Joining technology for dissimilar materials was developed for the fabrication of an ITER blanket first-wall, which consisted of Be, CuCrZr, and stainless steel (SS). The Be/CuCrZr/SS joint was fabricated using a hot isostatic pressing (HIP) method. Beryllium armor was joined to the CuCrZr/SS block at 580°C under 100MPa. The optimal interlayer coatings of Cr/Cu and Ti/Cr/Cu were developed using an ion-beam assisted physical vapor deposition. Beryllium is also a candidate armor material for the TBM first-wall. Successful joining of Be to ferritic-martensitic steel (FMS) was accomplished using an HIP method by introducing the thick diffusion barrier. A thick diffusion barrier of a Cu foil(10μm) limited the excessive diffusion and prevented the formation of brittle phases at the Be/FMS interface. Be and FMS were bonded at 650–850°C; however, a temperature of lower than 750°C was recommended to avoid material degradation of FMS. In addition, the joining of W to FMS has been developed. Tungsten is another armor material applicable to more severe plasma conditions. The large difference in the thermal expansion between W and FMS was resolved by introducing the Ti interlayer and Mo separator. Moreover, the double-staged HIP (the first stage at 900°C and 100MPa and the second stage at 750°C and 70MPa) was applied to suppress the edge delamination of W/FMS joints during thermal history.