Abstract
We investigated the phase-separated structure of nitrile butadiene rubber (NBR)/polyvinyl chloride (PVC) blends with different acrylonitrile (AN) contents in the NBR, using dynamic mechanical analysis measurements and scanning-transmission-electron-microscopy (STEM)-energy-dispersive-X-ray-spectroscopy (EDS) elemental analysis. Two separate sharp tan δ peaks were observed in the blend at the lower AN content of 18.0%, whereas a broad peak was observed in the blends with the higher AN contents of 29.0 and 33.5%, due to the increase in miscibility, as expected from the decrease in the solubility parameter difference with the increasing AN content. The STEM-EDS elemental analysis for the concentration distribution showed that the NBR was mixed in the large PVC domains with a diameter of several micrometers, and the excluded PVC existed around the interface of the domain-matrix phases in the blend with the lower AN content, whereas small domains with a diameter of several tens of nanometers were dispersed in the blend with the higher AN content. The concentration difference in PVC between the PVC domain and the NBR matrix became smaller with increasing miscibility as the AN content increased although the blends contained the same PVC content of 40 wt%.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.