Silk Fibroin Substrates Research Articles

Time-dependent changes in adhesive force between chondrocytes and silk fibroin substrate

In tissue engineering for cartilage repair using scaffold, initial chondrocyte–material interactions are significantly important for the following cell behaviors such as phenotypic expression and matrix synthesis. Silk fibroin scaffold is considered to be one of the useful materials in/on which chondrocytes can proliferate without dedifferentiating into fibroblast-like cells and can organize a hyaline-like tissue. For the purpose of seeking some useful aspects for designing scaffold, initial adhesive force of chondrocytes to the surface of fibroin substrate was measured by using a lab-made apparatus applying the cantilever beam method. It was found that the adhesive force per unit spreading area of chondrocytes on fibroin substrate had a clear peak between 6 and 12 h after seeding. From the results of immunofluorescence staining for actin and vinculin during this period, it could be thought that an immature formation of actin fibers which was uniquely observed at the periphery of cells attaching to fibroin substrate did not contribute to the increase of adhesive force. Results in this study suggested that surface of the fibroin substrate was gradually covered with some substances which inhibit the adhesion during this period. These cell–material interactions have a possibility to be useful information for designing the adhesive performance of scaffold surface in cartilage regeneration.

Nano-scaled hydroxyapatite/polymer composite IV. Fabrication and cell adhesion properties of a three-dimensional scaffold made of composite material with a silk fibroin substrate to develop a percutaneous device

Nano-scaled sintered hydroxyapatite (HAp) particles with an a-axis length of 87 +/- 23 nm, a c-axis length of 236 +/- 81 nm, and a mean aspect ratio ( c/ a) of 2.72 were covalently linked onto a silk fibroin (SF) substrate chemically modified by graft polymerization with gamma-methacryloxypropyl trimethoxysilane (MPTS). Graft polymerization with poly(MPTS) on SF was conducted by free-radical initiation in a water solvent with pentaethylene glycol dodecyl ether as a nonionic surfactant. The alkoxysilyl groups of the graft polymers avoided hydrolysis and maintained their activity in coupling with the hydroxyl groups on the HAp surface despite the use of water as the reaction solvent. The weight gain of poly(MPTS) on SF increased with increasing the reaction time, eventually reaching a plateau value of about 15 wt% after 50 min of reaction time. After HAp covalent coating, the particles separated or aggregated into several crystals, as shown by scanning electron microscopic observation. L929 fibroblast cells adhered more plentifully on HAp-coated SF compared to untreated SF and hydrolyzed poly(MPTS)-grafted SF during 24 h or 48 h of incubation. The cells adhered only on the HAp surface but not at all on the dehydrated grafted surface of SF without HAp. A button-shaped prototype for a percutaneous device was manufactured by transplantation of HAp-coated SF fibers of about 100 microm in length onto silicone moldings using an adhesive, and the device showed good cell adhesiveness.

Effects of alkali pretreatment of silk fibroin on microstructure and properties of hydroxyapatite-silk fibroin nanocomposite.

Nanocomposites comprising hydroxyapatite (HAp) and silk fibroin (SF) were synthesized from Ca(OH)2 suspension co-dispersed with SF fine particles and H3PO4 solution via a wet-mechanochemical route. The SF particles were modified with an alkali solution to increase contact points between HAp phase and SF matrix. HAp crystallites grow more preferentially along c-axis on alkali pretreated SF substrates. The composites exhibit porous microstructure with 70% of open porosity and about 70% of the interpores ranging from 40 to 115 microm in diameter. The peak shifts in amide II band of SF indicate that the chemical interactions between HAp crystals and SF matrix are intensified by the alkali pretreatment of SF. The stronger inorganic-organic interactions promote the formation of three-dimensional network extending throughout the composites, bringing about an increase of 63% in the Vickers hardness to the composite.

Nano-scaled hydroxyapatite/polymer composite I. Coating of sintered hydroxyapatite particles on poly(gamma-methacryloxypropyl trimethoxysilane)grafted silk fibroin fibers through chemical bonding.

The inorganic-organic composite consisting of nano-scaled hydroxyapatite (HAp) and silk fibroin (SF) fibers was prepared through covalent linkage to develop a novel biomaterial for a soft-tissue-compatible material. The preparation of the composite was conducted through the three-step procedure consisting of chemical modification using 2-methacryloxyethyl isocyanate (MOI) monomer to introduce vinyl groups on SF, poly(gamma-methacryloxypropyl trimethoxysilane) (MPTS) graft-polymerization on SF, and coupling process between the surface of polyMPTS-grafted SF and HAp nano-particles. The amount of the graft-polymerization of polyMPTS through vinyl groups was well controlled by the reaction time. The nano-crystals were subsequently coated on the grafted fibers by heating at 120 degrees C for 2 h in a vacuum. The crystalline structure of the SF substrate did not change in the procedure. In the SEM observation of the composite surface, it was found that the bonded nano-crystals were separated and partially aggregated with several crystals attached on the SF fiber surface. The HAp particles adhered more strongly on the SF surface with separation or aggregation of several crystals than on the surface of the original SF after ultrasonic treatment.