Abstract
Nanostructured WC–Co and WC–Co–Al coatings, with about 300-μm as-deposited coating thickness, were deposited by high velocity oxy-fuel (HVOF) spraying. Agglomerated nanostructured cermet powders produced by the Mechanomade® process was used for HVOF spraying. Dense and well-adherent coatings with crystal sizes below 30nm were deposited on stainless steel 304 substrate. Porosity was less than 5% and the bond strength with the substrate was around 60MPa. Experimental data on friction, wear, and abrasion resistance revealed that nanostructured WC–Co based coatings containing some Al as alloying element, exhibit improved tribological characteristics in comparison to nanostructured and micron-sized WC–Co coatings. This was attributed to a carbide particle distribution within the coating revealed by SEM, the absence of brittle W2C-like phases revealed by XRD, and the presence of Al at particle/matrix boundaries revealed by TEM.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.