Surface Mechanical Properties Research Articles

Evaluating surface mechanical properties and wear resistance of Ti–6Al–4V alloy subjected to ultrasonic pulsed waterjet peening

The alloy Ti–6Al–4V is widely utilized in various industrial applications, yet its inherent susceptibility to mechanical wear and friction has led to performance limitations. Addressing this, surface modification techniques have been employed to improve material surface properties. Among these, ultrasonic pulsed waterjet (UPWJ) peening emerges as a viable solution due to its ability to improve surface characteristics without causing excessive plastic deformation, unwanted thermal effects, or surface contamination. This study is focused on the influence of UPWJ peening parameters, particularly traverse speeds ranging from 200 to 1000 mm/s, on wrought Ti–6Al–4V (grade 5). Comprehensive characterization encompassed surface roughness, scratch hardness, and reciprocating wear analysis. Post-test examinations, including FE-SEM, CLSM, and EDS were employed to provide detailed microstructural and elemental insights. The results revealed that traverse speeds between 800 and 1000 mm/s yielded a remarkable 55 % enhancement in scratch hardness. Additionally, wear behavior exhibited a correlation with UPWJ traverse speed; notably, a speed of 900 mm/s indicated a 12 % improvement in wear resistance under a 40 N load. This research highlights the interplay relationship between UPWJ peening parameters and Ti–6Al–4V's wear performance, contributing to its broader understanding and application potential.

Effect of AC/DC mixed current waveform on surface oxidation, microstructure and mechanical properties of TIG welded TC4 titanium alloy

Coarse β-grains and severe surface oxidation are major factors plaguing the comprehensive properties of tungsten inert gas (TIG) welded joints of titanium alloy. To improve the performance of welded joints, a novel current waveform, alternating current/direct current (AC/DC) mixed current waveform which was named Mix-TIG was proposed. In Mix-TIG, the oxide film on the weld surface is broken up by the cathodic crushing effect. Cyclic variations of the current waveform produce stronger arc stirring and more intense oscillations in the molten pool which results in grain refinement. In addition, the lower temperature gradient in the melt pool due to the smaller heat input in Mix-TIG also contributes to grain refinement. The elongation and microhardness of the Mix-TIG were increased.

Fatigue life prediction model for shot-peened laser powder bed fused 304L steel considering residual stress relaxation and defect distribution

Shot peening (SP) is a post-treatment technology that enhances the surface smoothness, mechanical properties, and fatigue performance at the surface layer of metal materials produced through laser powder bed fusion (LPBF). Therefore, accurate life prediction is crucial to effectively design and evaluate the SP process and enhance fatigue life. This study employs a cost-effective and efficient analytical method to investigate relaxation in residual stress (RS). The method calculates the interaction between RS in SP and external loading and combines it with a life prediction model. In addition, a defect-based parameter area is employed to characterize the impact of the effective defect dimensions on the fatigue life of LPBF materials. The effects of compressive residual stress (CRS) introduced by SP and process-induced internal defects on the fatigue life of LPBF material are investigated via a modified Goodman‐Basquin model. The fatigue life of 304L stainless steel (SS) prepared by LPBF after SP is predicted, and good consistency between measurement and prediction is observed.

Tailoring electroless Ni-W-P polyalloy coatings: Unveiling the synergistic impact of cerium addition and annealing on surface functional properties

Electroless deposition of Ni-based coatings is a cost-effective solution to augment the surface mechanical and electrochemical properties of engineering components. This work explores the influence of addition of rare-earth element Ce on the characteristics of Ni-W-P coatings. The concentration of Ce salt in the deposition bath was varied in the range 0–14 mg/L, and the highest deposition rate was for the solution with 8 mg/L Ce. A homogeneous distribution of Ce over the coated surfaces was observed, and the share of Ce in the composition of the deposition varied monotonically with the Ce concentration in solution. Further, the coating surface compositions also depended on the Ce-content. Coating obtained using 8 mg/L Ce was found to have significantly improved scratch hardness (8.49 GPa), fracture toughness (7.05 MPa.m1/2), specific wear rate (3.1 × 10−6 mm3/N.m) and corrosion protection efficiency (94.16 %) as compared to the coating without Ce (3.87 GPa, 3.39 MPa.m1/2, 9.03 × 10−6 mm3/N.m, and 45.44 %, respectively). Interestingly, the ability of the coating to inhibit biofilm formation on the surface initially increased with increasing Ce content, but this effect also diminished above 8 mg/L Ce. Additionally, annealing the coatings caused further alterations in the microstructures, resulting in improvement in the microhardness, scratch, wear, and biocorrosion resistance, but at the cost of compromised corrosion resistance. Properties of such annealed coatings also depended on the annealing temperature. Therefore, this study indicates that a wide spectrum of combinations of surface physical, mechanical, and electrochemical properties can be achieved by controlling only two processing conditions, i.e., the Ce concentration, and the annealing temperature.

Comparison of STP and TP Modes of Wire and Arc Additive Manufacturing of Aluminum–Magnesium Alloys: Forming, Microstructures and Mechanical Properties

Aluminum–magnesium (Al–Mg) alloys, known for their lightweight properties, are extensively utilized and crucial in the advancement of wire and arc additive manufacturing (WAAM) for direct high-quality printing—a focal point in additive manufacturing research. This study employed 1.2 mm ER5356 welding wire as the raw material to fabricate two sets of 30-layer thin-walled structures. These sets were manufactured using two distinct welding modes, speed-twin pulse (STP) and twin pulse (TP). Comparative evaluations of the surface quality, microstructures, and mechanical properties of the two sets of samples indicated that both the STP and TP modes were suitable for the WAAM of Al–Mg alloys. Analyses of grain growth in the melt pools of both sample sets revealed a non-preferential grain orientation, with a mixed arrangement of equiaxed and columnar grains. The STP mode notably achieved a refined surface finish, a reduced grain size, and a slight increase in tensile strength compared to the TP mode. From the comparison of the tensile data at the bottom, middle, and top of the two groups of samples, the additive manufacturing process in the STP mode was more stable.

Fretting wear behaviour of high strength alloy steel induced by plasma nitriding and post-oxidation

Fretting wear is caused by a relative movement of the material surface on a small scale. Finding ways to reduce fretting wear is of great importance for extending equipment life and reducing maintenance costs. With the increase of load, the effecrt of fretting wear adhesion of surface treated material becomes more obvious. The materials treated with post-oxidation have stronger wear adhesion than those treated only with plasma nitriding, but the total wear volume is reduced. In this paper, the fretting wear of high strength steel alloy with different surface treatments is simulated by the finite element method. The coefficient of friction and wear volume can be obtained from the experimental results, and the wear coefficient is calculated using the wear energy model. The predicted two-dimensional wear profile curves (U-shape and W-shape wear profiles) under different wear conditions are compared with the experimental results. The W-shape wear profile is used to describe the adhesion state of the worn surface. In addition, the surface deformation and mechanical properties of U-shape and W-shape wear profiles are analysed. The simulation results show that double-sided wear and the addition of adhesive layer is important for the prediction of wear characteristics.

Covalently grafting polycation to bacterial cellulose for antibacterial and anti-cell adhesive wound dressings

Hydrogel-based wound dressings are becoming increasingly important for wound healing. Bacterial cellulose (BC) has been commonly used as wound dressings due to its good in vitro and in vivo biocompatibility. However, pure BC does not possess antibacterial properties. In this regard, polycation gel was grafted onto the BC using a surface-initiated activator regenerated by electron transfer atom transfer radical polymerization (SI-ARGET ATRP) with subsequent quaternization for antibacterial wound dressing. Dimethylethyl methacrylate (DMAEMA) was successfully polymerized on the BC surface which was confirmed by Fourier transform infrared spectroscopy and elemental analysis. The morphology structure, specific surface area, pore size, and mechanical properties were also characterized. The quaternized PDMAEMA grafted on the BC endowed it with excellent antibacterial activity against E. coli (Gram-negative) and S. aureus (Gram-positive) with a killing rate of 89.2 % and 93.4 %, respectively. The number of cells was significantly reduced on QPD/BC hydrogel, demonstrating its good anti-adhesion ability. In vitro cellular evaluation revealed that the antibacterial wound dressing exhibited good biocompatibility. Overall, this study provides a feasible method to develop antibacterial and anti-cell adhesive hydrogel, which has a promising potential for wound healing.

Synergetic impact of binary/ternary zeolitic composites on cellulose acetate membranes for potential CO2 removal and antibacterial attributes

The aim of this research is to synthesize multifunctional mixed matrix cellulose acetate (CA) membranes that can provide better CO2/N2 selectivity and will simultaneously fight against bacteria, to immaculate the indoor environment. For that purpose, two different fillers labelled as binary ZnO@Zeolite (1:10, ZZ) and ternary ZnO–CuO@Zeolite (0.8:0.2:10, ZZC) composites have been synthesized via co-precipitation method to entrench into CA matrix with 8 wt% each. The solution mixing technique assisted by thermal evaporation process (TEAP) has been adopted to formulate the desired membranes. Surface morphology, crystalline structure, thermal decomposition, and mechanical properties of novel composites ZZ and ZZC, along with their respective corresponding membranes CA/ZZ-8 and CA/ZZC-8, have been analyzed using field emission scanning electron microscopy (FESEM), X-ray diffraction (XRD), thermogravimetric analysis (TGA), and universal testing machine (UTM). The inclusion of tri-zeolitic composite (ZZC) favors the formation of denser CA membranes, with a smaller crystallite size (10.8 nm), higher thermal stability (%), and a notable increase in mechanical strength (MPa) in contrast to virgin CA as well as bi-zeolitic composite (ZZ) loaded membranes. The selectivity for CO2/N2 separation of tri-zeolitic composite loaded membranes (CA/ZZC-8) is almost six folds higher compared to the pristine CA membrane, whereas it is five folds for bi-zeolitic composite impregnated membrane (CA/ZZ-8). To eradicate bacterial fouling, bi/tri-zeolitic composite loaded membranes are tested against E. coli bacteria by broth culture method and the results validate their antibiotic nature. Synthesized novel CA membranes with hybrid composites provide convenient access towards the development of multipurpose membranes.

Effect of electropolishing on ultrasonic cavitation in hybrid post-processing of additively manufactured metal surfaces

This investigation centered on fundamental understanding of a hybrid post-processing method that synergistically combines electrochemical polishing and ultrasonic cavitation to improve the surface roughness and mechanical properties of additively manufactured parts efficiently and simultaneously in a single step. High-speed imaging was utilized to understand the effect of the DC bias applied during electropolishing on the cavitation generated at various ultrasonic amplitudes. This was aimed at validating the hypothesis that the hybrid process is characterized by more bubbles than with ultrasonic excitation alone, and, in the presence of the DC bias, the bubbles are transported from the cathode to the anode (workpiece) where their impacts cause surface hardening. High-speed imaging confirmed a higher bubble count in the hybrid process than in the cavitation-only process at different ultrasonic amplitudes. Microhardness measurements confirmed that the hybrid process yielded higher microhardness compared to cavitation peening alone, while microhardness in electrochemical polishing showed only incremental changes. This observation was also corroborated by the grain size measurements, with the hybrid process exhibiting more grain refinement than cavitation-only or electropolishing-only post-processing modes. Surface topography analysis revealed minimal improvement in surface roughness due to cavitation-only, emphasizing the importance of the hybrid process in enhancing both surface roughness and the mechanical properties. Scanning electron microscope (SEM) images showed randomly distributed micro-dimples on the surface produced by the hybrid process at the highest ultrasonic amplitude, attributed to the increased number of cavitation bubbles. This research provides fundamental insights into why the hybrid process excels in simultaneously reducing surface roughness and achieving superior surface microhardness.

Thermal aging behavior and heat resistance mechanism of ultraviolet crosslinked ultra‐high molecular weight polyethylene fiber

AbstractAs advances in heat resistant ultrahigh molecular weight polyethylene (UHMWPE) fiber via ultraviolet (UV) crosslinking, it is worth paying attention to its thermal aging behavior and heat resistance mechanism. UHMWPE fibers in different forms, the fully drawn yarn (FDY) and the UV crosslinked FDY (UVFDY), are subjected to isothermal aging at 135°C. The effects of thermal aging on their surface morphology and mechanical properties are studied and compared initially. The results demonstrate that UVFDY is a kind of a heat‐resistant fiber. Subsequently, to reveal the heat resistance mechanism of UVFDY, its crystalline and orientation structure evolution during thermal aging are further studied. It is indicated that the formation of dense‐packing crystals and disorientation behavior lead to fiber shrink, so that a number of grooves appear on the fiber surface. Since the crosslinked stucture of UVFDY hinders its molecules movement, the crystallization and disorientation behavior of UVFDY are weaker than those of FDY, resulting in UVFDY possesses slighter thermal shrinkage (Ts), fewer grooves and better mechanical properties than those of FDY. Therefore, the heat resistance of the fiber improves effectively after UV crosslinking. This work provides insights into the structure–property relationship of UVFDY during thermal aging, and offers basis data for its application in specific conditions.

Comprehensive Evaluation of Novel Biomaterials for Dental Implant Surfaces: An In Vitro Comparative Study.

Dental implantology is continually evolving in its quest to discover new biomaterials to improve dental implant success rates. The study explored the potential of innovative biomaterials for dental implant surfaces, including titanium-zirconium (Ti-Zr) alloy, hydroxyapatite-coated titanium (HA-Ti), and porous polyetheretherketone (PEEK), in comparison to conventional commercially pure titanium (CP Ti). A total of 186 samples were harvested for the analysis. Biomaterials were thoroughly evaluated in terms of surface topography, chemical composition, biocompatibility, mechanical properties, osseointegration performance, and bacterial adhesion. Study methods and techniques included scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDS), cell culture variants, tensile tests, hardness measurements, histological analysis, and microbiological testing. Surface topography examination showed significant disparities between the biomaterials: Ti-Zr had a better roughness of 1.23 μm, while HA-Ti demonstrated a smoother surface at 0.98 μm. Chemical composition evaluation indicated the presence of a Ti-Zr alloy in Ti-Zr, calcium-phosphorus richness in HA-Ti, and high titanium amounts in CP Ti. The mechanical properties assessment showed that Ti-Zr and CP Ti had good tensile strengths of 750 MPa and 320 HV. In addition, bacterial adhesion tests showed low propensities for Ti-Zr and HA-Ti at 1200 and 800 cfu/cm2, respectively. Ti-Zr and HA-Ti performed better than the other biomaterials in surface topography and mechanical properties and against bacterial adhesion. This study emphasizes that multi-parameter analysis is critical for clinical decision-making, allowing for the selection of the currently available biomaterial, which could be conducive to the long-term success of the implant.

Formation mechanism of surface gradient microstructure and mechanical properties evolution of Mg–Y-Nd-Gd-Zr alloy by ultrasonic rolling

The evolution mechanism of the microstructure and mechanical properties of a Mg–Y-Nd-Gd-Zr alloy subjected to different numbers of passes of the ultrasonic surface rolling process (USRP) was investigated. The results demonstrated an initial decrease followed by an increase in the surface roughness of the alloy. The optimal surface roughness was achieved after four passes, with a contour mean deviation of 0.06 μm and micro-roughness 10-point height of 0.55 μm. After the USRP, the alloy exhibited a composite gradient structure characterized by increased grain size and decreased dislocation, lamination, and twin densities. The depth of the gradient layer increased with each additional USRP pass, ranging from 650 μm (1 pass) to 910 μm (8 passes). Furthermore, the USRP treatment effectively enhanced the alloy strength; compared with the untreated samples; the yield strength increased by 34.2% in the gradient sample after one pass. No significant change was observed in the YS with an increasing number of rolling passes for Mg alloys, whereas both the tensile strength and elongation showed improvements. High-density twinning played a crucial role in enhancing the YS of the gradient samples without significant variation across different numbers of rolling passes, thus following a consistent pattern. The formation of more nanocrystals on the surface of Mg alloys after multiple rolling cycles is key to preventing premature fracture failure and improving the work-hardening rate.

Significant improvement in surface hardness of CrMnFeCoNi high entropy alloy via nanosecond pulse laser grain refinement

The CrMnFeCoNi alloy with a stable single face-centered cubic (FCC) phase, representing a typical class of high-entropy alloys (HEAs), has garnered considerable attention owing to their exceptional mechanical properties. However, the inherent low hardness has impeded their utilization in structural or contact components. This study attempted to improve the surface hardness of CrMnFeCoNi HEA via grain refinement realized by nanosecond pulse laser irradiation. The effects of laser parameters on the surface microstructures, chemical composition, and mechanical properties were investigated, and the mechanism for grain refinement was analyzed. The experimental results showed that the hardness of the laser-irradiated surface was significantly improved without altering the chemical composition. This study provides a simple but effective method to refine the grain of HEAs and improve their surface hardness.

The influence mechanisms of re-fused scanning on the surface roughness, microstructural evolution and mechanical properties of laser powder bed fusion processed AlMgScZr alloy

Laser powder bed fusion (LPBF) stands out as the foremost method for achieving intricate structure with superior design flexibility among additive manufacturing technologies. Within the LPBF process, surface roughness serves as a critical metric governing both fabrication precision and build quality. This study delves into the evolution of the top and side surface roughness as re-fused scanning times increase in LPBF-fabricated AlMgScZr alloy. Concurrently, the investigation evaluates alterations in microstructural characteristics and mechanical properties. Various characterization techniques, including confocal laser scanning microscope, scanning electron microscope, X-ray diffraction, electron backscatter diffraction, as well as tensile and microhardness tests, are employed. The findings concerning the top surface reveal that the initial application of re-fused scanning contributes to enhanced surface roughness. This improvement stems from refined grain structures and induced lattice distortions, facilitated by rapid heat dissipation and thermal recycling within the solidified layer. Consequently, microhardness increases. However, introducing the subsequent re-fused scanning exacerbates surface roughness and instigates Marongoni flow instability, magnesium depletion, and alterations in lattice structures. Moreover, with increasing the re-fused times, there is a noticeable enhancement in preferential crystallite growth orientation along the (200)α-Al crystal plane. Regarding the side surface, escalating re-fused times correlate with deteriorating roughness and alterations in molten pool shape and size, attributable to successive energy input. Despite these surface variations, minimal differences are observed in yield strength, tensile strength, and elongation. In essence, this research offers valuable insights into selecting optimal scanning methodologies during the LPBF process, thus guiding improvements in fabrication precision and component quality.

Effect of Post-Plasma Nitrocarburized Treatment on Mechanical Properties of Carburized and Quenched 18Cr2Ni4WA Steel

Under extreme conditions such as high speed and heavy load, 18Cr2Ni4WA steel cannot meet the service requirements even after carburizing and quenching processes. In order to obtain better surface mechanical properties and tribological property, a hollow cathode ion source diffusion strengthening device was used to nitride the traditional carburizing and quenching samples. Unlike traditional ion carbonitriding technology, the low-temperature ion carbonitriding technology used in this article can increase the surface hardness of the material by 50% after 3 h of treatment, from the original 600 HV0.1 to 900 HV0.1, while the core hardness only decreases by less than 20%. The effect of post-ion carbonitriding treatment on mechanical properties and tribological properties of the carburized and quenched 18Cr2Ni4WA steel was investigated. Samples in different treatment are characterized using optical microscopy (OM), scanning electron microscopy (SEM), optimal SRV-4 high temperature tribotester, as well as Vickers hardness tester. Under two conditions of 6N light load and 60 N heavy load, compared with untreated samples, the wear rate of ion carbonitriding samples decreased by more than 99%, while the friction coefficient remained basically unchanged. Furthermore, the careful selection of ion nitrocarburizing and carburizing tempering temperatures in this study has been shown to significantly enhance surface hardness and wear resistance, while preserving the overall hardness of the carburized sample. The present study demonstrates the potential of ion carbonitriding technology as a viable post-treatment method for carburized gears.

Bias voltage-induced structural change in PECVD-deposited diamond-like carbon coatings for optimizing the tribological performance

To improve the adhesion strength and enhance the wear resistance of diamond-like carbon (DLC) coatings, different negative bias voltages were utilized to deposit a-Si:C:H/H-DLC/DLC composite coatings on the 45 steel substrates using direct current plasma enhanced chemical vapor deposition technology. Influences of negative bias voltages on the surface morphology, microstructure, mechanical properties, and tribological performance were investigated. The results showed that as the bias voltages increased from −400 V to −600 V, the surface roughness and thickness of the coatings increased, reaching a maximum roughness of 0.426 μm and a maximum total thickness of 9.9 μm. Raman data illustrated the decrease of hydrogen contents and the increase in sp3 bonds content, matching well with the increasing hardness and elastic modulus. The residual stress tended to increase as the bias voltages, while the adhesion strength reached the maximum value of 62.45 ± 2.65 N at −550 V. Under the synergistic effects of surface roughness, interfacial adhesion strength, hardness and elastic modulus, the average friction coefficient and wear rate of the coatings initially decreased and then increased, reaching the best tribological performance at −550 V.

Effects of fatty acid esters on mechanical, thermal, microbial, and moisture barrier properties of carboxymethyl cellulose-based edible films

Fatty acid esters being biodegradable and environment friendly has been a sought-after class of molecule for various food grade applications. This work involves the incorporation of fatty acid esters namely cetyl-caprylate and cetyl-caprate in edible Carboxymethyl cellulose -based films. The esters were enzymatically synthesized by esterification of caprylic acid and capric acid respectively with cetyl alcohol at a molar ratio of 1:1, using Candida antarctica lipase B which was immobilized (10 % w/w) at 65 °C. Carboxymethyl cellulose films were prepared. To it, glycerol and by emulsification, cetyl-caprylate or cetyl-caprate esters were amalgamated. Film characterizations involved analysis of surface morphology, mechanical properties, and thermal properties. It was further characterized by X-Ray diffraction analysis, water vapor permeability, and moisture uptake. Barrier property carboxymethyl cellulose films showed significant improvement due to the incorporation of cetyl-caprylate or cetyl-caprate esters. However, when the film's melting point was measured, it was seen that glycerol influenced the thermal properties more prominently than cetyl-caprylate and cetyl-caprate esters. Thus, the addition of an optimized amount of glycerol and cetyl-caprylate or cetyl-caprate esters to the carboxymethyl cellulose films is required for improved mechanical strength and better thermal properties. Further, an antimicrobial well diffusion assay of both the esters established the antimicrobial property of the same, which thereby recommends the addition of the wax esters even more.

Effect of combined laser shock peening and nitrogen implantation on the microstructure and tribology of M50 bearing steel

The M50 bearing steel underwent a combined treatment of laser shock peening (LSP) and nitrogen ion implantation. The microstructure, surface mechanical properties and tribological behaviors were evaluated. Comparative analysis with the untreated sample revealed significant improvements in surface nano-hardness, increasing from 7.51 GPa to 11.35 GPa, 11.51 GPa, and 12.62 GPa for samples subjected to LSP, ion implantation, and combined strengthening, respectively. Correspondingly, surface compressive residual stress showed notable increases from −15.55 MPa to −1043.76 MPa, −451.34 MPa, and −1276.13 MPa, respectively. The improved surface mechanical properties observed in the combined strengthened sample are likely due to the synergistic effects of the combined strengthening. In friction tests, the combined strengthened sample exhibited the lowest friction coefficient, attributed to the presence of a metal nitride layer and a thicker amorphous layer. Wear mechanisms transitioned from fatigue spalling for the untreated specimen to slight wear and the formation of an oxidative adhesion layer after LSP and ion implantation. Remarkably, the surface of the combined strengthened specimen demonstrated minimal wear, with only an oxidative adhesion layer present.

Modified Titanium Surface with Nano Amorphous Calcium Phosphate@Chitosan Oligolactate as Ion Loading Platform with Multifunctional Properties for Potential Biomedical Application.

Titanium (Ti) is widely used in medical and dental implants. Calcium phosphate (CPs) coatings enhance Ti implants' osteoinductive properties, and additives further improve these coatings. Recently, a nano amorphous calcium phosphate (nACP) coating decorated with chitosan oligolactate (ChOL) and selenium (Se) showed immunomodulatory effects. This study investigates the surface morphology, composition, bioactivity, mechanical properties, and Se-release mechanism of the nACP@ChOL-Se hybrid coating on Ti substrates. Amorphous calcium phosphate (ACP) was synthesized, and the nACP@ChOL-Se hybrid coating was deposited on Ti substrates using in situ anaphoretic deposition. Physico-chemical characterization was used to analyze the surface of the coating (scanning electron microscopy (SEM), X-ray diffraction (XRD), and Fourier Transform Infrared Spectroscopy). The distribution of Se within the coating was examined with energy-dispersive X-ray spectroscopy (EDS). Bioactivity was evaluated in simulated body fluid (SBF), and adhesion was tested using a scratch test method. In vitro testing determined the release mechanism of Se. SEM images illustrated the surface morphology, while AFM provided a detailed analysis of surface roughness. XRD analysis revealed structural and phase composition, and EDS confirmed Se distribution within the coating. The coating exhibited bioactivity in SBF and showed good adhesion according to the scratch test. In vitro testing uncovered the release mechanism of Se from the coating. This study successfully characterized the surface morphology, composition, bioactivity, and Se-release mechanism of the nACP@ChOL-Se hybrid coating on Ti substrates, offering insights for developing immunomodulatory coatings for medical and dental applications.

Effects of removing superficial layer of cartilage on the surface morphology and mechanical behavior of cartilage

Superficial cartilage defect is an important factor that causes osteoarthritis. Therefore, it is very important to investigate the influence of superficial cartilage defects on its surface morphology and mechanical properties. In this study, the knee joint cartilage samples of adult pig were prepared, which were treated by enzymolysis with chymotrypsin and physical removal with electric friction pen, respectively. Normal cartilage and surface treated cartilage were divided into five groups: control group (normal cartilage group), chymotrypsin immersion group, chymotrypsin wiping group, removal 10% group with electric friction pen, and removal 20% group with electric friction pen. The surface morphology and structure of five groups of samples were characterized by laser spectrum confocal microscopy and environmental field scanning electron microscopy, and the mechanical properties of each group of samples were evaluated by tensile tests. The results show that the surface arithmetic mean height and fracture strength of the control group were the smallest, and the fracture strain was the largest. The surface arithmetic mean height and fracture strength of the removal 20% group with electric friction pen were the largest, and the fracture strain was the smallest. The surface arithmetic mean height, fracture strength and fracture strain values of the other three groups were all between the above two groups, but the surface arithmetic mean height and fracture strength of the removal 10% group with electric friction pen, the chymotrypsin wiping group and the chymotrypsin soaking group decreased successively, and the fracture strain increased successively. In addition, we carried out a study on the elastic modulus of different groups, and the results showed that the elastic modulus of the control group was the smallest, and the elastic modulus of the removal 20% group with electric friction pen was the largest. The above study revealed that the defect of the superficial area of cartilage changed its surface morphology and structure, and reduced its mechanical properties. The research results are of great significance for the prevention and repair of cartilage injury.