Abstract
Yttrium Iron Garnet (YIG) films were prepared on Si substrates by Chemical Solution Deposition (CSD) technique using acetic acid and deionized water as solvents. Well-crystallized and crack-free YIG films were obtained when annealed at 750 °C and 850 °C respectively, showing a low surface roughness of several nanometers. When annealed at 750 °C for 30 min, the saturated magnetization (Ms) and coercive field (Hc) of YIG films were 0.121 emu/mm3 (4πMs = 1.52 kGs) and 7 Oe respectively, which were similar to that prepared by PLD technique. The peak-to-peak linewidth of ferromagnetic resonance (FMR) was 220 Oe at 9.10 GHz. The results demonstrated that CSD was an excellent technique to prepare high quality yttrium iron garnet (YIG) films on silicon, which could provide a lower-cost way for large-scale production on Si-based integrated devices.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.