Investigation of the Microstructure and Wear Properties of Conventional Laser Cladding and Ultra-High-Speed Laser Cladding Alloy Coatings for Wheel Materials

Abstract

In this paper, Fe-based and Co-based alloy powders were chosen to perform laser cladding on wheel materials through conventional laser cladding (CLC) and ultra-high-speed laser cladding (UHSLC) processes, respectively. The microstructures, element distribution, phase composition and hardness of the Fe-based alloy and Co-based alloy coating layers using the CLC and UHSLC processes were compared and analysed. The results show that the CLC and UHSLC alloy coatings were dense and free of defects such as pores and cracks. Compared with the CLC alloy coating, the grain size of the UHSLC alloy coating was smaller, the coating composition was close to the powder design composition, and the distribution of Cr within and between the grains was more uniform. The Fe-based coating was mainly composed of (Fe, Ni) and Cr7C3, and the Co-based coating was mainly composed of γ-Co and Cr23C6. It was found that the cooling rate of the CLC alloy coating was smaller than that of the USHLC, and the hardness of the CLC alloy coating was less than that of the USHLC. The average hardness of the UHSLC Fe-based and Co-based alloy coatings was 709 HV and 525 HV, respectively. The average hardness of the CLC Fe-based and Co-based alloy coatings was 615 HV and 493 HV, respectively. The rolling friction and wear tests were carried out with the CLC-treated and UHSLC-treated wheel specimens on the GPM-30 rolling contact fatigue testing machine. The results showed that the wear rate of the UHSLC alloy coating on the wheel specimens was significantly lower than that of the CLC alloy coating on the wheel specimens. The wear rates of the UHSLC Fe-based and Co-based alloy coatings on the wheel specimens were reduced by 40.7% and 73.8%, respectively. It was demonstrated that the wear resistance of the USHLC alloy coatings was better than those of the CLC alloy coatings. The CLC alloy coating exhibited more severe fatigue damage with small cracks. Furthermore, the damage of the UHSLC alloy coating was relatively minor, with slight spalling. The Co-based alloy coating exhibited superior wear properties with the same laser cladding process.