Impact fatigue is a phenomenon that is the main cause of failure of reed valves in compressor systems. This phenomenon occurs in compressors due to repeated opening and closing of reed valves during suction and exhaust cycles of compressors. When the valve opens it creates bending fatigue stresses in the body of reed valve; when the valve closes it strikes against the valve plate creating impact stresses. This reed valve movement and impact is repeated billions of times. This cyclic movement influences the impact fatigue life of the reed valve and, hence, the performance of a compressor. The valve movement can be defined in terms of valve frequency, valve lift, valve velocity and impact velocity. Inside a reciprocating compressor, a number of parameters including the valve design, valve material, compressor operating frequency and suction/exhaust pressure influence the reed valve movement.In this paper, we studied the valve movement parameters for three different suction reed valve designs manufactured from Flap-X – a martensitic stainless steel grade developed for reed valves – tested in a custom-built impact fatigue test system. The valves were excited into movement using compressed air pulses varying in frequency up to 300 Hz and varying pulse width. The valve displacement and frequency was recorded by a laser sensor at 10 000 frames per second. Before starting each test, the operating conditions such as the operating frequency and the air pulse width were pre-set in the impact fatigue test system’s control software while the applied pressure was kept constant during the test. The valve response was measured to be different for the different valve designs tested in this study. The reed valve design influenced the important reed movement parameters such as the valve lift, valve velocity, impact velocity and the frequency of valve vibrations. The valves were not tested to failure as the focus of this study was to collect the dynamic data of valve movement. However, for a practical impact fatigue testing of the reed valves intended to achieve fracture of valves, the testing should be conducted at higher frequencies to reduce test times as well as for a stable amplitude of vibration and impact velocity as shown in this study. The information obtained from this study shows the applicability of the presented impact fatigue test system to study the reed valve movement as well as their impact fatigue characteristics.