Abstract
Amorphous Gd <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">x</inf> Fe <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">1-x</inf> (0 < x < 0.35) thin films were prepared by RF cosputtering using an iron target covered partially with small gadolinium pieces. The composition dependences of saturation magnetization, hysteresis curves, and domain structures were studied. Spark-like domains were observed when the magnetization was reversed from saturation. The uniaxial anisotropy was induced perpendicular to the film plane. The average value of the perpendicular uniaxial anisotropy constant Ku was about 2 × 10 <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">5</sup> erg/cm <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sup> . Ku, however, decreases as the saturation moment decreases in the vicinity of room temperature compensation. The stripe domain width was varied from 0.3 to 4 microns as the saturation moment decreased from 300 to 20 gauss. These magnetic properties of amorphous Gd-Fe sputtered films are similar to those of amorphous Gd-Co films.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call