Abstract
Hexagonal tungsten trioxide–base interstitial solid solutions of general formula CoxWO3, where 0.01 ≤ x ≤ 0.09, were prepared hydrothermally. The dopant homogeneity extent was found to depend on рН in the working solution. Interstitial solid solutions with the highest Co2+ concentrations were formed at рН of 2.3. The CoxWO3 samples with a fiber-like morphology with a fiber diameter of ca. 40 nm, which were prepared at рН of 2.3, had the highest specific surface area, equal to 38.6 m2/g. The key parameter for the stability of the CoxWO3 crystal structure appeared to be ammonium ions residing in the hexagonal channels of the crystal structure. When tested as photocatalysts of 1,2,4-trichlorobenzene oxidation under the UV light, the prepared samples showed high chloroarene conversions and low selectivities to yield a wide range of organic compounds, including chlorine-free ones.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.