Shofu Block HC Research Articles

Digital Volumetric Analysis of CAD/CAM Polymeric Materials after Tooth Brushing.

The objective of the study was to evaluate the volumetric wear of four composite materials for CAD/CAM (computer-aided design/computer-aided manufacturing) systems. The materials evaluated were: Cerasmart (CER), Shofu Block HC (SBH), Tetric CAD (TEC) and Brava (BRA). All the samples (n = 40) were subjected to simulated brushing (100,000 cycles). Wear was evaluated by superimposing pre-and post-brushing scans obtained with an intraoral optical scanner (CEREC Primescan; Dentsply Sirona, Germany), which were subsequently imported into the OraCheck software 5.0 (Dentsply Sirona, Germany). The data were analyzed by ANOVA test and Tukey’s HSD test was used for multiple comparisons. Cerasmart showed the least wear after brushing. All the tested materials exhibited mass loss.

Shear Bond Strength of a Direct Resin Composite to CAD-CAM Composite Blocks: Relative Contribution of Micromechanical and Chemical Block Surface Treatment.

This study aims to compare the shear bond strength (SBS) of a direct resin composite to CAD-CAM resin composite blocks treated with different surface treatments: micromechanical, chemical or a combination of both. Eight CAD-CAM resin composite blocks, namely Brilliant Crios, Cerasmart 270, Vita Enamic, Grandio block, Katana Avencia, Lava Ultimate, Tetric CAD and Shofu Block HC were chosen. The micromechanical surface treatment protocols tested were hydrofluoric acid, polyacrylic acid or sandblasting, and the chemical one was a universal primer. These treated CAD-CAM blocks were tested to determine the SBS of a light-curing composite resin Z100 bonded to their surface. Two-way ANOVA followed by Tukey’s post hoc test was used to investigate the difference in SBS. Failures were analyzed by Fisher’s exact test. Bonding interfaces were examined by scanning electron microscopy. The micromechanical surface treatments give the highest SBS values: sandblasting appears to be the most efficient procedure for dispersed filler composite blocks, while hydrofluoric acid etching is preferable for polymer-infiltrated ceramic network (PICN) blocks. The use of universal primer does not improve SBS values on dispersed filler composite blocks. For PICN blocks, the use of universal primer significantly increases SBS values when combined with hydrofluoric acid etching.

Influence of Artificial Aging on Mechanical Properties of Six Resin Composite Blocks for CAD/CAM Application

(1) The interactions in the oral cavity between resin composite blocks for CAD/CAM application and saliva, biofilm, and chemicals and their influence on mechanical properties are still mostly unknown. The purpose of this study is to examine the impact of artificial aging on the flexural strength, flexural modulus, hardness, Weibull modulus, and probability of failure of six resin composite CAD/CAM materials. (2) The aging was conducted by storing the specimens in water at 37 °C for 3 months, then a 3-point bending test was applied and measured. The microhardness was measured with a Vickers microhardness tester. Weibull analysis (according to ISO) was also performed. The shape and scale parameters were calculated. (3) After aging, the flexural strength values ranged from 95.51 (SD 9.07) MPa for the aged Shofu Block HC (HC) to 160.28 (SD 10.37) MPa for non-aged Gandio blocks (GR), and the flexural modulus values ranged from 7.75 (SD 0.19) GPa for HC to 16.77 (SD 0.60) GPa for GR. The microhardness (HV01) ranged from 72.71 (SD 1.43) for the Katana Avencia Block (AV) to 140.50 (SD 5.51) for GR. After aging, the Weibull characteristic strength ranged from 99.47 MPa for HC to 169.25 MPA for Brilliant Crios (CR). (4) Water storage led to a decrease in flexural strength and characteristic strength and slightly affected the flexural modulus. Gandio Blocks, Tetric CAD, and Brilliant Crios presented higher flexural strength than others.

Acid Resistance of CAD/CAM Resin Composites.

Acid resistance of CAD/CAM resin composites. Erosion-related tooth surface loss is closely related to acid exposure, such as contact with acidic beverages or disease-related reflux. As a result, dental restorations in affected patients are also exposed to acids, which indicates that the performance and longevity of a dental restoration is impacted by the acid resistance of the individually employed restorative materials. However, unlike for ceramic materials, the acid resistance of CAD/CAM resin composites is not commonly evaluated by the manufacturers, and no standardised test methods have yet been established. Against this background, the present in vitro study aimed to examine the long-term resistance of CAD/CAM resin composites (Brilliant Crios, Cerasmart, Grandio blocs, Lava Ultimate, Shofu Block HC) against three acidic media (tonic water, acetic acid, hydrochloric acid) as well as demineralized water and to investigate potential damage mechanisms. Changes in surface roughness (Sa) were detected by confocal laser scanning microscopy (CLSM), and changes in surface hardness were measured using Vickers hardness (HV). The damage mechanisms were analysed by scanning electron microscopy (SEM) with energy dispersive X-ray spectroscopy (EDS) and micro X-ray computer tomography (µXCT). For each material, few changes in either Sa or HV were identified for at least one of the different media; for Cerasmart, the sharpest deterioration in surface properties was observed. SEM–EDS revealed leaching of barium, aluminium, and titanium from fillers in a 2 µm zone on the rough but not on the polished surface of the specimen. Within the limitations of the current study, it can be concluded that polished CAD/CAM resin composites can be recommended for clinical use in patients with erosive conditions.

Effects of two methyl methacrylate-tributylborane-based luting agents with a silane-phosphate primer on bonding of four different CAD/CAM resin composite materials.

This study compared the bond strengths of four adhesive systems and four different resin composite block materials: Gradia Block (GR), Shofu Block HC (SH), Estelite Block (ES), and KZR-CAD HR2 (KZ). A primer (PZ-AB) containing a silane (γ-MPTS) with 10-methacryloyloxydecyl dihydrogen phosphate (MDP) was applied to ground surfaces of the resin composite block specimens, and the specimens were then bonded to stainless-steel rods using two methyl methacrylate-tributylborane (MMA-TBB)-based luting agents (SB and MT), designated as the PZ-AB/SB and PZ-AB/MT adhesive systems, respectively. The SB resin contained 4-methacryloyloxyethyl trimellitate anhydride (4-META), whereas the MT resin did not. The SB resin without primer (No primer/SB) and a dual-curing composite-type adhesive system (UPA/RelyX) were used as controls. The 24-h tensile bond strengths were determined and analyzed using the Tukey-Kramer HSD test (α = 0.05, n = 8). The highest bond strengths were obtained for the GR/PZ-AB/MT, GR/PZ-AB/SB, KZ/PZ-AB/MT, ES/PZ-AB/SB, and KZ/No primer/SB groups, whereas the KZ/UPA/RelyX, ES/UPA/RelyX, SH/UPA/RelyX, and SH/No primer/SB groups exhibited the lowest bond strengths. For each resin composite block material primed with γ-MPTS and MDP, the MMA-TBB-based luting agents, irrespective of the presence of 4-META, provided higher bond strengths than the dual-curing composite-type adhesive system.

Microtensile Bond Strength Between Resin-Matrix CAD/CAM Ceramics and Resin Cement after Various Surface Modifications and Artificial Aging.

To evaluate the effect of different surface modification methods on the microtensile bond strength (μTBS) of four resin-matrix CAD/CAM ceramics after artificial aging. Specimens of four CAD/CAM materials (Shofu Block HC, Lava Ultimate, Brilliant Crios, and Vita Enamic) were prepared and divided into four groups. Each group received one of the following treatments: group 1 (INT): no surface modification; group 2: sandblasting with 29-μm Al2O3 particles (SB); group 3: hydrofluoric acid etching (9%) + silane (HF+Si); group 4: sandblasting with 30-μm particles of the CoJet system (CJ). The specimens of each group were luted together in pairs using resin cement (RelyX Ultimate). After one week of water storage (37°C), the sandwich specimens were sectioned into rectangular microspecimens and half of them were immediately subjected to μTBS testing, while the other half was tested after six months. Data were statistically analyzed using FFANOVA including the factors of material, treatment, and storage time, with α = 0.05. After one week, the lowest μTBS was observed for INT, while the highest was found for either mechanical (SB and CJ) or chemical (HF+Si) treatments (p < 0.05). After six months, a significant decrease in μTBS was observed depending on treatment (p < 0.05), while artificial aging significantly influenced the μTBS of all experimental groups (p < 0.05). During the two storage periods, the failure type was mainly interfacial and was associated with the type of surface modification. After artificial aging, the μTBS appeared to depend on srface modification, while the parameter "material" did not influence the results. Consequently, adhesive strategies should be oriented towards surface modification techniques.

Characterisation of the Filler Fraction in CAD/CAM Resin-Based Composites

The performance of dental resin-based composites (RBCs) heavily depends on the characteristic properties of the individual filler fraction. As specific information regarding the properties of the filler fraction is often missing, the current study aims to characterize the filler fractions of several contemporary computer-aided design/computer-aided manufacturing (CAD/CAM) RBCs from a material science point of view. The filler fractions of seven commercially available CAD/CAM RBCs featuring different translucency variants were analysed using Scanning Electron Microscopy (SEM) with Energy Dispersive X-ray Spectroscopy (EDS), Micro-X-ray Computed Tomography (µXCT), Thermogravimetric Analysis (TG) and X-ray Diffractometry (XRD). All CAD/CAM RBCs investigated included midifill hybrid type filler fractions, and the size of the individual particles was clearly larger than the individual specifications of the manufacturer. The fillers in Shofu Block HC featured a sphericity of ≈0.8, while it was <0.7 in all other RBCs. All RBCs featured only X-ray amorphous phases. However, in Lava Ultimate, zircon crystals with low crystallinity were detected. In some CAD/CAM RBCs, inhomogeneities (X-ray opaque fillers or pores) with a size <80 µm were identified, but the effects were minor in relation to the total volume (<0.01 vol.%). The characteristic parameters of the filler fraction in RBCs are essential for the interpretation of the individual material’s mechanical and optical properties.

Food Solutions and Cigarette Smoke-Dependent Changes in Color and Surface Texture of CAD/CAM Composite Resins-An In Vitro Study.

To investigate the discoloration and surface properties of four CAD/CAM composite resins following storage in various food solutions and exposure to cigarette smoke. A total of 74 specimens (N = 370) were prepared for five materials: Brilliant Crios (BC), Cerasmart (GC), Lava Ultimate (LU), Shofu Block HC (SH), and Sonic Fill 2 (SO). Discoloration (ΔE) was investigated with a spectrophotometer. Measurements were taken before immersion in storage media (carrot juice, curry, cigarette smoke, red wine, energy drink, and distilled water), after 2 weeks of immersion, and after manual polishing of the specimens following immersion. The average surface roughness (Ra) was measured with a profilometer. Qualitative surface observation was performed with scanning electron microscopy (SEM). Data were analyzed using Kolmogorov-Smirnov test, Mann-Whitney U test, and one-way ANOVA with Tukey post hoc test. The highest influence on ΔE after immersion was observed for storage medium (ηηP2 = 0.878, P < .001), followed by the interaction between storage medium and material (ηP2 = 0.770, P < .001) and material (ηP2 = 0.306, P < .001). For ΔE after polishing, the highest influence was indicated by the interaction between material and medium (ηP2 = 0.554, P < .001), followed by medium (ηP2 = 0.244, P < .001) and material (ηP2 = 0.196, P < .001). Immersion in carrot juice led to the highest color change (ΔE: 8.0 to 10.4), whereas the lowest values were recorded in distilled water (ΔE: 2.0 to 2.4). Carrot juice and the energy drink caused the highest Ra values (0.120 μm to 0.355 μm). SEM pictures indicated a loss of the organic matrix after manual polishing. The different materials reacted dissimilarly to the various storage media in terms of discoloration. Surface roughness increased after immersion or polishing. Neither discoloration nor surface roughness could be reset to default by manual polishing. Int J Prosthodont 2023;36:194-202. doi: 10.11607/ijp.6950.

Aging behavior of high-translucent CAD/CAM resin-based composite blocks

ObjectiveThe aim of this study was to investigate the influence of artificial aging on the mechanical properties and fracture patterns of novel CAD/CAM resin-based composite blocks (RCB). MethodsFlexural strength and modulus of RCBs from seven manufacturers (Voco, Grandio Blocs, GB; Ivoclar Vivadent, Tetric®CAD, TC; DMG, Luxacam Composite, LC; Shofu Block HC, SF; 3M, Lava™ Ultimate, LU; GC, Cerasmart®, CS; Coltene, BRILLIANT Crios, CB) were assessed in a three-point-bending test after an aging process consisting of three sequential steps (14 days storage in artificial saliva, 10,000 thermo-cycles in distilled water between 5/55 °C, 48 h storage in ethanol 75%). Fracture origins were determined in a fractographic examination using reflected light stereomicroscopy combined with transillumination and scanning electron microscopy. Effects of aging were statistically analysed using one-way ANOVA with Tukey's HSD post hoc test (α = 0.05) and Weibull statistics. Correlations regarding filler amount were analysed using linear regression analysis. ResultsThe strongest influence on the flexural modulus and strength was exerted based on the parameter material (p < 0.001, ɳP2 = 0.957; ɳP2 = 0.770), but the influence of in vitro aging was also significant (p < 0.001, ɳP2 = 0.623; ɳP2 = 0.407). Storage in artificial saliva decreased the flexural modulus and flexural strength of all materials, apart from CS, significantly (p < 0.05). The Weibull moduli varied from 5.8 to 22.4. Filler amount correlated significantly with flexural modulus (p < 0.001; R2 = 0.739).Fractography revealed four different fracture patterns with fracture origins from the corner, edge or sub-surface and a smooth fracture surface with non-identifiable fracture origin. Specimens with smooth fracture surface showed the significantly lowest flexural strength (p < 0.001). Pores, agglomerates and inclusions were identified as fracture origins. ConclusionsStorage in artificial saliva mainly reduced the mechanical properties significantly while additional thermal aging mostly maintained the results. Aging in ethanol mostly maintained the results for flexural modulus but led to an increase in flexural strength values to the level of the unaged specimens. Fractographic analysis revealed a significant accumulation of sub-surface fracture origins after storage in ethanol arising from inherent flaws.

The Effects of Various Polishing Procedures on Surface Topography of CAD/CAM Resin Restoratives.

To investigate the effects of different polishing procedures on surface properties of CAD/CAM resin blocks. In this study, three different CAD/CAM restorative materials (Cerasmart, Lava Ultimate and Shofu Block HC) were used. CAD/CAM blocks were cut in 3-mm-thick slabs and divided into 5 groups. Group-1: Glaze; Group-2: Two-step Diamond Polisher; Group-3: One-step Diamond Polisher; Group-4: Three-step Diamond Polisher; Group-5: Polishing Discs+Diamond Paste. After polishing, top surfaces of the samples were prepared to screen by noncontact laser profilometer (Nanovea) for measurements. Data were analyzed using two-way analysis of variance (ANOVA). The arithmetical mean deviation of the profile was defined as Ra. The extension of Ra (a line's arithmetical mean height) to a surface was defined as Sa. Compared to the arithmetical mean of the surface, Sa expresses the difference in terms of each point's height as an absolute value. Sa was commonly used to assess surface roughness. The highest surface roughness (Ra) values in this study were 0.313 ± 0.05 for Cerasmart, 0.433 ± 0.10 for Lava Ultimate and 0.320 ± 0.05 for Shofu Block HC. The specimens in Group-4 displayed higher Ra values than other groups for each CAD/CAM material. According to surface topography (Sa) values, highest values were 2.936 ± 1.25 for Cerasmart, 2.633 ± 1.28 for Lava Ultimate and 3.489 ± 0.57 for Shofu Block HC. For Cerasmart, LAVA Ultimate and Shofu blocks, Group-1 exhibited significantly higher Sa values than other groups (p < 0.001). Optiglaze Color, Sof-Lex Diamond and Identoflex Diamond Ceramic Polisher create smooth CAD/CAM resin surfaces. However, surface roughness values of Cosmedent Nano/Microhybrid Diamond and Diapolisher Paste applied specimens were high. According to Sa values, highest roughness values belong to Optiglaze Color.

Fracture origin and crack propagation of CAD/CAM composite crowns by combining of in vitro and in silico approaches

PurposeFractographic analysis has been used to investigate the fracture behavior of Computer-aided design/computer-aided manufacturing (CAD/CAM) composite crowns by subjecting them to compression tests. However, it is difficult to investigate details of the fracture, including its initiation and propagation, using in vitro tests. The aim of this study was to determine the fracture origins and the order of crack initiation of CAD/CAM composite crowns using in silico nonlinear dynamic finite element analysis (FEA). Material and methodsThe following materials were used: Cerasmart (CS), Katana Avencia Block (KA), and Shofu Block HC (HC) as CAD/CAM crowns, Panavia SA Cement Plus (SA) as a luting material, and Clearfil DC Core Plus (DC) as an abutment. The elastic moduli and fracture strain of each material were obtained from the stress–strain curve of in vitro three-point bending tests. The fracture origins and order of crack initiation of the materials were determined by in silico nonlinear dynamic compression analysis. Load-displacement curves were statistically compared with the results of the in vitro compression tests (Pearson's correlation test, α = 0.05). ResultsThe nonlinear dynamic FEA demonstrated that crack initiation was primarily observed near the lingual side of the CAD/CAM crowns and immediately propagated to the central fossa. The models were fractured following the in vitro fracture strains, showing the same order for the products tested (CS/KA/HC, SA, and DC). Load-displacement curves with the use of CS, KA, and HC were significantly correlated to the corresponding in vitro compression tests results (CS: r = 0.985, p < 0.05, KA: r = 0.987, p < 0.05, and HC: r = 0.997, p < 0.05). ConclusionsThe in silico model established in this study clarified the crack initiation of the CAD/CAM composite crowns and the order of crack initiation among the investigated products, suggesting that the present approach is useful for analyzing the fracture behavior of CAD/CAM composite crowns in detail.

Effect of various surface treatments on the bond strength of resin luting agent and the surface roughness and surface energy of CAD/CAM materials.

The aim of this study was to examine the effect of various surface treatments on the bond strength of a resin luting agent and the surface roughness and surface energy of computer-aided design and computer-aided manufacturing (CAD/CAM) materials. Four types of CAD/CAM blocks (Shofu Block HC: BHC; GC Cerasmart: CER; VITA Enamic: ENA; and Lava Ultimate: LAV) were used. All blocks were randomly divided into eight groups based on the surface treatment as follows: no surface treatment (C), airborne-particle abrasion (AA), hydrofluoric acid etching (HA), silane coupling agent application (SL), AA/SL, HA/SL, AA/HA, and AA/HA/SL. The microtensile bond strength (µTBS), surface roughness and surface energy were measured. Three-way ANOVA revealed that all surface treatments significantly influenced the µTBS between the resin luting agent and all types of CAD/CAM materials; however, the effect of each surface treatment on surface roughness and energy was dependent on the CAD/CAM materials.

Effect of etching with low concentration hydrofluoric acid on the bond strength of CAD/CAM resin block.

The effect of etching for 90 s with low concentrations (0.5, 1.0, 2.0, 3.0, 3.5, and 4.0%) of hydrofluoric acid (HF) on the adhesiveness of computer-aided design/computer-aided manufacturing (CAD/CAM) resin blocks [CERASMART (CS), SHOFU BLOCK HC (HC), KATANA AVENCIA Block(KA), and VITA ENAMIC (EN)] was investigated. Energy dispersive spectroscopy revealed that the silicon content of HC, KA, and EN groups remained almost constant with HF etching of ≤4%. HF etching increased the surface roughness of all blocks. The HF concentration resulting in the highest shear bond strength in each group was as follows: CS (2.0%), HC (3.0%), KA (3.5%) and EN (0.5%). Scanning electron microscopy revealed that the bonding interface of etched surfaces differed significantly from that of airborne-particle abrasion surfaces. Thus, low concentration HF etching is effective for surface treatment of CAD/CAM resin blocks. The etching effect and optimum HF concentration differ with the block composition and structure.

Evaluation of the Surface Roughness and Accelerated Aging of CAD/CAM Materials.

To compare the influence of surface roughness and accelerated aging on the mechanical properties of polymer-based and ceramic CAD/CAM materials. Three polymers (Lava Ultimate [LVU], VITA ENAMIC [ENA], and Shofu Block HC [SFB]) and one ceramic (IPS Empress CAD [EMP]) were selected for this study. The specimens were treated with the aim of measuring surface roughness (Ra [mm]) and its influence on the mechanical properties. The treatments were: polishing (POL); etching with 9.6% hydrofluoric acid for 90 seconds (ETC); airborne-particle abrasion with 50-μm aluminum oxide at 2-bar pressure (SBT); and airborne-particle abrasion with 50-μm aluminum oxide at 2-bar pressure plus etching with 9.6% hydrofluoric acid (SAC) for 90 seconds. Before and after the accelerated aging (AA) protocol (30,000 cycles, 5°C and 55°C), the specimens were subjected to the 3-point bending test. The data were analyzed with two-way and three-way ANOVA and post hoc Tukey test (P < .05). The surface roughness ranged from 0.24 μm to 1.96 μm, with statistically significant differences (P < .05). The highest surface roughness, in descending order, was exhibited by: LVU > SFB > EMP > ENA. The AA demonstrated an influence on the flexural strength of LVU, ENA, and SFB. The surface treatment did not affect the flexural moduli of the materials tested. The LVU and SFB showed decreased moduli of resilience after the AA; however, modulus of resilience was not influenced by surface treatment. The polymer-based materials were affected by AA. In addition, surface treatment could jeopardize their mechanical properties in certain conditions.

Microshear bond strength of contemporary self-adhesive resin cements to CAD/CAM restorative materials: effect of surface treatment and aging

The objective of this in vitro study was to investigate the effect of material type, resin cement type, surface treatment, and aging on the microshear bond strength (µSBS) of self-adhesive resin cements (SARCs) to CAD/CAM blocks. CAD/CAM blocks (CeraSmart, CS; Lava Ultimate, LU; Shofu Block HC, HC; Vita Enamic, VE; Vitablocks Mark II, VM) were cut into 3-mm thick slices (96 specimens for each) and divided into groups: no treatment; 9% hydrofluoric acid etching; aluminum-oxide sandblasting; CoJet sandblasting. Following, the specimens were divided into three subgroups according to SARCs applied. Each specimen received four resin cement microtubules (n = 32 per subgroup). After 24 h, the cylinders of SARC were equally assigned into two groups (n = 16): immediate µSBS testing and µSBS testing after thermocycling. A shear force was applied to the adhesive interface through a μSBS testing device. Additionally, specimens were analyzed with a contact profilometer and were evaluated with scanning electron microscopy. The data were analyzed using four-way ANOVA, p < 0.05. Material type, resin cement type, surface treatment, and aging influenced the µSBS values (p < 0.001). A significant decrease in µSBS was recorded for all groups after thermocycling. The most common failure mode was detected as an adhesive failure. The surface treatment and material type influenced the surface roughness with a significant interaction. Sandblasting was more successful for CS, LU, and HC, while HF etching was better for VE and VM. The use of MDP-containing SARCs would be advantageous for the zirconia-containing CAD/CAM materials (LU and HC).

Influence of different surface treatments and universal adhesives on the repair of CAD-CAM composite resins: An in vitro study

Statement of problemThe repairability of computer-aided design and computer-aided manufacturing (CAD-CAM) composite resins might be adversely affected by the high degree of matrix polymerization that occurs during their manufacturing process. However, information on their repairability is lacking. PurposeThe purpose of this in vitro study was to evaluate the microtensile bond strength of CAD-CAM composite resins subjected to simulated repair procedures by using varying surface treatments and universal adhesives. Material and methodsFour different CAD-CAM blocks (Brilliant Crios, Lava Ultimate, Shofu Block HC, and Vita Enamic) were thermocycled (5000 times, 5/55 °C) and divided into 4 groups according to the surface treatment: control, 9% hydrofluoric acid etching, aluminum oxide airborne-particle abrasion, and tribochemical silica airborne-particle abrasion. After surface treatments, the surface roughness was measured with a nanoindenter and further examined with scanning electron microscopy. After the application of 3 different universal adhesives (Clearfil Universal Bond, Prime&Bond Universal, and Single Bond Universal), the specimens were subjected to a simulated repair process with composite resin. Bonded specimens were cut into 1 mm2 beams, and microtensile bond strength values were determined until failure at a crosshead speed of 0.5 mm/min. The bond strength data were analyzed with 3-way analysis of variance, and surface roughness data were analyzed with 2-way analysis of variance tests. Pairwise analyses were performed with the Tukey test (α=.05). ResultsAll surface treatments effectively improved repair microtensile bond strength values compared with the control (P<.05). Aluminum oxide airborne-particle abrasion had similar mean bond strength values compared with tribochemical silica airborne-particle abrasion (P>.05). Among the CAD-CAM blocks treated with hydrofluoric acid etching, Vita Enamic had the highest mean bond strength values. The highest mean microtensile bond strength repair values with the highest cohesive failure rates were found with the silane-containing universal adhesive (Single Bond Universal). ConclusionsSurface treatment with aluminum oxide airborne-particle abrasion and tribochemical silica airborne-particle abrasion produced successful repair results for aged resin nanoceramics, whereas hydrofluoric acid etching can be used for aged hybrid ceramic repair. Silane-containing universal adhesive reported increased bond strength. Application of universal adhesive after surface treatment is recommended to increase repair strength.

Evaluation of the Surface Characteristics of Dental CAD/CAM Materials after Different Surface Treatments.

Computer-aided design/computer-aided manufacturing (CAD/CAM) technology was developed to ensure the sufficient strength of tooth restorations, to improve esthetic restorations with a natural appearance and to make the techniques easier, faster and more accurate. In the view of the limited research on the surface treatments of the CAD/CAM materials and the need to evaluate the ideal surface characteristics of a material to achieve the best adhesion to tooth tissues, this study aimed to investigate the surface roughness and morphology of four different CAD/CAM materials using four different surface treatments. The CAD/CAM materials used in this study were three composites (Shofu Block HC, Lava Ultimate and Brilliant Crios) and a hybrid ceramic (Enamic). The surface of the specimens of each material received one of the following treatments: no surface treatment, sandblasting with 29 μm Al2O3 particles, 9% hydrofluoric acid etching and silane application, and the tribochemical method using CoJet System. Surface roughness was evaluated using optical profilometry, and surface morphology was observed by means of scanning electron microscopy. All surface treatments resulted in higher surface roughness values compared to the control group. Different treatments affected the surface properties of the materials, presumably due to discrepancies in their composition and structure.

Degradation of Computer-aided Design/Computer-aided Manufacturing Composites by Dietary Solvents: An Optical Three-dimensional Surface Analysis.

Computer-aided design/computer-aided manufacturing (CAD/CAM) composite resins are susceptible to degradation by dietary solvents. Dietary counselling is prudent when placing such CAD/CAM restorations. This study determined the effect of dietary solvents on the surface roughness (Ra) of direct, indirect, and computer-aided design/computer-aided manufacturing (CAD/CAM) dental composites. The materials evaluated were a direct composite (Filtek Z350 XT [FZ]), an indirect composite (Shofu Ceramage [CM]), and four CAD/CAM composites (Lava Ultimate [LU], Shofu Block HC [HC], Cerasmart [CS], and Vita Enamic [VE]). Specimens (12×14×1.5 mm) of each material were prepared, measured for baseline Ra, ranked, divided into six groups (n=12), and conditioned in the following media for 1 week at 37°C: air (control), distilled water, 0.02 N citric acid, 0.02 N lactic acid, heptane, and 50% ethanol-water solution. The composite specimens were then subjected to postconditioning Ra testing using an optical three-dimensional surface analyzer (G4e, Alicona Imaging GmbH, Raaba, Austria). Inter-medium and inter-material comparisons were performed with one-way analysis of variance and post hoc Bonferroni test at a significance level of α=0.05. Mean Ra values ranged from 0.086 ± 0.004 μm to 0.153 ± 0.005 μm for the various material/medium combinations. For all materials, conditioning in air (control) and distilled water generally resulted in significantly lower mean Ra than exposure to other dietary solvents. Conditioning in citric acid presented the roughest surfaces for FZ, CM, and CS. For LU, HC, and VE, exposure to lactic acid, heptane, and ethanol solution resulted in the highest mean Ra. Regardless of conditioning media, FZ had the highest and VE the lowest mean Ra compared with other composites. The CAD/CAM composites remained susceptible to surface degradation by dietary solvents despite their industrial polymerization.

Residual monomer elution from different conventional and CAD/CAM dental polymers during artificial aging.

Analyze and quantify the residual monomer elution of nine conventional and CAD/CAM (computer-aided design/computer-aided manufacturing) dental polymers during artificial aging. A total of 360 square-shaped specimens (14 × 12 × 2 ± 0.05mm) were fabricated from eight CAD/CAM polymer blanks (n = 40): Avadent Base material, Avadent Teeth material, PMMA Multi blank, PMMA Mono blank, Temp Premium, Telio CAD, Ceramill Temp, Shofu Block HC, and conventional polymer PalaXpress. Specimens were aged in distilled water for 60days at 37°C and the evaluation of the residual monomer elution was made through UV spectrophotometry. Statistical analysis was carried out in the SPSS software. One-way ANOVA and Scheffé post hoc test were applied (α < 0.05). Aging time significantly changed the elution in all groups, except for PalaXpress. Statistically significant differences of elution were found between the materials. Shofu Block HC presented the highest, whereas PMMA Multi blank A3 and Mono blank A1 presented the lowest elution after the 60th day of aging. CAD/CAM dental polymers as well as the conventional polymer PalaXpress eluted residual monomer within aging time. The differences in elution were material-dependent; still, the maximum elution found is below the specified threshold of ISO standard 20795-1. With the evolution of CAD/CAM technology, material's manufacturers have invested in the development of polymeric materials with higher resistance and stability to produce indirect restorations using CAD/CAM. It is expected that these materials present lower elution of residual monomer than conventional polymers.

Leaching behaviors of computer-aided design/computer-aided manufacturing composite resin component elements immersed in water

PurposeImmersion tests in purified water were conducted to evaluate the leaching behaviors of filler elements contained in computer-aided design/computer-aided manufacturing (CAD/CAM) composite resin. MethodsFour commercial CAD/CAM resin composite blanks were tested: Shofu block HC 2 layer, Cerasmart, Katana Avencia block, and KZR-CAD HR Block 2. The specimens in the size of 10.0×12.0×2.0mm were immersed in a 50-mL conical tube containing 40mL of purified water, and then placed in a constant-temperature oven set at a temperature of 37, 60, 70, or 80°C and stored statically for 30 days. After storage, the concentrations of leached elements in the immersion solution were measured with an inductively coupled plasma atomic emission spectrometer. To characterize the surface of the specimen after the immersion test, secondary electron images were obtained. ResultsThe immersion test resulted in the leaching of Si, the main component, from all materials tested. Some materials were found to have leached high amount of Ba or Sr in addition to Si, and remarkable surface degradation was observed. The amount of leached elements increased with increased immersion temperatures. ConclusionsFiller elements in CAD/CAM composite resins used in this study leached into purified water. The leached elements and its quantities greatly differed among materials and depend on the types of the oxides composing the filler. The amounts of leached elements varied in a temperature-dependent manner.