Abstract
Aluminum-doped zinc oxide (AZO) target was fabricated using AZO nanopowders synthesized by co-precipitation method and then the AZO films with different thicknesses were deposited on glass by d.c. magnetron sputtering at room temperature. AZO target is nodules free and shows homogeneous microstructure, ultra-high density and low resistivity. ZnAl2O4 phase appears in AZO target and disappears in AZO films. All AZO films show c-axis preferred orientation and hexagonal structure. With increasing film thickness from 153 to 1404 nm, the crystallinity was improved and the angle of (002) peak was close to 34.45°. The increase in grain size and surface roughness is due to the increase in film thickness. The decrease of resistivity is ascribed to the increases of carrier concentration and Hall mobility. The lowest resistivity is 9.6 × 10−4 Ω·cm. The average transmittance of AZO films exceeds 80%, and a sharp fundamental absorption edge with red-shifting is observed in the visible range. The bandgap decreases from 3.26 to 3.02 eV.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.