Flexural Strength Research Articles

Impact of repeated heat-pressing on the microstructure and flexural strength of lithium disilicate glass-ceramics

BackgroundThe leftover material from the heat-pressing of IPS e.max Press ceramic is often discarded, despite some laboratories exploring its potential for reuse. However, there is a lack of data on the performance of IPS e.max Press ceramic when combined with the button portions. This study investigated the impact of repeated heat-pressing on the crystal structure and flexural strength of lithium disilicate glass-ceramic (LDGC).MethodsSpecimens (N = 30, n = 10 per group) were categorized based on the number of heat-pressing cycles: G0 (control group, no heat-pressing), G1 (one cycle of heat-pressing), and G2 (two cycles of heat-pressing). The crystal structure of LDGC bars was characterized using X-ray diffraction (XRD). Flexural strength was tested, and microstructures were analyzed via scanning electron microscopy (SEM) and the ImageJ processing program. Data were analyzed using one-way analysis of variance (ANOVA), and multiple pairwise comparisons of means were performed with Tukey’s post-hoc test.ResultsG2 exhibited significantly lower flexural strength and crystallinity, as well as larger crystal size, compared to G1 and G0 (p < 0.05). Flexural strength values decreased significantly with an increased number of heat-pressing cycles.ConclusionsThe mechanical properties of LDGC significantly degraded after repeated heat pressing. Therefore, it is not clinically advisable to repeatedly press the lithium disilicate ingot together with the leftover material.

AN ANALYSIS ON THE USE OF MODIFIED EXPANDED PERLITE AND PUMICE IN INORGANIC BONDED FIBROUS COMPOSITE BOARDS

It is often stated that there is an energy efficiency difference between optimum energy use and actual energy use in the world. In the construction industry, various building materials are produced and used to optimize energy efficiency in buildings. Among these building materials, inorganic bonded fibrous composite boards, whose energy efficiency criteria have begun to be improved, are widely used both in Türkiye and in the world. This article presents an experimental analysis of the utilization of modified expanded perlite and pumice as key constituents in the development of inorganic bonded fibrous composite boards. The study investigates the influence of these modified porous materials on the physical, mechanical, and thermal properties of the composite boards. For this purpose; composite mortars were produced using micronized quartz sand, a hybrid fiber consisting of cellulose and glass fiber, modified expanded perlite (MEP) with stearic acid (1, 2, 3, 4, 5, 6, 7, 8, 9 wt.%) and modified pumice (MPU) with stearic acid (1, 2, 3, 4, 5, 6, 7, 8, 9 wt.%). In order to make a comparison, a control mortar that did not contain modified expanded perlite and modified pumice was produced. Through a series of experiments, it is concluded that the density values of all other mixture designs with MEP and MPU aggregate additives under equivalent conditions are lower than the control sample. The water absorption values of the samples always remained below the control sample, and with the increase in the MPU ratio and decrease in the MEP ratio, the water absorption values of the samples also decreased. The average modulus of rupture (MOR) value of control sample in the analysis made after 14 days of curing under ambient conditions is 3.73 MPa. The highest MOR value of the test samples is 3.51 MPa, which is the mixture using the highest MPU. The thermal conductivity value of the control mixture is 0.352 W/mK. The thermal conductivity value of test mixtures with MEP and MPU aggregates varies between 0.175 W/mK and 0.287 W/mK.

Incorporating an artificially synthesized fluoride complex into urethane-acrylate-based 3D printing resin: Effects on mechanical properties, cytotoxicity, antimicrobial actions, and its long-term fluoride-releasing properties

ObjectivesTo synthesize a 3D printing resin with antibacterial and long-term fluoride-releasing properties. Methods(4,4-Bis-4-[2‑hydroxy-3-(2-methacryloyloxy)propoxy]-phenyl-pentanol-amine)-N,N-diacetic acid zirconium (IV) fluoride complex was synthesized from 4,4-bis-(4-hydroxyphenyl)-pentanoic acid and monitored using proton nuclear magnetic resonance spectroscopy. The synthesized complex was incorporated into a urethane-acrylate-based (UA) resin at 5 wt% and 10 wt% (5F-UA and 10F-UA groups, respectively). The UA resin without the synthesized complex was considered as the control group. All groups were 3D printed using a DLP printer, followed by 10 min of washing and 20 min of curing. Surface characteristics were observed using scanning electron microscopy. The mechanical properties were assessed by measuring its flexural strength and Vickers hardness. The antibacterial property was investigated with direct and indirect contact tests and a WST-8 metabolic activity assay. The suspension was fully mixed and diluted for counting the number of colony-forming units. The cell viability test was performed using a cell proliferation assay. The amount of fluoride released was measured daily for 28 days using ion chromatography. One-way analysis of variance was performed for statistical analyses using SPSS software. ResultsThe amount of fluoride released increased with the concentration of fluoride complex in the resin. The fluoride ions were constantly released at a low concentration from the 3D printed specimens (5F-UA: around 0.13 ppm daily; 10F-UA: around 0.22 ppm daily). The antibacterial efficacy was acceptable in both the 5F-UA and 10F-UA groups, and higher in the latter. No cytotoxicity of the resin was detected. The mechanical properties were significantly influenced by the addition of the fluoride-releasing complex. ConclusionsThe present 3D printing UA resin incorporating a fluoride complex effectively inhibited the growth of S. mutans and demonstrated the ability to slowly release fluoride over an extended period of time. Clinical significanceThis study provided informative composition of a fluoride-releasing UA-based 3D printing resin, ideal for dental applications such as crowns, bridges, removable partial dentures, and orthodontic appliances, which can benefit from sustained fluoride release and antimicrobial properties. Further modifications to the resin composition can be easily achieved to enhance the resin qualities.

Bioinspired surface modification of mussel shells and their application as a biogenic filler in polypropylene composites

This study explores the potential of mussel shells (MS) as biogenic fillers in polymer composites. The chemical composition and crystal structures of MS were characterised. To improve MS filler dispersion and adhesion within a polypropylene (PP) matrix, three surface modification methods were evaluated: polydopamine (PDA) coating, maleic anhydride-grafted polypropylene (MAPP) modification, and PDA/MAPP co-modification. The PDA coating, inspired by the adhesive properties of mussel foot proteins, successfully functionalized the MS surface, as confirmed by X-ray photoelectron spectroscopy (XPS). Thermodynamic analysis, based on contact angle measurements, revealed that MAPP and PDA/MAPP modifications reduced surface energies and potential energy differences. These changes enhanced filler dispersion and interfacial bonding by increasing hydrophobicity and reducing agglomeration in the PP matrix. Consequently, PP composites with 20% PDA/MAPP-modified MS fillers exhibited a 2.9% increase in tensile strength and a 7.5% increase in flexural strength compared to neat PP. Scanning electron microscopy (SEM) also showed reduced filler-matrix debonding and fewer voids. The proposed mechanism attributes these macroscopic property enhancements to the ability of the PDA coating to facilitate chemical and hydrogen bonding between MS fillers and MAPP.

Optimization of mixing ratio for the production of particle board from bamboo leaves, saw dust and urea formaldehyde

This study investigated the best mix sawdust, bamboo leaves, and urea formaldehyde to create particleboard by optimizing the mixing ratio. Finding the optimal ratio of sawdust, urea formaldehyde, and bamboo leaves for the binders used in particle board production was the aim of this study. The particle boards' mechanical and physical tests were investigated. The surface morphology of particleboards and its elemental compositions were examined using Scanning Electron Microscopy (SEM) and Energy Dispersive X-ray Spectroscopy (EDS). The result observed from mechanical and physical tests conducted particle boards showed that best particleboard of composition 100 % sawdust, 50 % bamboo leaves and 2.5 g urea had the highest density of 675.643 kg/m3, modulus rupture of 3.84 N/mm2 and modulus elasticity of 2756 N/mm2. The optimal level generated by the experimental design of composition 50 % sawdust, 50 % bamboo leaves and 2.0 g urea were validated. MOR of 13.02 N/mm2 and MOE observed were 881.39 N/mm2. The SEM and EDS results revealed that optimal particleboard of validated experiment had surface with more fibrous network structures than particle board of the best process level. The particleboard that was produced from validated experiment complied with the American National Standard ANSI/A208.1–999.

Effect of sintering cycle on the strength and translucency of multilayered zirconia.

A newly introduced sintering protocol promises to offer higher translucency while not significantly compromising the flexural strength of the material. However, the effect of the novel sintering protocol has not been thoroughly validated. The purpose of this study was to measure and compare the effect of two sintering protocols on the translucency and flexural strength of two multilayered zirconia materials. Two types of multilayered zirconia materials (ZirCAD Prime and Prime esthetic) were selected. Presintered disk specimens were obtained from Translucent, Gradient, and Dentin layers (n = 20). The disks were allocated to 2 groups: standard sintering protocol (peak temperature 1500°C) and high translucency sintering protocol (peak temperature 1600°C). After the sintering process, 10 specimens from each group were randomly selected. The optical values (L*, a*, b*) were measured and used to assess translucency using the relative translucency parameter (RTP00) and translucency differences (ΔRTP00). Then, all 20 specimens were tested for biaxial flexural strength. The outcomes were analyzed. The analysis of variance is used to analyze any significant effects on translucency and flexural strength. Then, any significant difference in the translucency and flexural strength between all pairs of materials was analyzed using Bonferroni-corrected Student's t-test (α = 0.05). The high translucency sintering protocol significantly decreased biaxial strength in the Prime translucent and dentine layer, Prime esthetic translucent, and gradient layer. RTP00 was significantly reduced in the Prime gradient and Prime esthetic gradient layer when sintered with a high translucency protocol. The lowest ΔRTP00 was observed in the Prime dentine layer, while the highest ΔRTP00 was observed in the Prime esthetic dentin layer. High translucency protocol significantly lowers the biaxial flexural strength of both multilayered materials, but the alteration in translucency is within clinically acceptable thresholds (TAT00 = 2.62).

Multi-objective optimization of micro crystalline cellulose and montmorillonite filled poly lactic acid bio–composite and its characterizations

In this research study, the synthesis of poly lactic acid (PLA) based bio composite material factors contributions were investigated through the Taguchi-based grey relational analysis (GRA) technique. Effects of micro crystalline cellulose (MCC) and montmorillonite (MTT) nano clay filler, sorbitol (S) plasticizer, and temperature (T) operating factor on the PLA matrix through melt-mixing preparation method. The tensile strength (TS), Young modulus (YM), flexural strength (FS), flexural modulus (FM), hardness, impact strength (IS), water absorption (WA), and density properties of bio composite material were investigated for each experimental setup (orthogonal array, L16). Additionally, neat PLA and optimal sample structural, thermal, and morphological properties were examined through Fourier transform infrared spectroscopy (FTIR), X-Ray diffraction (X-RD), thermal gravimetry analysis/differential thermal gravimetry (TGA/DTG), and DSC and SEM analyses. The obtained result for optimal mechanical and physical properties of MCC/MTT/S/PLA bio composite was MCC at level 3 (6%), MTT at level 4 (9%), S at level 2 (10%), and T at level 4 (175 °C). Analysis of variance (ANOVA) shows that MTT has the greatest significant effect on mechanical and physical properties of MCC/MTT/S/PLA bio composite followed by MCC, T, and S. The confirmation test indicates that the improvement of weighted grey relational grade (GRG) from 0.7896 to 0.846 and the FTIR, XRD, thermal gravimetry/differential scanning calorimetry (TG/DSC), and scanning electron microscopy (SEM) results indicates that the good interaction between PLA and fillers, improvement of thermal and morphological properties of optimal (6MCC/9MTT/10S/175 °C) bio composite samples. Therefore, the multi-response characteristics of MCC/MTT/S/PLA bio composite can be highly improved by this technique.

Al(SO4)(OH)·5H2O Stemming from Complexation of Aluminum Sulfate with Water-Soluble Ternary Copolymer and further Stabilized by Silica Gel as Effective Admixtures for Enhanced Mortar Cementing

A water-soluble ternary copolymer bearing carboxyl, sulfonic, and amide functional groups was synthesized using ammonium persulfate-catalyzed free radical polymerization in water, resulting in high monomer conversion. This copolymer was then complexed with aluminum sulfate, forming an admixture containing Al(SO4)(OH)·5H2O, which was subsequently combined with silica gel. Characterization revealed that the synthesized copolymer formed a large, thin membrane that covered both the aluminum compounds and the silica gel blocks. The introduction of this complex admixture, combining the copolymer and aluminum sulfate, not only reduced the setting times of the cement paste but also enhanced the mechanical strengths of the mortar compared to using aluminum sulfate alone. The complex admixture led to the formation of katoite, metajennite, and C3A (tricalcium aluminate) in the mortar, demonstrating significant linking effects, whereas pure aluminum sulfate could not completely transform C3S within 24 h. Further addition of silica gel to the complex admixture further shortened the setting times of the paste, slightly reduced compressive strength, but improved flexural strength compared to the initial complex admixture. The silicon components appeared to fill the micropores and mesopores of the mortar, accelerating cement setting and enhancing flexural strength, while slightly decreasing compressive strength. This study contributed to the development of new cementing accelerators with improved hardening properties.

A theoretical approach based on machine learning for estimation of physical properties of LLDPE in moulding process

This study explores the prediction of mechanical characteristics of linear polyethylene based on oven residence time, employing various regression models and hyper-parameter tuning through the Whale Optimization Algorithm. The dataset comprises one input variable (oven residence time) and three output parameters (Tensile Strength, Impact Strength, and Flexure Strength). The models investigated include Multilayer Perceptron, K-Nearest Neighbors, Support Vector Regression, Polynomial Regression, and Theil–Sen Regression. The results showcased distinct performances across the models for each output parameter. The Polynomial Regression (WOA-PR) method has been identified as the most suitable option for predicting Tensile Strength due to its ability to achieve the lowest errors in terms of Mean Absolute Error, Root Mean Square Error, and Average Absolute Relative Deviation. K-Nearest Neighbors (WOA-KNN) outperforms other models in predicting Impact Strength due to its superior accuracy and reliability. Additionally, Support Vector Regression (WOA-SVR) emerges as the best model for predicting Flexure Strength, showcasing notable performance in minimizing prediction errors. These findings underscore the significance of model selection and optimization techniques in accurately predicting the mechanical properties of polymers, paving the way for enhanced manufacturing processes and material design.

Enhancing bending strength in continuous drive friction welding of PEEK polymer cylinders through the innovative progressively increased welding area method

The continuous drive friction welding (CDFW) stands out for its low energy consumption within the welding realm. Polyetheretherketone (PEEK) represents a high-performance engineering thermoplastic, falling under the polyaryletherketone family. Renowned for its outstanding mechanical, thermal, and chemical attributes, PEEK finds utility across a diverse array of industries. However, the discovery of numerous voids at the weld interface has revealed limitations in the mechanical properties of PEEK welded samples. This study introduces an innovative approach named progressively increased welding area (PIWA) method, to mitigate voids within the weld interface. In general, the Taguchi method was used to optimize the process parameters of CDFW of dissimilar PEEK round rods to reduce random efforts by the trial-and-error method. It was found that the proposed PIWA method can definitely enhance the bending strength of rotational friction welded samples due to reduction of voids inside the weld interface. The optimal process parameters for the CDFW with the PIWA method involve a rotational speed of 2500 rpm, a cone angle of 120°, a cone top width of 8 mm, and a feed rate of 0.1 mm/s. The most influential factor affecting the bending strength of the PEEK welded samples is the feed rate, followed by cone angle, rotational speed, and cone top width. Specifically, the contribution ratios for feed rate, cone angle, rotational speed, and cone top width are about 71 %, 20 %, 7 %, and 2 %, respectively. The confirmation tests showed that the bending strength of the PEEK welded samples using optimal process parameters can be increased by approximately 68 % compared with the maximum bending strength of 180 MPa using the conventional method with a cone angle of 180° The proposed PIWA method has industrial applicability and practical value because this technique can enhance the mechanical properties of PEEK welded samples under low environmental pollution and energy consumption.

Improvement of aerogel-incorporated concrete by incorporating polyvinyl alcohol fiber: Mechanical strength and thermal insulation

Aerogel incorporated concrete (AIC) effectively improves its thermal insulation performance. However, the potential mechanical strength degradation in AIC limits its further promotion and application. Fiber reinforcement is an effective means for improving the properties of cement-based materials. However, there is currently a lack research on enhancement mechanisms involved in fiber-reinforced AIC. In this study, polyvinyl alcohol (PVA) fibers with high strength and low thermal conductivity are introduced. The influence on the properties of AIC with various lengths (6–12 mm) and proportions (0–1.2 wt%) of PVA fiber was analyzed, and the mechanism of AIC enhancement was discussed based on microscopic test. The enhancing mechanism of PVA fiber on AIC was studied at microscopic scale to establish new solutions to the development of cementitious materials with both excellent load-bearing capacity and thermal insulation performance. The results revealed a synergistic effect of hydrophobic aerogel and PVA fiber on the fluidity of the mix due to the improvement of particle dispersibility and distribution uniformity. Additionally, the PVA fibers crossed aerogel particles around could inhibit crack expansion caused by aerogel fractures, thus effectively mitigating the loss of strength heat transfer with aerogel incorporation. At the same time, PVA fiber also plays a role in thermal resistance. Specifically, the incorporation of 0.6 wt% 9-mm fibers yielded the best overall reinforcement results, with an increase of 31.4 % and 15.5 % in flexural and compressive strengths, respectively, and a 28.5 % decrease in thermal conductivity. The microstructural tests indicated that incorporating PVA fibers at 0–0.6 wt% could optimize the pore structure, reduce the porosity, and increase the water resistance of AIC. The hydration degree of the cement matrix increased due to Ca2+ adsorption by PVA fibers. This study provides an optimized design strategy incorporating PVA fibers to enhance both the physical properties, mechanical strength, and thermal insulation properties of AIC.

Comparison of Flexural Strength and Wear of Injectable, Flowable and Paste Composite Resins

Comparison of Flexural Strength and Wear of Injectable, Flowable and Paste Composite Resins

Durability Properties of Steel Textiles and Bonding Properties at the Interface of Steel Textiles with Reinforced Mortar-Reinforced Concrete Systems.

Aging and deterioration of building structures have been persistent concerns in the field of engineering. To address these challenges while supporting modern green and sustainable development goals, this study introduces an innovative reinforcement system that employs steel textiles as the primary reinforcing material. The steel textiles were engineered by optimizing the compatibility between steel fibers and a hot melt adhesive (HMA). These textiles were then used to reinforce concrete structures, creating a steel textile-reinforced mortar (STRM)-reinforced concrete system. The study also examined the durability of the steel textiles and the interfacial bonding performance within the STRM-reinforced concrete system. The results showed that the compatibility between steel fibers and ethylene vinyl acetate copolymer (HMA-2) is better, and the steel textiles prepared with it have superior hydrothermal and corrosion resistance. After the system had been maintained for 28 days, the overall flexural strength of the STRM-reinforced concrete system was increased by 100.03%, the interfacial shear load by 49.54%, the interfacial shear stiffness by 61.2%, and the positive tensile bond performance by 26.1%. This proves that STRM has a good reinforcement effect on the concrete reinforcement system.

Achieving excellent mechanical and antioxidant properties in MoAlB ceramics through spark plasma sintering-high-frequency (SPS-HF) sintering

A fully dense MoAlB ceramic was synthesized utilizing MoAlB powder through SPS-HF technology. The Vickers hardness, fracture toughness and bending strength of the MoAlB ceramic reached 14.08GPa, 6.70MPa m1/2 and 407MPa, respectively. The electrical conductivity and thermal conductivity of the MoAlB ceramic at room temperature were measured to be 3.20 × 106 S⋅m−1 and 23.50W⋅m−1⋅K−1, respectively. The ceramic exhibited excellent high-temperature oxidation resistance at 800-1200 ℃ for up to 64h. Even after 64h of oxidation at 800 ℃ and 1000 ℃, the thickness of the oxide layer was only 2.09µm and 2.20µm, respectively. The oxidation behavior was controlled by a diffusion process. The rapid formation of a continuous and dense Al2O3 oxide layer effectively inhibited the inward diffusion of oxygen and the oxide layer is well bonded to the matrix.

Achieving high thermal conductivity and strong bending strength diamond/aluminum composite via nanoscale multi-interface phase structure engineering

Diamond/aluminum composites, as a new generation of thermal management materials, are caught in the dilemma between inhibiting the formation of Al4C3 and improving the performance. Herein, we proposed a strategy for nanoscale multi-interface phase structure engineering, utilizing a combination of magnetron sputtering and vacuum heat treatment to obtain diamond particles with nanoscale TiC-Ti layers. Prolonging the vacuum heating time increases the content of TiC, but results in significant differences in the morphology and coverage of TiC formed on the diamond(100) and (111) facets. First-principles calculations reveal that the work of adhesion and C-Ti reaction tendency of diamond(100)/Ti are stronger than those of diamond(111)/Ti, clarifying the difference in interfacial properties between diamond/Ti and diamond/TiC. Diamond-TiC-Ti configuration obtained in advance contributes to fabricating the composite with diamond-TiC-Al(Al3Ti) structure, and the multi-interface phase structure is beneficial to improve the interface bonding, adjust the acoustic mismatch, and inhibit the formation of Al4C3. (800 °C 0.5 h)@Ti-coated diamond(100 μm)/aluminum composite with the multi-interface phase exhibits excellent thermal conductivity(646 W m−1 K−1) and outstanding bending strength(358 MPa), exceeding 90 % of the theoretical prediction of the differential effective medium model. The performance of (800 °C 0.5 h)@Ti-coated diamond/aluminum composite is about 30 % higher than that of traditional Ti-coated diamond/aluminum composite. The TiC layer formed by increasing the heat treatment time is thicker and discontinuous, leading to a decrease in the thermal conductivity of the composite and a weakening effect of Al4C3 inhibition. We clarified the formation mechanism of interface structure related to diamond orientation by multi-scale characterization. Based on the thermal conductivity prediction models, the interface structures corresponding to different diamond orientations were considered, and the predicted values showed good consistency with the experimental results. By interface modification engineering, we overcome the dilemma of introducing modified layer to inhibit Al-C reaction while leading to additional interface thermal resistance, providing insights into the interfacial thermal transport mechanism.

Material properties of particleboards produced from Ciol®-treated wood shavings

ABSTRACT This study investigated the potential of wood particles from Ciol®-treated wood in particleboard production. Ciol® is a renewable formulation from water, citric acid, and sorbitol, which has been commercially developed as a promising alternative for wood modification. Radiata pine wood was impregnated with 60% and 85% concentrations of the Ciol® solution for 150 mins. The impregnated boards were cured and subsequently planned. Particleboards were thereafter produced from the wood shavings using urea formaldehyde (UF) and melamine urea formaldehyde resin (MUF). The boards were produced with or without the use of ammonium nitrate as a hardener. The wood particles and produced boards were characterized via analytical techniques and standard test methods. The effect of Ciol® treatment and its concentration on the properties of the shavings and the particleboards was investigated as well as the effect of the resin type on the panel properties. The use of MUF without the hardener gave the best bending strength of 13 N/mm² and modulus of elasticity of 3187 N/mm². However, there was no significant difference in the results obtained when the hardener was added to MUF resins. Recycling Ciol®-treated wood shavings in particleboard production proved to be a promising approach with MUF resins.

Effect of Hybrid Nanofillers on the Mechanical Characteristics of Polymethyl Methacrylate Denture Base Composite

The research study focused on enhancing the mechanical characteristics of polymethyl methacrylate (PMMA) denture bases. PMMA is commonly used in dentistry due to its easy fabrication, cost-effectiveness, and favourable physical properties. However, its limitations include low wear resistance, hardness, and mechanical strength, making it less suitable for long-term dental applications. To address these limitations, the study employed a combination of hybrid nano-fillers, specifically HNTs (halloysite nanotubes) and MWCNTs (multi-walled carbon nanotubes), at varying loading levels to improve the mechanical characteristics of the PMMA composite. These nano-fillers underwent treatment by using a coupling agent to enhance their compatibility with PMMA. Key findings of the research include that introducing HNTs/MWCNTs into the PMMA matrix led to a substantial increase in flexural strength, with a significant improvement of 109.1 MPa compared to unfilled PMMA. This indicates that the composite material became more resistant to bending or deformation. There was a substantial rise in flexural modulus values, suggesting improved stiffness in the nanocomposite compared to unfilled PMMA. In addition, the tensile strength of the PMMA composite increased by 64.4 MPa with the addition of the hybrid nano-fillers, indicating enhanced resistance to stretching or pulling forces. The study found that the improvement in flexural and tensile strength was dependent on the concentration of MWCNTs. Increasing the MWCNT concentration up to 0.75 wt.% led to improved mechanical properties, but further increases resulted in a reduction in PMMA properties. Although there was a modest improvement in Vickers hardness (approximately 18.93 kg/mm&amp;lt;sup&amp;gt;2&amp;lt;/sup&amp;gt;), the addition of HNTs/MWCNTs as hybrid nano-fillers effectively enhanced the properties of the PMMA nanocomposite. The study concludes that incorporating hybrid nano-fillers into PMMA could contribute to the longevity and durability of dental composites, addressing some of the material&amp;apos;s inherent limitations. The specific combination and concentration of nano-fillers played a crucial role in determining the mechanical properties of the resulting nanocomposite.

Effect of the Addition of Manganese Dioxide Nanoparticles on the Mechanical Properties of Concrete against Carbonation and Sulfate Attack

This study evaluates the impact of the addition of nanoparticles of anodic manganese dioxide (NAMD) on the mechanical properties and resistance to chemical attack of concrete. The research focused on nine concrete mixtures with water/cement ratios of 0.40, 0.45, and 0.50 and NAMD contents of 0, 5, and 10%. The properties of NAMD were analyzed, and fresh concrete properties such as temperature, unit weight, and consistency were measured. The compressive strength was determined at different ages (7, 14, 28, 56, and 90 days). The tensile and flexural strength were evaluated at 28 days, and the longitudinal change generated by the SO4Mg attack was monitored until 90 days. In addition, an accelerated carbonation test was performed on concrete samples with 28 days of curing exposed to an atmosphere of 6% CO2 for one week. The addition of NAMD did not significantly affect the temperature or unit weight of the fresh concrete, but it did influence the consistency. An increase in compressive, tensile, and flexural strength was observed, especially at early ages and for low w/c ratios. The addition of NAMD reduced the expansion of concrete exposed to magnesium sulfate, with 5% being the most effective dose, and reduced the carbonation rate of concrete by up to 40% in mixes with w/c ratios of 0.40 and 0.50. It was shown that the addition of 5% as an effective dose of NAMD improves the mechanical and durability properties of concrete, especially in mixtures with a low water/cement ratio, contributing to the improvement of the quality and strength of concrete.

Polyacrylonitrile fiber reinforced 3D printed concrete: Effects of fiber length and content

Polyacrylonitrile (PAN) fibers significantly improve the toughness, strength, and crack resistance of conventional concrete. This research explores the impact of PAN fibers, in lengths of 6 mm and 12 mm and dosages of 0 %, 0.1 %, 0.2 %, 0.3 %, and 0.4 %, on the rheology, extrudability, buildability, mechanical performance, and anisotropic characteristics of 3D printed concrete. Scanning electron microscopy (SEM) was used to examine the fiber distribution in the concrete. The findings show that as the PAN fiber content increases, the flowability and extrudability of the 3D printed concrete decrease. Optimal buildability was achieved with 6 mm PAN fibers at dosages between 0.1 % and 0.2 %. Compressive strength initially increases and then decreases with higher PAN fiber content, whereas flexural strength continuously increases with fiber content. The 12 mm PAN fibers outperform the 6 mm fibers in enhancing flexural strength, with a maximum improvement of 42.41 %. Increased fiber length and content lead to greater anisotropy and weaker interlayer bonds in the 3D printed concrete, with specimens showing the highest compressive and flexural strengths in the X and Y directions, respectively. SEM results indicate that the distribution of fibers is the main factor causing the mechanical anisotropy.

Recycling and optimum utilization of GFRP waste into low-carbon geopolymer paste for sustainable development

To provide an eco-friendlier alternative to traditional ordinary Portland cement (OPC) binder, this study utilized glass fiber reinforced polymer (GFRP) waste powder as a precursor material to prepare geopolymer paste (GP). Through a series of mechanical, thermal, and mineral admixture activation procedures, efforts are made to augment the reactivity of GFRP powder-based geopolymers. The research reveals that subjecting GFRP powder to a 30-min grinding process amplifies the compressive strength of GP by up to 37 %. Moreover, elevating curing temperatures to 60 °C leads to a substantial enhancement in the strength of GFRP powder-based GP, attributable to the formation of more amorphous N-A-S-H and C-(A)-S-H gels. However, prolonged grinding durations yield only marginal alterations in particle size, while curing at 80 °C demonstrates a detrimental effect on strength. The choice of resin exhibits a discernible impact on both workability and strength. Notably, pure glass fiber powder-based GP displays superior compressive strength but exhibits increased brittleness, whereas GFRP powder-based GP excels in flexural strength. Moreover, the inclusion of ground granulated blast furnace slag (GGBS) in the mixture accelerates setting time and reduces flowability of GFRP powder-based GP. Strength shows a positive correlation with GGBS content, although the impact on flexural strength is less pronounced compared to compressive strength. Life cycle assessment (LCA) showed GFRP powder-based GP with 50 % GGBS replacement had a 35 %–48 % lower Global Warming Potential (GWP)/strength ratio compared to OPC pastes. Furthermore, this formulation demonstrates a 15 % decrease relative to GGBS-based GP, and a reduction of 13 %–25 % compared to GGBS/Fly Ash (FA)-based GPs. These results underscore its potential as an environmentally preferable building material.