Abstract
AbstractAn aluminium alloy for potential high temperature application containing substantial additions of chromium, iron, and nickel has been examined. Structural changes during consolidation, phase identification, and structural stability of the extrudate have been assessed. The rapidly solidified powders are non-spherical and contain a considerable proportion of particles in the size range 30–60 μm. The microstructure of the powder particles exhibits fine, individual spherulites surrounded by an aluminium matrix containing fine precipitates. X-ray analysis shows that the powder contains α Al, Al13Cr2, and an unknown phase or phases, the spherulites being a mixture of all these phases. The powder is readily cold compacted and a linear relationship between compaction pressure and density is shown. Clearly defined powder particles are retained in the billet section during the extrusion sequence and a break-up of oxide envelopes occurs, but no oxide presence is found in the extrudates. The multiphase spheru...
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.