam melting-fabricated porous Ti6Al4V scaffolds incorporating growth factor-doped fibrin glue

Electron beam melting (EBM)-fabricated porous titanium implants possessing low elastic moduli and tailored structures are promising biomaterials for orthopedic applications. However, the bio-inert nature of porous titanium makes reinforcement with growth factors (GFs) a promising method to enhance implant in vivo performance. Bone-morphogenic protein-2 (BMP-2) and vascular endothelial growth factor (VEGF) are key factors of angiogenesis and osteogenesis. Therefore, the present study is aimed at evaluating EBM-fabricated porous titanium implants incorporating GF-doped fibrin glue (FG) as composite scaffolds providing GFs for improvement of angiogenesis and osteogenesis in rabbit femoral condyle defects. BMP-2 and VEGF were added into the constituent compounds of FG, and then this GF-doped FG was subsequently injected into the porous scaffolds. In five groups of implants, angiogenesis and osteogenesis were evaluated at 4 weeks post-implantation using Microfil perfusion and histological analysis: eTi (empty scaffolds), cTi (containing undoped FG), BMP/cTi (containing 50 μg rhBMP-2), VEGF/cTi (containing 0.5 μg VEGF) and Dual/cTi (containing 50 μg rhBMP-2 and 0.5 μg VEGF). The results demonstrate that these composite implants are biocompatible and provide the desired gradual release of the bioactive growth factors. Incorporation of GF delivery, whether a single factor or dual factors, significantly enhanced both angiogenesis and osteogenesis inside the porous scaffolds. However, the synergistic effect of the dual factors combination was observable on angiogenesis but absent on osteogenesis. In conclusion, fibrin glue is a biocompatible material that could be employed as a delivery vehicle in EBM-fabricated porous titanium for controlled release of BMP-2 and VEGF. Application of this method for loading a porous titanium scaffold to incorporate growth factors is a convenient and promising strategy for improving osteogenesis of critical-sized bone defects.

A novel cytocompatible, hierarchical porous Ti6Al4V scaffold with immobilized silver nanoparticles

Owing to their mechanical properties and bioinertness titanium alloys remain the preferred load-bearing implant material in orthopedics. However, unsatisfactory osteointegration and risks of infection are the two major problems. Herein, Ti6Al4V prostheses with 3D hierarchical (macro/micro-nano) porosity were constructed by combining the state-of-art electron beam melting (EBM) additive manufacturing (AM) process with a traditional micro-arc oxidization (MAO) technique for enhanced integration with bone tissues, and as a measure to improve their antimicrobial properties, releasable silver nanoparticles (AgNPs) were homogeneously immobilized on the multi-scaled porous surfaces via a mussel-inspired strategy. The cytocompatibility of the engineered scaffolds (EBM–MAO/Ag) outperformed the untreated, due to synergistic benefits from micro/nano-porous topography and adhesive chemical composition.

Improving osteointegration and osteogenesis of three-dimensional porous Ti6Al4V scaffolds by polydopamine-assisted biomimetic hydroxyapatite coating.

Titanium alloys with various porous structures can be fabricated by advanced additive manufacturing techniques, which are attractive for use as scaffolds for bone defect repair. However, modification of the scaffold surfaces, particularly inner surfaces, is critical to improve the osteointegration of these scaffolds. In this study, a biomimetic approach was employed to construct polydopamine-assisted hydroxyapatite coating (HA/pDA) onto porous Ti6Al4V scaffolds fabricated by the electron beam melting method. The surface modification was characterized with the field emission scanning electron microscopy, energy dispersive spectroscopy, water contact angle measurement, and confocal laser scanning microscopy. Attachment and proliferation of MC3T3-E1 cells on the scaffold surface were significantly enhanced by the HA/pDA coating compared to the unmodified surfaces. Additionally, MC3T3-E1 cells grown on the HA/pDA-coated Ti6Al4V scaffolds displayed significantly higher expression of runt-related transcription factor-2, alkaline phosphatase, osteocalcin, osteopontin, and collagen type-1 compared with bare Ti6Al4V scaffolds after culture for 14 days. Moreover, microcomputed tomography analysis and Van-Gieson staining of histological sections showed that HA/pDA coating on surfaces of porous Ti6Al4V scaffolds enhanced osteointegration and significantly promoted bone regeneration after implantation in rabbit femoral condylar defects for 4 and 12 weeks. Therefore, this study provides an alternative to biofunctionalized porous Ti6Al4V scaffolds with improved osteointegration and osteogenesis functions for orthopedic applications.

Comparative Analysis of the Oxygen Supply and Viability of Human Osteoblasts in Three-Dimensional Titanium Scaffolds Produced by Laser-Beam or Electron-Beam Melting.

Synthetic materials for bone replacement must ensure a sufficient mechanical stability and an adequate cell proliferation within the structures. Hereby, titanium materials are suitable for producing patient-individual porous bone scaffolds by using generative techniques. In this in vitro study, the viability of human osteoblasts was investigated in porous 3D Ti6Al4V scaffolds, which were produced by electron-beam (EBM) or laser-beam melting (LBM). For each examination, two cylindrical scaffolds (30 mm × 10 mm in size, 700 µm × 700 µm macropores) were placed on each other and seeded with cells. The oxygen consumption and the acidification in the center of the structures were investigated by means of microsensors. Additionally, the synthesis of pro-collagen type 1 was analyzed. On the LBM titanium scaffolds, vital bone cells were detected in the center and in the periphery after 8 days of cultivation. In the EBM titanium constructs, however, vital cells were only visible in the center. During the cultivation period, the cells increasingly produced procollagen type 1 in both scaffolds. In comparison to the periphery, the oxygen content in the center of the scaffolds slightly decreased. Furthermore, a slight acidification of the medium was detectable. Compared to LBM, the EBM titanium scaffolds showed a less favorable behavior with regard to cell seeding.

Tantalum coating on porous Ti6Al4V scaffold using chemical vapor deposition and preliminary biological evaluation

Porous tantalum (Ta), produced via chemical vapor deposition (CVD) of commercially pure Ta onto a vitreous carbon, is currently available for use in orthopedic applications. However, the relatively high manufacturing cost and the incapability to produce customized implant using medical image data have limited its application to gain widespread acceptance. In this study, Ta film was deposited on porous Ti6Al4V scaffolds using CVD technique. Digital microscopy and scanning electron microscopy indicated that the Ta coating evenly covered the entire scaffold structure. X-ray diffraction analysis showed that the coating consisted of α and β phases of Ta. Goat mesenchymal stem cells were seeded and cultured on the Ti6Al4V scaffolds with and without coating. The tetrazolium-based colorimetric assay exhibited better cell adhesion and proliferation on Ta-coated scaffolds compared with uncoated scaffolds. The porous scaffolds were subsequently implanted in goats for 12weeks. Histological analysis revealed similar bone formation around the periphery of the coated and uncoated implants, but bone ingrowth is better within the Ta-coated scaffolds. To demonstrate the ability of producing custom implant for clinical applications via this technology, we designed and fabricated a porous Ti6Al4V scaffold with segmental mandibular shape derived from patient computerized tomography data.

Porous Ti6Al4V Scaffold Directly Fabricated by Sintering: Preparation and In Vivo Experiment

The interface between the implant and host bone plays a key role in maintaining primary and long‐term stability of the implants. Surface modification of implant can enhance bone ingrowth and increase bone formation to create firm osseointegration between the implant and host bone and reduce the risk of implant losing. This paper mainly focuses on the fabricating of 3‐dimensiona interconnected porous titanium by sintering of Ti6Al4V powders, which could be processed to the surface of the implant shaft and was integrated with bone morphogenetic proteins (BMPs). The structure and mechanical property of porous Ti6Al4V was observed and tested. Implant shaft with surface of porous titanium was implanted into the femoral medullary cavity of dog after combining with BMPs. The results showed that the structure and elastic modulus of 3D interconnected porous titanium was similar to cancellous bone; porous titanium combined with BMP was found to have large amount of fibrous tissue with fibroblastic cells; bone formation was significantly greater in 6 weeks postoperatively than in 3 weeks after operation. Porous titanium fabricated by powders sintering and combined with BMPs could induce tissue formation and increase bone formation to create firm osseointegration between the implant and host bone.

Ectopic bone formation by 3D porous calcium phosphate-Ti6Al4V hybrids produced by perfusion electrodeposition

Successful clinical repair of non-healing skeletal defects requires the use of bone substitutes with robust bone inductivity and excellent biomechanical stability. Thus, three-dimensionally functionalised porous calcium phosphate-Ti6Al4V (CaP–Ti) hybrids were produced by perfusion electrodeposition, and the in vitro and in vivo biological performances were evaluated using human periosteum derived cells (hPDCs). By applying various current densities at the optimised deposition conditions, CaP coatings with sub-micrometer to nano-scale porous crystalline structures and different ion dissolution kinetics were deposited on the porous Ti6Al4V scaffolds. These distinctive physicochemical properties caused a significant impact on in vitro proliferation, osteogenic differentiation, and matrix mineralisation of hPDCs. This includes a potential role of hPDCs in mediating osteoclastogenesis for the resorption of CaP coatings, as indicated by a significant down-regulation of osteoprotegerin (OPG) gene expression and by the histological observation of abundant multi-nucleated giant cells near to the coatings. By subcutaneous implantation, the produced hybrids induced ectopic bone formation, which was highly dependent on the physicochemical properties of the CaP coating (including the Ca2+ dissolution kinetics and coating surface topography), in a cell density-dependent manner. This study provided further insight on stem cell-CaP biomaterial interactions, and the feasibility to produced bone reparative units that are predictively osteoinductive in vivo by perfusion electrodeposition technology.

Multi-Level Factorial Analysis of Ca2+/Pi Supplementation as Bio-Instructive Media for In Vitro Biomimetic Engineering of Three-Dimensional Osteogenic Hybrids

We report on the in vitro use of Ca(2+)/P(i) supplementation as a bio-instructive medium to drive human periosteum-derived cells (hPDCs) toward osteogenic differentiation on three-dimensional (3D) porous Ti6Al4V scaffolds. Through a multilevel factorial analysis, we have systematically investigated the biological effect and interactions of Ca(2+) or P(i) supplementation in three selected media preparations (i.e., basic growth medium, osteogenic medium [OM], and osteogenic medium without β-glycerophosphate [OM(-)]) and have identified specific conditions which induce proliferation and significant osteogenic differentiation of two-dimensional (2D) hPDC cultures. These findings were translated from 2D to 3D cultures conditions to instruct hPDCs to populate porous Ti6Al4V scaffolds and to differentiate into the osteoblast lineage with collagenous matrix production and subsequent matrix mineralization on the 3D structures. These osteogenic hybrids may potentially serve as a clinically relevant customizable bone reparative unit, providing a biomimetic template to more effectively mediate in vivo bone regeneration.