Mesio-occlusal-distal Cavities Research Articles

Comparative estimation of fracture resistance of teeth restored with new fiber impregnated composite, short fiber composite, and nanohybrid composite – An in-vitro study

INTRODUCTION. Composite resins, used in restorative dentistry, offer enhanced esthetic and mechanical qualities. Nevertheless, the significant issue of volumetric shrinkage during polymerization remains a concern. Shrinkage-induced stress has the potential to cause marginal defects and enamel and cuspal fractures, especially in high stress-bearing areas. The present study aimed at assessing and comparing the fracture resistance and fracture patterns of teeth restored with new impregnated cubical composite, short fiber reinforced composite, and nanohybrid composite in mesio-occlusal-distal (MOD) cavities.MATERIALS AND METHODS. This was an in-vitro study comprising 45 extracted premolars cleaned and mounted in resin blocks. The MOD cavities were prepared in all the samples and were divided into three groups; Group I samples restored using ESPE Filtek Z350 XT restorative composite syringeTM, Group II using GC EverX posterior compositeTM (4mm), and Group III using Fibrafill cube S. Restorations were finished and polished.RESULTS. The mean fracture resistance was 844.5±264.8, 1249.7±518.3, and 1240.8±453.3 in Group I, II, and III, respectively. Group II and III fracture resistance was comparable (p=1.00) but higher than Group I (p=0.03 with Group II, p = 0.04 with Group III). No significant difference was present in the favourable and nonfavourable fracture patterns between the three groups (p=0.108).CONCLUSIONS. Short fiber and cubic fiber integrated composites performed similarly in terms of fracture resistance resulting in favourable fracture, however better over conventional nanohybrid composites.

Finite Element Analysis and Clinical Applications of Transverse Post for the Rehabilitation of Endodontically Treated Teeth.

Introduction The preservation of tooth structure during cavity preparation is crucial for maintaining tooth strength and longevity of restorations. The biomechanical behavior of teeth, especially those with mesio-occlusal-distal (MOD) cavity preparations, is significantly affected by the extent of cavity preparation and the type of restorative treatment employed. The aim of the current study was to evaluate and analyze the stress distribution seen in the mandibular molar with MOD cavity when restored with transverse post, using finite element analysis (FEA). Materials and methodology FEA was utilized to evaluate stress distribution in an endodontically treated mandibular first molar with MOD cavity preparation, restored using a transverse post and composite restoration. Three-dimensional models incorporating the tooth and the surrounding structures, along with the transverse post and composite restoration, were constructed based on known biomechanical properties. After meshing the models, loads were defined on the buccal and lingual cusps with a constant value of 600N and at an angle of 45 degrees. Preprocessing involved model preparation followed by postprocessing to obtain results representing the degree and type of stress distribution. Results FEA simulations revealed the distribution of stress within the tooth structure under functional occlusal forces. The transverse post system effectively reinforced the tooth by deflecting incident forces and providing uniform stress distribution. von Mises stresses were analyzed to assess the likelihood of material failure. The distribution of the stress in the restored tooth model was comparable to that seen in the intact model. Conclusion Transverse postalong with composite restoration provides a conservative and cost-effective alternative to fullcoverage crowns while providing a functional and aesthetic outcome. Further research and clinical studies are warranted to validate these findings and optimize the clinical application of transverse post systems in restorative dentistry.

Co-Influence of Restoration Bonding and Inlay Cavity Design on Fracture Load of Restored Tooth.

The aim of this study was to investigate the co-influence of indirect mesio- occlusal-distal (MOD) cavity geometry and inlay restoration bonding on quasi-static fracture load of the restored tooth. Forty-eight intact human molar teeth were selected and prepared for standardized edge-shaped or round-shaped MOD cavities. The resin composite (Cerasmart, GC) inlays were bonded with the state-of-the-art inlay bonding protocol or with intentionally deteriorated bonding using n-hexane-wax solution for preconditioning. Restored teeth were loaded along the long axis of the tooth. Ultimate fracture load was recorded, and the type of fracture was visually determined and classified. Statistical analysis of load values was performed by Kruskal-Wallis test. Round-shaped cavity design with bonded restoration presented the highest fracture load (1658N). Bonding had significant influence on the fracture load of roundshaped cavity design (p=0.0003), whereas cavity design had no influence when the bonding was deteriorated (p=0.8075). In the case of deteriorated bonding, either the inlay or tooth fractured separately whereas in the bonded inlays fractures were commonly found both in the tooth and inlay. According to this study, bonded inlay restoration increased fracture resistance, while cavity design had no statistical difference on fracture resistance of the restored tooth.

Influence of internal angle and shape of the lining on residual stress of Class II molar restorations

Polymerization shrinkage is a major side effect of resin composite materials that affects the success and longevity of caries restorations. This study was to analyze the effect of the internal angle and shape of the lining on the shrinkage residual stress of dental restorations in Class II mesio-occlusal-distal (MOD) cavities through finite element analysis (FEA). A 3D reconstructed model of a human mandibular first molar was created from micro-CT images, and then the tooth was prepared as a Class II MOD cavity. 3D models of four regular internal corner shapes of Class II MOD cavities with different internal angles of lining and one 90° filleted corner model were created. The thermal expansion technique was applied to approximate the shrinkage impact of composite resin polymerization in the FE software ABAQUS. Von Mises stress was taken as a metric. The results showed that the level of residual stresses in the Class II MOD cavities was greatly dependent on the internal angle of the lining. The maximum von Mises stress in tooth tissue decreased as the internal angle of the lining increased. The internal shapes of the lining had no obvious effect on the stress, and the filleted corner model had less stress. This lining strategy is appropriate for Class II MOD cavities with serious loss of tooth tissue.

Microleakage and Marginal Integrity of Ormocer/Methacrylate-Based Bulk-Fill Resin Restorations in MOD Cavities: SEM and Stereomicroscopic Evaluation.

This in vitro study aimed to compare the microleakage and marginal integrity of methacrylate/ormocer-based bulk-fill composite (BFC) restorations used in cervical marginal relocation with two different layering thicknesses in mesio-occlusal-distal (MOD) cavities exposed to thermo-mechanical loading. Standard MOD cavities were prepared in 60 mandibular molars and assigned into three groups: x-tra fil/AF + x-tra base/XB, Tetric N-Ceram Bulk Fill/TNB + Tetric N-Flow Bulk Fill/TFB, and Admira Fusion x-tra/AFX + Admira Fusion x-base/AFB. Each group was further divided into two subgroups (2 mm and 4 mm) based on the thickness of flowable BFCs (n = 10). The specimens were subjected to thermo-mechanical loading (240,000 cycles) and immersed in 0.2% methylene blue. Following mesiodistal sectioning, the specimens were examined under stereomicroscope (×25) and scored (0-3) for microleakage. Marginal integrity was examined using a scanning electron microscope (SEM). Descriptive statistical methods and the chi-square test were used to evaluate the data (p < 0.05). While there was no statistically significant difference in gingival cement microleakage in the XB and AFB specimens with a 4 mm thickness, microleakage was significantly increased in the TFB specimen (p = 0.604, 0.481, 0.018 respectively). A significantly higher amount of score 0 coronal microleakage was detected in the AFX2 mm + AFB4 mm compared to the TNB2 mm + TFB4 mm (p = 0.039). The SEM examination demonstrated better marginal integrity in groups with 2 mm thick flowable BFCs. Ormocer and methacrylate-based materials can be used in marginal relocation with thin layers.

Fracture Load of Molars Restored with Bulk-fill, Flowable Bulk-fill, and Conventional Resin Composite After Simulated Chewing.

This study aimed to compare the fracture toughness of molars with wide mesio-occlusal-distal (MOD) cavities restored with regular and flowable bulk-fill resin composite and a conventional resin composite after 250,000 mechanical cycles of chewing simulation. Thirty-two extracted mandibular third molars were selected and class II MOD cavities involving 2/3 of the intercuspal width and 4 mm depth were prepared. Teeth were divided into four groups based on resin composite type and insertion technique (n=8): (1) CT, unprepared teeth (control); (2) CV, conventional resin composite (Tetric N-Ceram, Ivoclar Vivadent) with incremental technique; (3) R-BF, regular bulk-fill resin composite (Tetric N-Ceram Bulk Fill, Ivoclar Vivadent) with a single increment; and (4) F-BF, flowable bulk-fill resin composite (Tetric N-Flow Bulk Fill, Ivoclar Vivadent) with a single increment, except for a 1-mm-thick layer at the occlusal surface, restored with conventional resin composite (Tetric N-Ceram). All specimens were evaluated to detect the presence and propagation of enamel cracks using a LED transilluminator before and after 250,000 mechanical cycles (SD Mechatronic GmbH). After a chewing simulation, they were subjected to a compressive force in a universal testing machine (DL-2000, EMIC) until fracture. The maximum fracture load of the specimens was measured (N) and the fracture patterns were classified based on the fracture site (above or below the cementoenamel junction [CEJ]). Data were statistically analyzed with one-way ANOVA. All specimens survived after 250,000 mechanical cycles, and no statistically significant differences among groups were observed regarding the fracture toughness (p<0.05). The fracture analysis demonstrated that failures below the CEJ were more common in CV (75%), while CT, R-BF, and F-BF showed this type of failure in 38%, 63%, and 63% of the specimens, respectively. The results of the crack analysis showed that the occurrence of new cracks and crack propagation was also higher in CV (33.3%), followed by R-BF, F-BF, and CT (14%, 14%, and 11% of the specimens, respectively). Teeth restored with regular and flowable bulk-fill composites showed similar fracture toughness after the chewing simulation compared to those restored with the conventional resin composite and unprepared teeth. Furthermore, teeth restored with both regular and flowable bulk-fill composites showed a lower incidence of enamel cracks and fractures below the CEJ compared to those restored with the conventional resin composite.

Microleakage of three different combinations of adhesive and composite resins

Aim The aim of the present study was to evaluate the influence of 3 adhesive systems on microleakage of direct composite restorations with proximal margins under the cement-enamel junction (CEJ) and in the enamel. Materials and methods In 30 extracted molars standardized MOD (mesio-occlusal-distal) cavities were prepared with a proximal margin located 1 mm under the cement-enamel junction and another one in the enamel, and subsequently randomly divided in 3 groups of 10 using 3 different adhesives and the same composite: Flowable (G-aenial Universal Injectable, GC) + universal adhesive (G2-Bond universal, GC) with selective-etch technique (Group 1); Flowable (G-aenial Universal Injectable, GC) + self-etch adhesive (Clearfil SE Bond 2, Kuraray) with 2-step technique (Group 2); Flowable (G-aenial Universal Injectable, GC) + total-etch adhesive (Optibond FL, Kerr) with 3-step technique (Group 3). Samples were tested for microleakage using silver nitrate and infiltration was classified in 5 levels. The differences in microleakage were statistically evaluated with significance set at P<0.05. Results In the margin located in the enamel, group 1 showed an average of 0 microleakage, group 2 an average of 0.2 and group 3 an average of 0.1. In the margin located in the dentin, group 1 showed an average score of 1.1, group 2 of 2.15 ang group 3 of 1.25. No statistically significant difference was found in the enamel. Conclusion The combination of adhesive G2-Bond universal and Optibond FL showed the highest sealing ability both in margins located in the enamel and margins located in the dentin. The adhesive interface in the enamel produced a very good seal, while the adhesive interface in the dentin showed varying degrees of microleakage in all groups.

Fracture Behavior of Short Fiber-Reinforced Direct Restorations in Large MOD Cavities.

The aim of this research was to study the impact of using a short fiber-reinforced composite (SFRC) core on the fatigue performance and fracture behavior of direct large posterior composite restorations. Moreover, the influence of the consistency (flowable or packable) of occlusal composite coverage was assessed. A total of 100 intact molars were collected and randomly distributed into five groups (n = 20). Deep mesio-occlusal-distal (MOD) cavities were prepared in all groups. After adhesive treatment and rebuilding the missing interproximal walls with conventional composite, the specimens in four experimental groups were restored by an SFRC core (everX Flow), which was applied and cured either in bulk or in oblique layers (each 2 mm thick). Packable (G-aenial Posterior) or flowable (G-aenial Injectable) conventional composites were used as a final occlusal layer. The control group was restored with only packable conventional composite. Fatigue survival was measured for all specimens using a cyclic loading machine until a fracture occurred or a total of 25,000 cycles was achieved. Kaplan–Meyer survival analyses were conducted, followed by pairwise log-rank post hoc comparisons. The static load-bearing capacity of surviving teeth was tested using a universal testing machine. Fracture patterns were evaluated visually. There was no statistically significant (p > 0.05) difference in terms of survival between the tested groups. All groups for which flowable SFRC was used showed statistically significantly higher load-bearing capacities compared to the control group (p < 0.05). There were no significant differences regarding fracture resistance among the fiber-reinforced study groups. Regarding the fracture pattern during the survival analysis, all specimens that received SFRC showed a dominantly restorable type of fracture, while the control specimens presented a dominantly non-restorable type. The use of flowable SFRC as a reinforcing core for large MOD direct restorations showed promising achievements regarding fracture behavior.

Cuspal Deflection and Temperature Rise of MOD Cavities Restored through the Bulk-Fill and Incremental Layering Techniques Using Flowable and Packable Bulk-Fill Composites.

Background: The aim of this study was to investigate cuspal deflection caused by material shrinkage and temperature rise occurring in the pulp chamber during photopolymerization. The aim of this study was also to investigate the effect of flowable and packable bulk-fill composites on cuspal deflection occurring in mesio-occlusal–distal (MOD) cavities restored through the bulk-fill or through the incremental layering technique. Additionally, mechanical and thermal properties of bulk-fill composites were considered. Methods: Two bulk-fill composites (high-viscosity and low-viscosity), largely differing in material composition, were used. These composites were characterized through linear shrinkage and compressive test. Cuspal deformation during restoration of mesio-occlusal–distal cavities of human premolars was evaluated using both the bulk-fill and the incremental layering techniques. Temperature rise was measured through thermocouples placed 1 mm below the cavity floor. Results: Shrinkage of the flowable composite was significantly higher (p < 0.05) than that of packable composite, while mechanical properties were significantly lower (p < 0.05). For cusp distance variation, no significant difference was observed in cavities restored through both restorative techniques, while temperature rise values spanned from 8.2 °C to 11.9 °C. Conclusions: No significant difference in cusp deflection between the two composites was observed according to both the restorative techniques. This result can be ascribed to the Young’s modulus suggesting that the packable composite is stiffer, while the flowable composite is more compliant, thus balancing the cusp distance variation. The light curing modality of 1000 mW/cm2 for 20 s can be considered thermally safe for the pulp chamber.

Evaluation of fracture resistance of pulpotomized second primary molars restored with fiber-reinforced composite

Abstract Objectives Fiber reinforcement of composite restorations can help decrease the fracture risk in restored pulpotomized teeth with severe coronal lesions. This study aimed to evaluate the fracture resistance of pulpotomized second primary molars restored with fiber-reinforced composite (FRC). Methods This experimental study was done on 40 extracted primary second molars in four groups (n = 10). The negative controls were intact untreated teeth; while, other samples were pulpotomized with the mesio-occlusal-distal (MOD) access cavities prepared on their buccal and lingual surfaces. Positive control group was left unrestored. Composite group received glass ionomer on Zonalin and was restored with flowable composite and then composite. The FRC group received glass ionomer as the preceding group; the glass fiber was embedded within flowable composite, and the cavity was restored with composite. The compressive forces leading to fracture were recorded in Newton. Comparisons were made through one-way ANOVA and Tukey's post-hoc test (α = 0.05). Results The highest mean fracture resistance belonged to the intact teeth (604.45 ± 59.02 N), then the FRC group (584.31 ± 57.18 N). Unrestored teeth had the lowest fracture resistance (235.60 ± 45.60 N); however, they were not significantly different from composite group in this regard (P = 0.47). Although FRC group had significantly higher fracture resistance than the unrestored and composite group, it was not significantly different from intact teeth. Conclusions Fiber reinforcement improved the fracture resistance of pulpotomized primary molar with large MOD cavities.

Comparison of the fracture resistance of three different recent composite systems in large Class II mesio-occlusal distal cavities: An in vitro study.

Background:The present study was undertaken to evaluate the most suitable recent restorative material for extensively mutilated teeth.Aim:This study aims to evaluate and compare the fracture resistance of maxillary premolars with Class II mesio-occlusal distal (MOD) cavities restored with recent Ever X posterior, bulk-fill composite, and Estelite sigma quick composite systems.Materials and Methods:Sixty human maxillary premolars were selected. Fifteen intact teeth served as positive control (Group 1). MOD cavities were prepared in the remaining 45 teeth with standardized dimensions and were randomly divided into three experimental groups (Group 2, 3, and 4) (n = 15). Teeth in Group 2, 3, and 4 were reinforced with 3M ESPE Filtek Bulk-fill posterior, GC Ever X posterior, and Tokuyama Estelite sigma quick composites, respectively. Fracture resistance was measured in Newton (N).Results:Group 4 (1432.60 N) showed the highest mean fracture resistance followed by Group 3 (1326.20 N), Group 1 positive controls (1288.53 N), and Group 2 (946.66N), respectively. One-way analysis of variance (ANOVA) test revealed a statistically significant difference between all the groups (P = 0.005). Post hoc Tukey test revealed a statistically significant difference in mean fracture resistance between the Group 2 and Group 4 (P = 0.004), as well as between the Group 2 and Group 3 (P = 0.033). However, there were no significant differences among the other groups.Conclusion:Among the experimental groups, Estelite sigma quick composite showed the highest fracture resistance. Statistically, a significant difference was seen between all groups.

Structural Integrity Evaluation of Large MOD Restorations Fabricated With a Bulk-Fill and a CAD/CAM Resin Composite Material.

To evaluate the effect of two composite restorative techniques (direct bulk fill vs indirect CAD/CAM) on the fracture resistance and mode of fracture of extended mesio-occlusal-distal (MOD) cavity preparations. Fifty-one sound human mandibular third molars were divided into three groups (n=17). Extended bucco-lingual MOD cavities were prepared. Teeth in group 1 were restored with a bulk-fill resin composite (Filtek Bulk-Fill Posterior Restorative), teeth in group 2 were restored with composite computer-aided design/computer-aided manufacturing (CAD/CAM) inlays (Lava Ultimate), and teeth in group 3 served as control and remained intact. All specimens were submitted to thermocycling, and a fracture resistance test was performed using a Universal testing machine (0.5 mm/min). Mode of fracture was classified into five types. One-way analysis of variance and the Duncan test were used to analyze the fracture load data at a significance level of α = 0.05. A chi-square test was used for the analysis of fracture mode between the restorative groups. Statistical analysis showed significant differences in fracture resistance among the experimental groups. The teeth restored with the bulk-fill composite exhibited lower fracture resistance (1285.3±655.0 N) when compared to the teeth restored with the composite CAD/CAM inlays (1869.8±529.4 N) (p<0.05). Mode of fracture showed the same distribution between the restorative groups. Although both types of restorations failed at loads larger than those found in the oral cavity, the CAD/CAM composite inlays increased the fracture resistance of teeth with large MOD cavities when compared to direct bulk-fill composite restorations. The majority of fracture types were intraorally repairable for both restorative techniques.

Intracoronal stress transfer through enamel following RBC photopolymerisation: A synchrotron X-ray study

ObjectivesTo measure the spatial distribution of crystallographic strain in tooth enamel induced by the photo-polymerisation of a dimethacrylate resin based composite cavity restoration. MethodsSix sound first premolar teeth, allocated into two groups (n=3), were prepared with mesio-occlusal distal cavities. The enamel was machined at the point of maximum convexity on the outer tooth to create a vertical fin of thickness 100μm and 0.5mm depth to allow for synchrotron X-ray diffraction measurements. 2D diffraction patterns were used to determine crystallite orientation and quantify changes in the hydroxyapatite crystal lattice parameters, before and after photo-polymerisation of a composite material placed in the cavity, to calculate strain in the respective axis. The composite was photo-polymerised with either relatively high (1200mWcm−2, group 1) or low (480mWcm−2, group 2) irradiances using LED or quartz halogen light sources, respectively. A paired t-test was used to determine significant differences in strain between irradiance protocols at ɑ=0.001. ResultsPhoto-polymerisation of the composite in the adjacent cavity induced significant changes in both the crystallographic c and a axes of the enamel measurement area. However the magnitude of strain was low with ∼0.1% difference before and after composite photo-polymerisation. Strain in enamel was not uniformly distributed and varied spatially as a function of crystallite orientation. Increased alignment of crystallites perpendicular to the cavity wall was associated with higher c axis strain. Additionally, strain was significantly greater in the c (p<0.001) and a axis (p<0.001) when using a high irradiance photo-polymerisation protocol. SignificanceAlthough cuspal deflection is routinely measured to indirectly assess the ‘global’ effect of composite shrinkage on the tooth-restoration complex, here we show that absolute strains generated in enamel are low, indicating strain relief mechanisms may be operative. The use of low irradiance protocols for photo-polymerisation resulted in reduced strain.

Simulated cuspal deflection and flexural properties of high viscosity bulk-fill and conventional resin composites

ObjectivesThe purpose of this study was to investigate the simulated cuspal deflection and flexural properties of high viscosity bulk-fill and conventional resin composites. MethodsSeven high viscosity bulk-fill resin composites and eight conventional resin composites were used. Aluminum blocks (10 mm x 8 mm x 15 mm) with a mesio-occlusal-distal (MOD) cavity [4 (W) mm x 8 (L) mm x 4 (D) mm] were prepared and randomly divided into groups for different measurement techniques [micrometer vs CSLM] and further subdivided according to type of resin composite (high viscosity bulk-fill vs conventional resin composite). The simulated cuspal deflection resulting from the polymerization of resin composite bonded to a precisely machined MOD cavity within an aluminum block was measured with either a novel highly accurate submicron digimatic micrometer (MDH-25 M, Mitsutoyo, Tokyo, Japan) or a confocal laser scanning microscope (CLSM, VK-9710, Keyence, Tokyo, Japan) cuspal measurement method. In addition, flexural properties of tested resin composites were measured to investigate the relationship between simulated cuspal deflection and flexural properties. Scanning electron microscopy observation of tested resin composites was also conducted. ResultsThe simulated cuspal deflection of high viscosity bulk-fill resin composites was similar to that of conventional resin composites, regardless of measurement method. There were no statistically significant differences (p > 0.05) between the micrometer and CLSM cuspal measurement methods. There were statistically significant differences (p < 0.05) in flexural strength and elastic modulus depending on the material, regardless of the type of resin composite. Pearson correlation analysis did not show any statistically significant (p < 0.05) relationship between flexural properties and cuspal deflection. ConclusionsThe results of this study indicate that high viscosity bulk-fill resin composites show similar cuspal deflection with bulk-filling techniques, to those shown by conventional resin composites with incremental filling techniques. Simulated cuspal deflection can be measured using either a micrometer or CLSM, but this experiment failed to show any relationship between the flexural properties and simulated cuspal deflection of resin composites. SignificanceHigh viscosity bulk-fill resin composites produce the same level of cuspal deflection as a conventional incrementally filled resin composite.

Comparison of different base materials on fracture strength of mesio-occlusal-distal composite restorations

Abstract Objective: The aim of this study was to evaluate the influence of different base materials on fracture strength of mesio-occlusal-distal (MOD) composite restorations. Materials and Methods: Forty-eight extracted, intact maxillary molar teeth with standardized, deep MOD cavities were randomly assigned into four groups according to the base material placed: Control group (CO); no base material, SDR group; bulk-fill flowable composite, CGIC group; chemically curing glass ionomer cement (GIC), and RGIC group; light curing resin reinforced GIC. All the specimens were then restored with a nanocomposite (CeramX Duo/Dentsply) in combination with etch and rinse adhesive following the manufacturer’s instructions. After aging fracture, strength of the specimens was tested by the application of a ramped oblique load to the buccal cusp in a universal testing machine. Mean fracture strength values for each group were calculated and compared using one-way ANOVA (P = 0.05). Fracture patterns of the specimens were also evaluated. Results: The mean loads necessary to fracture the samples were as follows: control: 819.22 ± 253.65; SDR: 694.46 ± 266. 55; CGIC: 559.15 ± 277.34; RGIC 861.87 ± 277.28: N. The control and RGIC groups showed significantly higher fracture strength than CGIC and SDR groups (P &lt; 0.05). Although the mean fracture strength value of SDR group was higher than that of CGIC group, the difference between these groups was not statistically significant (P &gt; 0.05). Most frequently observed fracture patterns were adhesive (58.3%) in CO, cohesive (50%) in SDR group, cohesive (83.3%) in CGIC group, and mixed (41.7%) in RGIC group. Conclusions: Resin-modified glass-ionomer cement as a base material or restoration of the tooth only with composite resin resulted in higher fracture strength than composite resin restoration with a conventional glass ionomer base or a flowable bulk-fill material. Fracture pattern distributions diversed according to the base material placed under composite restoration.

Influence of the restorative procedure factors on stress values in premolar with MOD cavity: a finite element study.

In order to investigate the influence of cusp reduction, cavity isthmus width, and restorative material on stress values in premolar with mesio-occlusal-distal (MOD) cavity, numerical simulations were done on three-dimensional (3D) models of a maxillary second premolar designed using computerized tomography (CT) scan images. The use of four restorative materials (direct resin composite, direct resin composite with resin-modified glass-ionomer cement as the base, indirect resin composite, ceramic), three cavity preparation designs (without cusp coverage, 2-mm palatal cusp coverage, 2-mm palatal and buccal cusp coverage), and two cavity isthmus widths (1/2 and 2/3 intercuspal width) were simulated. After applying a static load of 200N on the occlusal surface of the tooth, von Mises stresses in the enamel, dentin, and restoration were calculated using finite element analysis (FEA). Stress values in the enamel were primarily influenced by cavity preparation design, while restorative material showed higher contribution in dentin. The lowest stress values were obtained in models with cusp coverage and indirect restorations. Cavity isthmus width had minimal influence on stress values in tooth structures. None of the investigated factors determined stress values in the restoration. In conclusion, the use of ceramic restoration covering both palatal and buccal cusp provided the most favourable stress distribution of premolars with MOD cavity. Graphical abstract ᅟ.

The Effects of Cavity Preparation and Composite Resin on Bond Strength and Stress Distribution Using the Microtensile Bond Test.

To evaluate the effect of flowable bulk-fill or conventional composite resin on bond strength and stress distribution in flat or mesio-occlusal-distal (MOD) cavity preparations using the microtensile bond strength (μTBS) test. Forty human molars were divided into two groups and received either standardized MOD or flat cavity preparations. Restorations were made using the conventional composite resin Z350 (Filtek Z350XT, 3M-ESPE, St Paul, MN, USA) or flowable bulk-fill (FBF) composite resin (Filtek Bulk Fill Flowable, 3M-ESPE). Postgel shrinkage was measured using the strain gauge technique (n=10). The Z350 buildup was made in two increments of 2.0 mm, and the FBF was made in a single increment of 4.0 mm. Six rectangular sticks were obtained for each tooth, and each section was used for μTBS testing at 1.0 mm/min. Polymerization shrinkage was modeled using postgel shrinkage data. The μTBS data were analyzed statistically using a two-way analysis of variance (ANOVA), and the postgel shrinkage data were analyzed using a one-way ANOVA with Tukey post hoc test. The failure modes were analyzed using a chi-square test (α=0.05). Our results show that both the type of cavity preparation and the composite resin used affect the bond strength and stress distribution. The Z350 composite resin had a higher postgel shrinkage than the FBF composite resin. The μTBS of the MOD preparation was influenced by the type of composite resin used. Irrespective of composite resin, flat cavity preparations resulted in higher μTBS than MOD preparations ( p<0.001). Specifically, in flat-prepared cavities, FBF composite resin had a similar μTBS relative to Z350 composite resin. However, in MOD-prepared cavities, those with FBF composite resin had higher μTBS values than those with Z350 composite resin. Adhesive failure was prevalent for all tested groups. The MOD preparation resulted in higher shrinkage stress than the flat preparation, irrespective of composite resin. For MOD-prepared cavities, FBF composite resin resulted in lower stress than Z350 composite resin. However, no differences were found for flat-prepared cavities. FBF composite resin had lower shrinkage stress than Z350 conventional composite resin. The μTBS of the MOD preparation was influenced by the composite resin type. Flat cavity preparations had no influence on stress and μTBS. However, for MOD preparation, composite resin with higher shrinkage stress resulted in lower μTBS values.

Effect of Light Activation of Pulp-Capping Materials and Resin Composite on Dentin Deformation and the Pulp Temperature Change.

To analyze the effect of pulp-capping materials and resin composite light activation on strain and temperature development in the pulp and on the interfacial integrity at the pulpal floor/pulp-capping materials in large molar class II cavities. Forty extracted molars received large mesio-occlusal-distal (MOD) cavity bur preparation with 1.0 mm of dentin remaining at the pulp floor. Four pulp-capping materials (self-etching adhesive system, Clearfil SE Bond [CLE], Kuraray), two light-curing calcium hydroxide cements (BioCal [BIO], Biodinâmica, and Ultra-Blend Plus [ULT], Ultradent), and a resin-modified glass ionomer cement- (Vitrebond [VIT], 3M ESPE) were applied on the pulpal floor. The cavities were incrementally restored with resin composite (Filtek Z350 XT, 3M ESPE). Thermocouple (n=10) and strain gauge (n=10) were placed inside the pulp chamber in contact with the top of the pulpal floor to detect temperature changes and dentin strain during light curing of the pulp-capping materials and during resin composite restoration. Exotherm was calculated by subtracting postcure from polymerization temperature (n=10). Interface integrity at the pulpal floor was investigated using micro-CT (SkyScan 1272, Bruker). The degree of cure of capping materials was calculated using the Fourier transform infrared and attenuated total reflectance cell. Data were analyzed using one-way analysis of variance followed by the Tukey test (α=0.05). Pulpal dentin strains (μs) during light curing of CLE were higher than for other pulp-capping materials ( p<0.001). During resin composite light activation, the pulpal dentin strain increased for ULT, VIT, and CLE and decreased for BIO. The pulpal dentin strain was significantly higher during pulp-capping light activation. The temperature inside the pulp chamber increased approximately 3.5°C after light curing the pulp-capping materials and approximately 2.1°C after final restoration. Pulp-capping material type had no influence temperature increase. The micro-CT showed perfect interfacial integrity after restoration for CLE and ULT; however, gaps were found between BIO and pulpal floor in all specimens. BIO had a significantly lower degree of conversion than ULT, VIT, and CLE. Light curing of pulp-capping materials caused deformation of pulpal dentin and increased pulpal temperature in large MOD cavities. Shrinkage of the resin composite restoration caused debonding of BIO from the pulpal floor.

Mechanical behavior of bulk direct composite versus block composite and lithium disilicate indirect Class II restorations by CAD-FEM modeling

ObjectivesTo study the influence of resin based and lithium disilicate materials on the stress and strain distributions in adhesive class II mesio-occlusal-distal (MOD) restorations using numerical finite element analysis (FEA). To investigate the materials combinations in the restored teeth during mastication and their ability to relieve stresses. MethodsOne 3D model of a sound lower molar and three 3D class II MOD cavity models with 95° cavity-margin-angle shapes were modelled. Different material combinations were simulated: model A, with a 10μm thick resin bonding layer and a resin composite bulk filling material; model B, with a 70μm resin cement with an indirect CAD-CAM resin composite inlay; model C, with a 70μm thick resin cement with an indirect lithium disilicate machinable inlay. To simulate polymerization shrinkage effects in the adhesive layers and bulk fill composite, the thermal expansion approach was used. Shell elements were employed for representing the adhesive layers. 3D solid CTETRA elements with four grid points were employed for modelling the food bolus and tooth. Slide-type contact elements were used between the tooth surface and food. A vertical occlusal load of 600 N was applied, and nodal displacements on the bottom cutting surfaces were constrained in all directions. All the materials were assumed to be isotropic and elastic and a static linear analysis was performed. ResultsDisplacements were different in models A, B and C. Polymerization shrinkage hardly affected model A and mastication only partially affected mechanical behavior. Shrinkage stress peaks were mainly located marginally along the enamel-restoration interface at occlusal and mesio-distal sites. However, at the internal dentinal walls, stress distributions were critical with the highest maximum stresses concentrated in the proximal boxes. In models B and C, shrinkage stress was only produced by the 70μm thick resin layer, but the magnitudes depended on the Young’s modulus (E) of the inlay materials. Model B mastication behavior (with E=20GPa) was similar to the sound tooth stress relief pattern. Model B internally showed differences from the sound tooth model but reduced maximum stresses than model A and partially than model C. Model C (with E=70GPa) behaved similarly to model B with well redistributed stresses at the occlusal margins and the lateral sides with higher stress concentrations in the proximal boxes. Models B and C showed a more favorable performance than model A with elastic biomechanics similar to the sound tooth model. SignificanceBulk filling resin composite with 1% linear polymerization shrinkage negatively affected the mechanical behavior of class II MOD restored teeth. Class II MOD direct resin composite showed greater potential for damage because of higher internal and marginal stress evolution during resin polymerization shrinkage. With a large class II MOD cavity an indirect composite or a lithium disilicate inlay restoration may provide a mechanical response close to that of a sound tooth.

The effects of cavity-margin-angles and bolus stiffness on the mechanical behavior of indirect resin composite class II restorations

ObjectiveTo study the influence of the different class II mesio-occlusal-distal (MOD) cavity shape on the stress and strain distributions in adhesive indirect restorations, using numerical finite element analysis (FEA). To investigate the relationship between restored teeth failure and stiffness of food, three values of Young’s modulus were used for the food. MethodsA 3D model of a sound lower molar and three class II MOD cavities with different shape were created. Slide-type contact elements were used between tooth surface and food. An adhesive resin-based cement, modeled with fixed-type contact elements, and a single restorative filling materials were considered. To simulate polymerization shrinkage effect, which is basically restricted to the thin composite cement layer, shell elements were employed and the thermal expansion approach was used. A vertical occlusal load of 600N was applied, while assigning fixed zero-displacements on the cutting surfaces below the crevices. All the materials were assumed to be isotropic and elastic. A static linear analysis was carried out. ResultsIn the lingual cusp, the displacements increased as the values of the stiffness food increased. In the restored teeth, the stress near the restoration-tooth interface was strongly dependent on the MOD cavity shape. The stress peaks were mainly located along the enamel–dentin interface at the lingual side; wedge-shaped MOD cavity with a low angle, in combination with the lowest food stiffness provided the best results. SignificanceA more complex load application on the occlusal surfaces was introduced. Food stiffness slightly affected the stress distribution of the restored and sound teeth. Teeth with adhesive class II MOD indirect resin composite restorations were potentially more susceptible to damage if the class II MOD cavity-margin-angle was higher than 95°. Restored teeth with a higher cavity-margin-angle led to considerable stress concentration in the lingual cusp along the enamel–dentin interface. These models were more susceptible to fracture in the lingual cusps when compared to the buccal ones.