Abstract
Thermal barrier coatings (TBCs) enable nickel-base superalloy gas turbine blades to run at their highest possible temperatures. Currently, a bond coat (BC) is utilized to adhere the yttria-stabilized zirconia (YSZ) top coat to the nickel-base superalloy substrate. However, this increases cost. In this study, YSZ top coats were applied directly to the nickel-base superalloy Rene N5. The Rene N5 samples were pre-oxidized at 1150°C in atmosphere in order to form an α-Al2O3 layer to enhance bonding to the YSZ top coat. YSZ dense vertically cracked (DVC) and columnar morphologies were then applied. These samples were then cyclically and isothermally tested in atmosphere at 1150°C. Both SPS DVC and SPS Columnar coatings were found to have poor adhesion. The lack of adequate α-Al2O3 layer thickness, the rapid formation of spinel and the grit blasting process preceding coating deposition were determined to be the primary causes of poor performance.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call