Tungsten carbides are primarily used as cutting tools and abrasive materials in the form of composites with a binder metal, such as Co or Ni. However, these binder phases have inferior chemical characteristics compared to the carbide phase and the high cost of Ni or Co. Therefore, low corrosion resistance of the WC–Ni and WC–Co cermets has generated interest in recent years for alternative binder phases. In this study, TiAl3 was used as a novel binder and consolidated by the pulsed current activated sintering (PCAS) method. Highly dense WC–TiAl3 with a relative density of up to 99% was obtained within 2min by PCAS under a pressure of 80MPa. The method was found to enable not only the rapid densification but also the inhibition of grain growth preserving the nano-scale microstructure. The average grain sizes of the sintered WC and WC–TiAl3 were lower than 100nm. The addition of TiAl3 to WC enhanced the toughness without great decrease of hardness due to crack deflection and decrease of grain size.