Abstract
Mordenite zeolite have been successfully synthesized from prepared nano-silica by hydrothermal method at 25 0C for 3 days. The produced sample was studied using XRD, XRF, SEM, FT-IR, AFM and BET surface area. SEM showed that the prepared sample crystallized in needle shape crystals. BET surface area and pore size of H-mordenite zeolite were 336.7 m2/g and 2.49 nm, respectively. AFM show that the average crystal diameter was 111 nm. Si/Al ratio and ion exchange percentage measured by XRF were 7.544 and 99.62 %, respectively.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: IOP Conference Series: Materials Science and Engineering
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.