Optibond Solo Research Articles

The Effect of Additional Silane Pre-Treatment on the Microtensile Bond Strength of Resin-Based Composite Post-and-Core Build-Up Material

The aim of this study was to evaluate the effect of additional silane treatment on the immediate and aged microtensile bond strength (µTBS) between resin-based composite (RBC) post-and-core build-up material and an RBC CAD/CAM block. Twelve sample blocks (12 mm × 14 mm × 9 mm) were prepared using RBC post-and-core build-up material and were divided into six groups: Kerr Silane Primer (Sil) + OptiBond eXTRa Universal adhesive (EXA); OptiBond eXTRa Universal Primer (EXP) + EXA; Sil + OptiBond Universal (OBU); OBU; Sil + OptiBond Solo Plus (OSP); and OSP. Each treated sample was luted to a CAD/CAM block using an NX3 Nexus Third-Generation instrument. After storage in 37 °C water for 1 week, microspecimens were fabricated, and μTBS was tested immediately or after further immersion in water at 37 °C for 6 months. The failure mode of each specimen was determined using stereomicroscopy and scanning electron microscopy. For the immediate groups, no significant difference in µTBS was found between specimens with or without silane treatment for each adhesive (p > 0.05). For the aged groups, silane treatment significantly decreased µTBS for OptiBond eXTRa Universal (p < 0.05). Our findings indicate that additional silane treatment prior to the application of adhesive did not enhance µTBS.

Shear Bond Strength and Color Stability of Novel Antibacterial Nanofilled Dental Adhesive Resins.

Experimental adhesives containing co-doped metaloxide nanoparticles were demonstrated to display strong and long-term antibacterial properties against Streptococcus mutans biofilms. The present study represents an effort to characterize the shear-bond strength (SBS) and color stability (CS) of these novel biomaterials. Experimental adhesives were obtained by dispersing nitrogen and fluorine co-doped titanium dioxide nanoparticles (NF_TiO2, 10%, 20% or 30%, v/v%) into OptiBond Solo Plus (OPTB). Dentin surfaces were wet-polished (600-Grit). Specimens (n = 5/group) of Tetric EvoCeram were fabricated and bonded using either OPTB or experimental (OPTB + NF_TiO2) adhesives. Specimens were stored in water (37 °C) for twenty-four hours (T1), three months (T2), and six months (T3). At T1, T2, or T3, specimens were removed from water storage and were tested for SBS. Disc-shaped specimens (n = 10/group; d = 6.0 mm, t = 0.5 mm) of adhesives investigated were fabricated and subjected to thermocycling (10,000 cycles, 5−55 °C, 15 s dwell time). Specimens’ colors were determined with a VITA Easyshade® V spectrophotometer (after every 1000 cycles). SBS data was analyzed using two-way ANOVA and post-hoc Tukey tests, while CS data was analyzed using one-way ANOVA and post-hoc Tukey tests (α = 0.05). Mean values of SBS ranged from 16.39 ± 4.20 MPa (OPTB + 30%NF_TiO2) to 19.11 ± 1.11 MPa (OPTB), from 12.99 ± 2.53 MPa (OPTB + 30% NF_TiO2) to 14.87 ± 2.02 (OPTB) and from 11.37 ± 1.89 (OPTB + 20% NF_TiO2) to 14.19 ± 2.24 (OPTB) after twenty-four hours, three months, and six months of water storage, respectively. Experimental materials had SBS values that were comparable (p > 0.05) to those from OPTB independently of nanoparticle concentration or time-point considered. Experimental materials with higher NF_TiO2 concentrations had less intense color variations and were more color stable than OPTB even after 10,000 thermocycles. In combination, the results reported have demonstrated that experimental adhesives can establish strong and durable bonds to human dentin while displaying colors that are more stable, thereby suggesting that the antibacterial nanotechnology investigated can withstand the harsh conditions within the oral cavity without compromising the esthetic component of dental restorations.

The Effect of Dentin Contamination by Topical Anesthetics on Micro-Shear Bond Strength: An In Vitro Experiment.

Topical anesthetics are commonly used to minimize pain and anxiety during dental procedures. Research is scarce on the influence of topical anesthetics on bond strength. Thus, this research evaluated the effect of dentin contamination by topical anesthetic solution and gel on the micro-shear bond strengths of etch-and-rinse and self-etch bonding systems. Ninety transversally hemi-sectioned dentin discs were prepared and randomly assigned to three groups: no contamination (control group), contamination with topical anesthetic solution (Xylonor spray, Septodont), and contamination with topical anesthetic gel (Xylonor gel, Septodont). Each contamination group was subdivided into two subgroups (n = 15) based on whether the adhesive system was etch-and-rinse (Optibond Solo Plus, Kerr) or self-etch (Optibond XTR, Kerr). Tygon tubes with resin composite (Filtek Z350 XT, 3M ESPE) were placed on each surface and light cured. After 24 h, a universal testing machine was used to measure micro-shear bond strength (MPa). Furthermore, nine additional specimens of non-contaminated and contaminated dentin were prepared and scanned by a scanning electron microscope. The data of micro-shear bond strength were analyzed using two-way ANOVA, and narrative analysis was used to qualitatively interpret visual data of the micro-morphology of dentin from the scanning electron microscope. No significant differences in micro-shear bond strength among different contamination groups and adhesive systems were found (p > 0.05). The results are supported by micro-morphology of the treated dentin surfaces and modes of failure, as the micro-morphology was similar among contamination and control groups. There was no significant impact of topical anesthetic forms and dentin bonding systems on the micro-shear bond strength, which was supported by the micro-morphology from a scanning electron microscope.

Characterization of Experimental Nanoparticulated Dental Adhesive Resins with Long-Term Antibacterial Properties.

Experimental adhesives with functional nitrogen-doped titanium dioxide nanoparticles (N_TiO2) have been shown to display improved properties. However, these materials have not been characterized regarding their degree of conversion (DC), biaxial flexure strength (BFS), surface roughness (SR), elastic modulus (EM), and long-term antibacterial functionalities. Experimental adhesives were synthesized by dispersing N_TiO2 (10%, 20%, or 30%, v/v%) into OptiBond Solo Plus (OPTB, Kerr Corp., USA). Unpolymerized adhesives (volume = 50 μL/drop, n = 3/group) were individually placed onto a heated (37 °C) attenuated total reflectance (ATR) monolithic diamond crystal (Golden Gate, Specac). The spectra of composites were obtained with a Fourier-transform infrared (FTIR) spectrometer (Nicolet IS50; 500-4500 cm-1; resolution = 4 cm-1, 10 internal scans/spectrum) before and after polymerization. Disk-shaped specimens (diameter = 6.0 mm, thickness = 0.5 mm) for BFS (n = 12/group), SR and EM (n = 3/group), and for antibacterial testing (n = 18/group/time-point) were fabricated and photopolymerized (1 min each; 385-515 nm, 1000 mW/cm2; VALO). DC values (%) were calculated from pre- and post-polymerization spectra using the two-frequency method and tangent-baseline technique. BFS was assessed using a universal testing machine (Instron 68TM-5, crosshead speed = 1.27 mm/min, 25 °C). SR and EM were investigated using an atomic force microscope (Multimode 8) with aluminum-coated silicon probes (8 nm pyramidal tip, spring constant 40 N/m, Bruker). Antibacterial testing was performed by growing Streptococcus mutans biofilms (UA159-ldh, 37 °C, microaerophilic) on the surfaces of specimens for 24 h and then measuring the relative luminescence units (RLU) with a Biotek Synergy HT multi-well plate reader. Results demonstrate that experimental materials containing 10%, 20%, and 30% of N_TiO2 displayed higher levels of DC, had better mechanical properties, and were able to exert strong and durable antibacterial properties without visible light irradiation and after extended periods of simulated shelf-life and aging in PBS. The reported experimental materials are expected to increase the service lives of polymer-based bonded restorations by decreasing the incidence of secondary caries.

The Cytotoxicity of OptiBond Solo Plus and Its Effect on Sulfur Enzymes Expression in Human Fibroblast Cell Line Hs27

The aim of the study was to determine the cytotoxic concentrations and incubation times of the commonly used dental adhesive system OptiBond Solo Plus in its non-polymerized form, and to test how it relates to oxidative stress by determining the reduced and oxidized glutathione (GSH and GSSG) levels as well as to study its influence on cell number and the expression of selected sulfur enzymes, with particular emphasis on cystathionine γ-lyase (CTH) and 3-mercaptopyruvate sulfurtransferase (MPST). All investigations were conducted on an in vitro model of human fibroblast cell line Hs27. Changes in cellular plasma membrane integrity were measured by the LDH test. The expression levels were determined by RT-PCR and Western blot protocols. Changes in cell number were visualized using crystal violet staining. The RP-HPLC method was used to determine the GSH and GSSG levels. Reduced cell number was shown for all tested concentrations and times. Changes in the expression on the mRNA and protein level were demonstrated for CTH and MPST enzymes upon exposure to the tested range of OptiBond concentrations. Levels of low-molecular sulfur compounds of reduced and oxidized glutathione were also established. Cytotoxic effect of OptiBond Solo Plus may be connected with the changes of MPST and CTH sulfur enzymes in the human fibroblast Hs27 cell line. The elevated levels of these enzymes could possibly show the antioxidant response to this dental adhesive system. OptiBond Solo Plus in vitro results should be taken into consideration for further in vivo tests.

Effects of Immediate Coating on Unset Composite with Different Bonding Agents to Surface Hardness.

This study evaluated the surface microhardness of composite, affected by surface coating with different dental adhesive systems. A total of 100 composite discs were divided into five groups. Group 1 was uncoated (control group C), and groups 2 to 5 were coated with different adhesive systems (OptiBond FL: FL, OptiBond SOLO Plus: SOLO, OptiBond XTR: XTR, and OptiBond All in one: AIO, respectively). The Vickers microhardness (VHN) was measured without and with 500 thermocycles. The data were analyzed using two-way ANOVA and Tukey's posthoc test at the 95% confidence level. At 24 hours, the VHN of C (59.96 ± 3.68) and FL (59.83 ± 4.54) were significantly higher than SOLO (51.73 ± 4.63) and AIO (51.45 ± 4.11). The VHN of XTR (54.96 ± 3.68) was not significant compared with that of C and all other groups. After thermocycling, VHN were significantly decreased in all groups. However, there were no significant differences among all groups. At 24 hours, composite coated with different adhesive systems have different effects to VHN. Thermocycling all adhesive resin systems coated on composite surface significantly decreased the VHN.

Effect of Casein Phosphopeptide Amorphous Calcium Phosphate Conditioning on Microtensile Bond Strength of Three Adhesive Systems to Deep Dentin

Objectives:This study aimed to assess the effect of casein phosphopeptide amorphous calcium phosphate (CPP-ACP) on microtensile bond strength of three adhesive systems to deep dentin.Materials and Methods:In this in vitro study, the occlusal surface of 30 sound human third molars was sectioned at 2 mm below and above the cementoenamel junction. The samples were randomly divided into three groups of OptiBond Solo Plus, G-Bond, and Clearfil SE Bond. Before composite resin bonding, each group was divided into two subgroups with and without dentin preparation with CPP-ACP. The teeth were then sectioned into 1 mm rods (n=15), and their microtensile bond strength was measured at a crosshead speed of 0.5 mm/min. Data were analyzed using two-way ANOVA and post-hoc Bonferroni test.Results:There was no significant difference in bond strength of OptiBond Solo Plus (P=0.44) and Clearfil SE Bond (P=0.67) with/without CPP-ACP. A significant difference was found between the two subgroups of G-Bond in this respect (P<0.001). The differences in microtensile bond strength among all subgroups were significant (P<0.05).Conclusion:The microtensile bond strength in use of G-Bond is significantly higher following dentin treatment with CPP-ACP compared with no use of CPP-ACP.

Influence of the volume of restorative material on the concentration of stresses in the restorative interface.

BackgroundTo evaluate the microtensile strength in the adhesive interface depending on the volume of the composite resin used to restore class I cavities. Material and MethodsForty-eight human third molars received a standardized class I cavity preparation and they were separated into six experimental groups: G1 – single-bottle adhesive system; G2 - bonding system with load; G3 – single-bottle adhesive associated with low-viscosity composite resin; G4 – loaded adhesive associated with low-viscosity composite; G5 - resin-modified glass ionomer associated with single-bottle adhesive; and G6 - resin-modified glass ionomer associated with loaded adhesive. All cavities were restored with a universal restorative composite. After completing the restorations, the samples were stored for seven days in a stove (37°C) and the microtensile bond strength was evaluated by producing slices and applying axial loading in an Instron universal testing machine at a speed of 0.5 mm/min. The thickness of the intermediate layer formed on the cavity floor to verify the relationship between the volume of restorative composite and the concentration of stresses in the buccal wall. With the data obtained in the microtensile strength test, an Analysis of Variance (ANOVA) was performed entirely at random. ResultsDuncan’s test showed that group 4 (Filtek Flow/Optibond Solo Plus) obtained the highest mean of microtensile strength with no statistically significant difference to groups 3 (Filtek Flow/Single Bond), 5 (Vitremer/Single Bond), and 6 (Vitremer/Optibond Solo Plus). It also showed a statistically significant difference to groups 2 (Optibond Solo Plus) and 1 (Single Bond), with no statistical difference between the other groups studied. ConclusionsThe highest mean of microtensile strength was obtained when the volume of the restorative material decreased through the interposition between the material and the adhesive system of a base with low elasticity modulus. Key words:Adhesion, microtensile, composite resin.

Morpho-functional effects of different universal dental adhesives on human gingival fibroblasts: an in vitro study

To analyze the effects of four universal adhesives (Optibond Solo Plus—OB, Universal Bond—UB, Prime&Bond Active—PBA, FuturaBond M + —FB) on human gingival fibroblasts in terms of cytotoxicity, morphology and function. After in vitro exposure for up to 48 h, fibroblast viability was determined by the MTT assay determined, morphology by phase-contrast microscopy and migration by the scratch wound assay. Expression levels of IL1β, IL6, IL8, IL10, TNFα and VEGF genes were assessed by RT-PCR and their protein production by Western blot analysis. Apoptosis and cell cycle were analyzed by flow cytometry. OB and UB induced early morphological changes on fibroblasts (3 h) with extended cell death at 24 h/48 h. Gene expression of collagen type I and fibronectin increased fivefold compared with controls, elastin disappeared and elastase increased threefold, indicating gingival tissue tended to become fibrotic. Only UB and OB increased gene expression of inflammatory markers: IL1β at 3 and 48 h (up to about three times), IL6 and IL8 at 3 h (up to almost four times) which corresponded to the increase of the activated form NF-kB. All adhesives showed an effect on the functionality of fibroblasts with cytotoxic effect time and concentration dependent. Among all the OB and UB adhesives, they showed the greatest cell damage. The in-depth analysis of the effects of universal adhesives and possible functional effects represents an important information for the clinician towards choosing the most suitable adhesive system.

Genotoxic and cytotoxic potential of methacrylate-based orthodontic adhesives

ObjectivesThe biocompatibility of methacrylate-based adhesives is a topic that is intensively discussed in dentistry. Since only limited evidence concerning the cyto- and genotoxicity of orthodontic adhesives is available, the aim of this study was to measure the genotoxic potential of seven orthodontic methacrylate-based adhesives.Materials and methodsThe XTT assay was utilized to determine the cytotoxicity of Assure Plus, Assure Bonding Resin, ExciTE F, OptiBond Solo Plus, Scotchbond Universal Adhesive, Transbond MIP, and Transbond XT after an incubation period of 24 h on human gingival fibroblasts. We also performed the γH2AX assay to explore the genotoxic potential of the adhesives within cytotoxic dose ranges after an incubation period of 6 h.ResultsThe XTT assay showed a concentration-dependent reduction in cell viability. The decrease in cellular viability was in the same dose range most significant for Assure Plus, rendering it the adhesive material with the highest cytotoxicity. Employing the γH2AX assay, a concentration-dependent increase in H2AX phosphorylation was detected, indicating induction of DNA damage.ConclusionsFor most products, a linear correlation between the material concentration and γH2AX foci was observed. The most severe effect on γH2AX focus induction was found for Transbond MIP, which was the only adhesive in the test group containing the co-initiator diphenyliodonium hexafluorophosphate (DPIHP).Clinical relevanceThe data indicate that orthodontic adhesives, notably Transbond MIP, bear a genotoxic potential. Since the study was performed with in vitro cultivated cells, a direct translation of the findings to in vivo exposure conditions should be considered with great diligence.

Shear Bond Strength of Bulk-Fill Composites to Resin-Modified Glass Ionomer Evaluated by Different Adhesion Protocols.

ObjectiveThe aim of this study was to investigate the shear bond strengths (SBS) of different nano-resin-based composites (RBCs) to resin-modified glass-ionomer cement (RMGIC) after the application of different adhesion protocols.Material and MethodsThree RBCs (Filtek One Bulk Fill [FOBF], Tetric N-Ceram Bulk Fill [TNCBF], and Filtek Z350 XT [Z350XT]) were used as layering materials over GC Fuji II LC RMGIC. Three adhesive systems — Total-etch (OptiBond Solo Plus [OB]), self-etch (CLEAR FIL SE Bond 2 [CFSE]), and a universal bond (Single Bond Universal [SBU]) — were used. In total, 160 RMGIC blocks were prepared. Ten samples (n = 10) were layered with the same material to form a reference-cohesive control group. The remaining samples were distributed among the following groups: No treatment [NT]; Total-etch [OB]; Self-etch [CFSE]; Universal bond in the “total-etch” mode [SBU-TE]; and Universal bond in the “self-etch” mode [SBU-SE]. Samples were stored, and aged by thermocycling (5000 cycles at 5 °C / 55 °C, 30 s) and then prepared for SBS testing. Fracture modes were examined by stereomicroscopy. Data were collected and analyzed statistically at a significance level of P<0.05.ResultsThe highest mean SBS (14.30±1.08 MPa) was reported in the OB group with the TNCBF material, while the lowest was in the NT group (5.05±0.69 MPa) with FOBF. Samples in the NT group showed SBS statistically significantly lower than those of samples in all other groups (P<0.0001). Bulk-fill materials had significantly higher SBS than Z350XT in OB, CFSE, and SBU-SE (P<0.0001). SBU-TE produced SBS statistically significantly lower than those of other groups for FOBF (P<0.0001), and lower than that of OB for TNCBF (P=0.027).ConclusionOB, CFSE, and SBU-SE are reliable adhesion protocols for bonding bulk-fill RBCs to RMGIC when the “sandwich technique” is used for restorations. However, SBU-TE may not be effective in such procedures.

A Comparative Clinical Study of the Self-Adhering Flowable Composite Resin Vertise Flow and the Traditional Flowable Composite Resin Premise Flowable

Background. The aim of this research was to carry out a comparative clinical study of a self-adhesive, light-curing composite material called Vertise Flow and a traditional flow material called Premise flowable used in combination with dedicated bonding systems. In order to standardize the clinical environment, the stability of oral hygiene (analyzed with the oral hygiene index and the approximal plaque index) was taken into consideration. Methods. The study involved 37 patients with 64 fillings. They were distributed into three groups: 22 fillings in Group I, 22 fillings in Group II and 20 fillings in Group III. In Group I (G I), Vertise Flow material was applied without the use of an etching agent or a bonding system; in Group II (G II), Premise flowable material was applied without the use of an etching agent, but with the use of the OptiBond All-In-One seventh-generation bonding system; in Group III (G III), Premise flowable material was applied after etching and treatment of the hard tooth tissues using a fifth-generation OptiBond Solo Plus bonding system. Then, at appropriate time intervals (0, i.e., right after filling and after 6, 12 and 24 months), the fillings were subjected to clinical evaluation, conducted according to the Ryge scale criteria with the use of registration by means of a fluorescent high-intensity visible light beam produced by a camera (Vista Proof). Results. The quality of fillings performed with the use of comparable materials was subjected to clinical evaluation using the Ryge scale of fillings after 6, 12, and 24 months; the examination showed significant differences between the tested materials. The Vertise Flow material used without an etching agent or a bonding system (G I) presented the weakest results with respect to marginal adaptation and smoothness among those evaluated in this study. The intensification of the degradation continued over time until the final clinical observation at 24 months. The results confirmed that the best quality was achieved with the Premise flowable material after etching and treatment of the hard tooth tissues using a fifth-generation OptiBond Solo Plus bonding system (G III) relative to others for all time points during the observation. Conclusions. The used preparation scheme and bonding system have an impact on the final quality of the composite filling. There is a need to carry out a qualitative clinical evaluation of dental restorative materials under uniform conditions using evaluation scales.

Sorption, solubility and cytotoxicity of novel antibacterial nanofilled dental adhesive resins

Dental adhesives hydrolyze in the mouth. This study investigated the water sorption (SOR), solubility (SOL) and cytotoxicity (CYTO) of experimental adhesives containing nitrogen-doped titanium dioxide nanoparticles (N_TiO2). Specimens (n = 15/group [SOR, SOL]; n = 10/group [CYTO]) of unaltered Clearfil SE Protect (CSP), OptiBond Solo Plus (OSP), Adper Scotchbond (ASB) and experimental adhesives (OSP + 25% or 30% of N_TiO2) were fabricated, desiccated (37 °C) and tested for SOR and SOL according to ISO Specification 4049 (2009). CYTO specimens were UV-sterilized (8 J/cm2) and monomer extracted in growth medium (1, 3 or 7 days). Human pulp cells were isolated and seeded (0.5 × 104) for MTT assay. SOR and SOL data was analyzed using GLM and SNK (α = 0.05) and CYTO data was analyzed with Kruskal–Wallis and SNK tests (α = 0.05). SOR and SOL values ranged from 25.80 μg/mm3 (30% N_TiO2) to 28.01 μg/mm3 (OSP) and 23.88 μg/mm3 (30% N_TiO2) to 25.39 μg/mm3 (25% N_TiO2). CYTO results indicated that pulp cells exposed to experimental materials displayed comparable viabilities (p > 0.05) to those of OSP. Experimental materials displayed comparable SOR, SOL and CYTO values (p > 0.05) when compared to unaltered materials. N_TiO2 incorporation have not adversely impacted SOR, SOL and CYTO properties of unaltered adhesives.

Advanced characterization of surface-modified nanoparticles and nanofilled antibacterial dental adhesive resins

Nanotechnology can improve the performance of dental polymers. The objective of this study was to modify the surfaces of nanoparticles with silanes and proteins, characterize nanoparticles’ agglomeration levels and interfaces between nanoparticles and the polymeric matrix. Undoped (n-TiO2), nitrogen-doped (N_TiO2) and nitrogen-fluorine co-doped titanium dioxide nanoparticles (NF_TiO2) were synthesized and subjected to surface modification procedures in preparation for Small-Angle X-Ray Scattering (SAXS) and Small-Angle Neutron Scattering (SANS) characterizations. Experimental adhesives were manually synthesized by incorporating 20% (v/v) of n-TiO2, N_TiO2 or NF_TiO2 (as-synthesized or surface-modified) into OptiBond Solo Plus (OPTB). Specimens (n = 15/group; d = 6.0 mm, t = 0.5 mm) of OPTB and experimental adhesives were characterized using Time-of-Flight Secondary Ion Mass Spectroscopy (ToF-SIMS), 2-D ToF-SIMS chemical imaging and SANS. SAXS results indicated that surface-modified nanoparticles displayed higher scattering intensities in a particle-size dependent manner. ToF-SIMS results demonstrated that nanoparticles’ incorporation did not adversely impact the parental polymer. 2-D ToF-SIMS chemical imaging demonstrated the distribution of Ti+ and confirmed nitrogen-doping levels. SANS results confirmed nanoparticles’ functionalization and revealed the interfaces between nanoparticles and the polymer matrix. Metaloxide nanoparticles were successfully fabricated, incorporated and covalently functionalized in a commercial dental adhesive resin, thereby supporting the utilization of nanotechnology in dentistry.

Bond assessment of resin modified glass ionomer cement to dentin conditioned with photosensitizers, laser and conventional regimes.

To assess different conditioning regimes on shear bond strength (SBS) of resin modified glass ionomer cement (RMGIC) bonded to dentin MATERIAL AND METHODS: Fifty non carious intact maxillary molars were cleaned, isolated and randomly divided into five groups (n = 10). Before randomization, dentin surface was exposed and finished. Samples in group 1 were conditioned with methylene blue photosensitizer (MBP) 50 mg/l and activated by photodynamic therapy (PDT), Group 2: surface treated with Er,Cr:YSGG (ECL), Group 3: surface conditioned with polyacrylic acid (PAA) (control), Group 4: surface conditioned with 17 % Ethylenediaminetetraacetic acid (EDTA), Group 5: surface conditioned with total etch (Optibond solo Plus). For SBS testing the samples were placed in universal testing machine. Fracture analysis of debonded surfaces were evaluated using stereomicroscope at 40x magnification. Means and standard deviations were calculated using analysis of variance (ANOVA) and Tukey's post hoc test at a significance level of (p < 0.05). The maximum bond strength was found in group 5 conditioned with Optibond solo plus total etch (23.15 ± 3.21 MPa). Whereas, the lowest bond values were observed in group 1 treated with MBP (15.25 ± 1.54 MPa). Moreover, samples in group 2, group 3 and group 4 resulted in comparable bond strength (p > 0.05). MBP at 50 mg/l is not recommended to condition dentin prior to RMGIC application. Moreover, ECL has a potential to be suggested for dentin conditioning compared to PAA.

Cytotoxicity of Self-Etch Versus Etch-and-Rinse Dentin Adhesives: A Screening Study.

Six dentin adhesives were tested in vitro regarding their cytotoxicity on human fibroblasts. The adhesives Hybrid Bond, One-up Bond F Plus, AdheSE, Clearfil SE Bond, Optibond Solo Plus and Syntac were eluted with culture medium as single or sequentially applied adhesive part for 24 h. 75 Petri dishes were produced per group. They were evaluated triangulated, comprising the quantitative evaluation (105 ones) to determine “viable”, “dead” and “debris” cells with the use of a cell-counter and the reactivity index was also identified based on the qualitative assessment (420 ones). One-up Bond F Plus, AdheSE and Clearfil SE Bond showed a statistical difference of viable cells to the cell control. For One-up Bond F Plus, statistically, differences compared to hybrid bond and Syntac were also found. All the adhesives except One-up Bond F Plus showed significant differences between single and sequentially applied adhesive part regarding the quantitative evaluation. The test material showed a moderate grade of cytotoxicity. As a result, a statistically significant difference of the cytotoxicity between the self-etch and etch-and-rinse adhesives cannot be demonstrated regarding the qualitative evaluation and the reactivity index, but the differences between sequentially applied and single applied components can be proved.

Cytotoxicity of universal dental adhesive systems: Assessment in vitro assays on human gingival fibroblasts

Universal adhesives are the most important innovation in restorative dentistry. They are composed of different monomers, solvents and fillers. The potential cytotoxic effect of these materials is an important scientific aspect in recent literature. The aim of this study was to determine, using different in vitro techniques, the cytotoxicity evaluation of seven universal enamel-dental adhesives on human gingival fibroblasts. For this purpose, seven universal dental enamel adhesives have been evaluated by in vitro cytotoxicity tests using direct contact tests (an unpolymerized and a polymerized method) and an indirect contact test: preparation of extracts. The polymerized method showed a cytotoxicity range from 36% (G-PremioBond, GPB) to 79% (FuturaBond M+, FB). With the unpolymerized direct methods the range was from 4% (Prime&Bond Active, PBA) to 40% (Ibond Universal, IB) for undiluted adhesives; generally passing to the major dilutions the test showed a strong inhibitory activity by all the adhesives. Whereas with the indirect method by diluting the extracts of all dental adhesives the cell viability increased. The data obtained from the work has shown a lower cytotoxic effect of Optibond Solo Plus (OB) and Adhesive Universal (AU) with more reliable results with the extracts technique. The choice of reliable in vitro cytotoxic technique could represent, in dental practice, an important aid for clinical procedures in the use of adhesive systems.

Stability of Bonded Resin Composite Restorations to Enamel after Bleaching with 20% Carbamide Peroxide

This study aimed to examine the effect of postoperative home bleaching using 20% carbamide peroxide on the shear bond strengths of different adhesives to enamel and to verify the failure mode for each test specimen. One hundred sound human molars were used in this study. Bonding procedures were performed on the flattened buccal enamel surfaces according to the manufacturer's instructions. OptiBond Solo Plus adhesive (Kerr), Single Bond Universal adhesive (3M ESPE) applied with both the total-etch and self-etch techniques, and Tetric N-Bond Universal adhesive (Ivoclar Vivadent) applied with both the total-etch and self-etch techniques were used, followed by resin composite post fabrication (Filtek Z350 XT; 3M ESPE). All specimens were thermo-cycled for 5000 cycles and then divided into the control (non-bleach) and postoperative bleaching groups (20% carbamide peroxide). The shear bond strength values were measured and compared between the two groups. Data were analyzed using one-way analysis of variance with Tukey's test (p = 0.05). The failure modes of debonded specimens were evaluated using a digital microscope (50×). The bonding interfaces of the resin composite posts to different enamel conditions (control and postoperative bleaching) were observed by a scanning electron microscope (SEM) before the shear bond test. The shear bond strength values of all tested adhesives were lower in the postoperative bleaching group than they were in the control (non-bleach) group, particularly the bond strength values of self-etch adhesives. The stability of bonded resin composite restorations to enamel, using different dental adhesives, could be compromised after the bleaching procedure at varying sensitivity levels. Replacement of bonded resin composite restorations to enamel might be considered after bleaching procedures, especially if these restorations were previously bonded with self-etch adhesives.

Avaliação da resistência da união imediata à dentina de sistemas adesivos simplificados

Objetivo: Avaliar quatro sistemas adesivos comerciais de diferentes composições quanto ao desempenho da resistência da união à dentina.&#x0D; Métodos: Vinte incisivos bovinos tiveram a dentina vestibular exposta e receberam restaurações de resina confeccionadas com quatro (n=5) diferentes sistemas adesivos simplificados: Magic Bond DE e OptiBond Solo (convencionais), One-Up Bond F e Adper Prompt L-Pop (auto-condicionantes). Os dentes foram seccionados perpendicularmente a interface adesiva utilizando-se um disco de diamante, de modo a se obter palitos de 1mm² de área de secção. Os palitos foram submetidos ao ensaio de micro-tração em uma máquina de ensaios universal. Os valores médios de resistência de união dos diferentes sistemas adesivos foram comparados utilizando-se ANOVA de uma via e teste Tukey, em um nível de significância de 5%.&#x0D; Resultados: Os valores médios de resistência da união foram 48,81±0,56 para o Magic Bond DE, 47,52±13,03 para o OptiBond Solo, 44,68±13,32 para o One-Up Bond F e 31,59±11,81 para o Adper Prompt L-Pop. O adesivo Adper Prompt L-Pop apresentou resistência de união inferior a dos adesivos convencionais (p

Antibacterial dental adhesive resins containing nitrogen-doped titanium dioxide nanoparticles

The development of dental adhesive resins with long-lasting antibacterial properties is a possible solution to overcome the problem of secondary caries in modern adhesive dentistry. Objectives(i) Synthesis and characterization of nitrogen-doped titanium dioxide nanoparticles (N_TiO2), (ii) topographical, compositional and wettability characterization of thin-films (unaltered and experimental) and, (iii) antibacterial efficacy of N_TiO2-containing dental adhesives against Streptococcus mutans biofilms. Materials and methodsNanoparticles were synthesized and characterized using different techniques. Specimens (diameter = 12 mm, thickness ≅ 15 μm) of OptiBond Solo Plus (Kerr Corp., USA) and experimental adhesives [50, 67 and 80% (v/v)] were fabricated, photopolymerized (1000 mW/cm2, 1 min) and UV-sterilized (254 nm, 800,000 μJ/cm2) for microscopy, spectroscopy, wettability and antibacterial testing. Wettability was assessed with a contact angle goniometer by dispensing water droplets (2 μL) onto four random locations of each specimen (16 drops/group). Drop profiles were recorded (1 min, 25 frames/s, 37 °C) and contact angles were calculated at time = 0 s (θINITIAL) and time = 59 s (θFINAL). Antibacterial testing was performed by growing S. mutans (UA159-ldh, JM10) biofilms for either 3 or 24 h (anaerobic conditions, 37 °C) with or without continuous light irradiation (410 ± 10 nm, 3 h = 38.75 J/cm2, 24 h = 310.07 J/cm2) against the surfaces of sterile specimens. ResultsN_TiO2 was successfully prepared using solvothermal methods. Doped-nanoparticles displayed higher light absorption levels when compared to undoped titania. Experimental adhesives demonstrated superior antibacterial efficacy in dark conditions. ConclusionsThe findings presented herein suggest that N_TiO2 is a feasible antibacterial agent against cariogenic biofilms.