Abstract The tensile strength test of highly porous ceramic foams has been developed and first results have been obtained on bioactive glass foams. The tested material was a 45S5 Bioglass ® derived foam-like scaffold intended for use in bone tissue engineering which was manufactured by Bioglass ® slurry coating of polyurethane foam and subsequent sintering. The Bioglass ® foam structure was investigated in two states: uncoated (as fabricated) and with a PDLLA polymer coating. The tensile testing procedure is based on fixation of the foam into aluminium pots by a suitable adhesive. Tensile test samples having cross-section of 10×10 mm 2 and a length of 30 mm were used for the experiments. Basic fractographic analysis was applied to get relevant information about specimens' behaviour during tensile loading. In Bioglass ® based scaffolds, the presence of PDLLA coating led to a significant increase of the fracture strength, which is attributed to the interaction of the polymer phase with propagating cracks, e.g. enabling a crack bridging mechanism to take place.