Electrical Conductivity Measurements Research Articles

Complex Permittivity Spectra of Granular Polymer Composites with Dispersed Ag-Coated Cu Flakes

Conductive particle-containing granular composites with tuneable negative permittivity are being studied to improve the performance of electromagnetic devices, such as shielding materials. In this study, we investigated the relative complex permittivity and electrical conductivity of granular composites of polyphenylene sulfide (PPS) resin and Ag-coated Cu flakes in the radio- to microwave-frequency range and compared them with those of PPS/bare Cu flake composites. Electrical conductivity measurements revealed that the PPS/Ag-coated Cu flake composites have a lower percolation threshold (φc) than the PPS/bare Cu flake composites, whereas the electrical conductivity of the PPS/Ag-coated Cu flake composites in the percolated particle state was higher at the same particle volume fraction. At particle contents above φc, a low-frequency plasmonic state of conduction electrons was achieved in the percolated particle chains in both composites, and negative permittivity spectra were obtained. The percolated PPS/Ag-coated Cu flake composites had a negative permittivity up to a higher frequency than the percolated PPS/bare Cu flake composites. Furthermore, the Drude model was used to analyze the negative permittivity spectra of the composites in the percolated particle state. The plasma frequency of the composites with percolated Ag-coated Cu flakes was higher than that of the composites with percolated bare Cu flakes. Thus, coating Ag on Cu particles improved the conductivity of the composite, leading to negative permittivity up to higher frequencies. This study contributes to the enhancement of the negative permittivity achieved by granular composites, which is useful for microwave technology applications.Graphical

3D printing carbon from aqueous all aromatic polyimides

All-aromatic polyimides serve as versatile precursors for carbon formation due to their high aromatic content and repeating unit planarity, which synergistically enables pyrolysis to ordered carbon. Recent publications disclosed facile synthetic methods for additive manufacturing (3D printing) of all-aromatic polyimides using a pendant salt approach for ultraviolet-assisted direct ink write (DIW) additive manufacturing. This manuscript describes the introduction of pendant sodium sulfonate functionality to the poly(amic acids), and water-soluble all-aromatic polyimide precursors displayed suitable rheological properties for DIW at room temperature and vat photopolymerization (VP) at 50 °C. These aqueous solutions enabled the formation of microporous polyimide structures with a direct freeze-casting method and dense structures with gradual heating under inert atmosphere to 200 °C and subsequent thermal post-processing to 400 °C. Furthermore, polyimide 3D structures function as efficient carbon precursors when pyrolyzed at 2000 °C under inert atmosphere. Raman spectroscopy revealed carbonized 3D structures with characteristic graphitic and disordered carbon bands, which was indicative of polycrystalline, disordered glassy carbon. Furthermore, electrical conductivity measurements suggest opportunities for the formation of 3D conductive structures.

Fundamental study on measurement of soil pH and electrical conductivity in batch tests for the determination of soil-soil solution distribution coefficient

Soil-soil solution distribution coefficient, Kd, is used to understand the mobility of radionuclides in the soil environment. Soil pH and electrical conductivity (EC) are the important factors affecting soil Kd, but existing methods for Kd employed different conditions, as well, standard soil pH and EC methods varied in the test conditions. It would be desirable to measure both pH and EC using the same soil solution for Kd with portable meters (non-glass electrode type) that need only a small liquid volume. In this study, at first, we utilized portable pH and EC meters to examine effects of different conditions on measurements, i.e., the water/soil ratios, contact time and standing time. The results showed that portable meter measurements of soil supernatant after 1 h shaking and 1 h standing could provide comparable pH and EC values with other standard soil tests. Then measurements of pH, and EC up to 168 h were carried out, considering the Kd methods for radiocesium (Cs); only slight differences in these values were observed compared to the standard test method. Considering these results, further analysis was carried out on the correlation between soil Kd-Cs and pH and found a clear decrease of Kd-Cs at pH < 5.

Assessment on the Effect of Rapid Urbanization on Groundwater Quality of Mirpur Area, Dhaka City, Bangladesh

Dhaka’s population is increasing day by day as more people are migrating towards Dhaka city for improving their level of living and for availing the cities amenities. Hence, this is creating pressure on the overall water quality of Dhaka city. The work intended to assess the groundwater standard in Mirpur area of Dhaka City, Bangladesh by analyzing eight (08) different physicochemical water quality parameters. In December 2023, six (06) separate water samples were taken throughout the dry season from six (06) sites across the area. The results showed that all sites had pH levels between 7.18 to 7.50, which is within acceptable ranges for drinking water quality and indicates neutral to slightly alkaline conditions. Total dissolved solids (TDS) continued to be far below safety limits (210–250 ppm), indicating that the water's mineral content was quite low. Electrical conductivity (EC) measurements fell within acceptable ranges (290-350 μS/cm), indicating suitable groundwater quality. Dissolved oxygen (DO) levels varied (3.7-9.3 mg/L), with some sites exhibiting satisfactory oxygenation while others raised concerns about potential water quality issues. Total hardness (TH) levels (330-900 mg/L) exceeded recommended limits (200-500 mg/L) at all sites, suggesting potential issues with water quality. However, chemical oxygen demand (COD) levels were minimal or zero (0-3 mg/L), indicating minimal organic pollution. Iron concentrations were generally low (0-0.05 mg/L). Total chlorine (TC) concentrations varied (0- 0.03 mg/L) across sites. In summary, the study emphasizes how crucial it is to continuously monitor and regulate the quality of groundwater in order to guarantee the sustainability and safety of water resources in the Mirpur region.

Simulation of Quench Rate by Jominy End Quench Test for 6082 Aluminium Alloys

In the present study, it is aimed to investigate the influence of quench rate on the hardness and electrical conductivity that obtained after artificial aging by using Jominy End Quench test method. The Jominy End Quench test bars were solution heat treated at 560°C for 3 hours. After solution heat treatment, water, spray, and air quenching medias were used in order to obtain different quench rates. After the quench, quench rate determination, hardness and electrical conductivity measurements were performed for three different quenching medias. Then, artificial aging heat treatment were applied to all samples at 180°C for 8 hours to understand the effect of quench rate on aging process. The relationship between quench rate, hardness and electrical conductivity have presented.

Enhanced gas sensing performance of ZnO and Pt-doped ZnO nanostructured films by chemical spray pyrolysis

This study focuses on the preparation and characterization of zinc oxide (ZO) and platinum-doped zinc oxide (Pt-ZO) nanostructured thin films using the chemical spray pyrolysis technique. Structural and morphological properties of the films were investigated via X-ray diffraction (XRD) and field emission scanning electron microscopy (FESEM). To understand the semiconducting nature and carrier dynamics, UV-Vis spectroscopy, electrical conductivity measurements, and a static gas sensing system were employed. The films exhibited crystallization in the hexagonal wurtzite structure with a preferred orientation along the (002) plane. FESEM images revealed the presence of small bright particles, particularly abundant in the 5 wt% Pt-doped ZO thin film, indicating the presence of platinum catalysts. Electrical conductivity measurements confirmed the semiconducting nature of the films. Optical parameters such as band gap and absorption index were obtained from UV-Vis spectroscopy. Gas sensing performance towards liquefied petroleum gas (LPG) showed that the 5 wt% Pt-doped ZO thin film exhibited a high response (69.9) to a 50 ppm concentration of LPG at 350 °C. The gas response and recovery times were observed to be 8 s and 12 s, respectively. These results are attributed to interactions between LPG molecules and adsorbed oxygen species on the sensor surface. Platinum atoms on the oxide surface facilitate the formation of oxygen vacancies and the dissociation of oxygen molecules at low temperatures, leading to increased adsorption and reaction with LPG molecules. This results in significant changes in the sensor's resistance, thereby amplifying the sensor response. The findings demonstrate the potential of Pt-doped ZO thin films for practical gas sensing applications.

Measurement of electrical conductivity of human tissue: A feasibility study of a novel time-domain approach

A straightforward, non-invasive experimental approach to the extraction of electrical conductivity of human tissue using the transient electromagnetic field coupling between two loop antennas is presented. The main objective of this initial study is to demonstrate the feasibility of the new time-domain (TD) methodology. The designed loop antennas and the experimental setup with its instrumentation are described. The presented results show that the proposed method is capable of obtaining accurate values of the electrical conductivity of human tissue.

Research on the Influence of Matrix Shape on Percolation Threshold Values for Current Flow Conducted Using the Monte Carlo Simulation Method

In this study, in order to determine the effect of matrices’ shape on the percolation threshold values, computer simulations were performed using the Monte Carlo method for a 200 × 200 square-shaped matrix and rectangular matrices containing the same number of nodes as the square matrix. Based on the simulations, the average values of the percolation thresholds and standard deviations for the current flow along and across the matrices were determined. It was determined that for a square-shaped matrix, the average values of the percolation thresholds in both directions of the current flow were the same. Extending the rectangular matrix while reducing its height causes the average value of the percolation threshold in the direction of the current flow along the matrix to increase from 0.592740 to 0.759847, while in the transverse direction, it decreases from 0.592664 to 0.403614. The values of the classical asymmetry coefficients of the probability distributions of the percolation thresholds for both directions of the current flow were determined. Histograms of the probability distributions of the percolation threshold values for a square-shaped matrix and rectangular matrices were made and compared with the normal distributions. It was found that the occurrence of two percolation thresholds in rectangular layers should be considered when analyzing the electrical conductivity measurements of nanocomposite thin films.

The Rectangular Niobium Oxyiodide Cluster Nb4OI10 – A Narrow Band‐Gap Semiconductor

AbstractA metal‐rich niobium oxyiodide was prepared by soft reduction of NbI4. The structure of the new compound Nb4OI10 was determined by single‐crystal X‐ray diffraction and contains a rectangular Nb4(μ4‐O) cluster that is interconnected into layers by iodide ligands. The local structure of the Nb4OI10 cluster bears a close relationship to a defect Nb6I11 structure. The two‐dimensional van der Waals material Nb4OI8I4/2] is a small band‐gap semiconductor (&lt;1 eV), as analysed by electrical conductivity measurements, photoresponse, experimental band gap determination, and band structure calculation.

Identification of sodicity-tolerant banana varieties to harness the salt-affected ecosystem

"Salt Affected Soils" (SAS) refers to a category of soils that contain either an excess of soluble salts or exchangeable sodium. Soils are divided into four categories: normal, saline, sodic, and saline-sodic, based on the electrical conductivity (EC), pH and exchangeable sodium percentage (ESP) measurements. At the Horticultural College and Research Institute for Women in Trichy, fifteen genotypes of bananas were assessed for growth, yield, and physiological parameters in a saline-sodic environment. Four replications of the field experiment were set up in RBD and evaluated for three years. The growth physiological and biochemical characters were recorded in the seventh month after planting (MAP), and the bunch characters were recorded at harvest time. FHIA 1 (83.4%), Saba (81.0%) and Karpooravalli (78.0%) had the highest relative water content. The highest yield was recorded in FHIA-1 (23.5 kg), Saba (22.2 kg), Udhayam (22.5 kg) and Karpooravalli (22.0 kg). The sodicity injury symptoms in the leaves were evaluated using a scoring technique, and the genotypes FHIA-1(1.0) Saba recorded the lowest score for sodicity damage. A significant negative correlation was observed between salt injury degree and leaf K+/Na+. So, the varieties that maintain higher K+/Na+ ratio in leaf and root are salt tolerant. The general ranking of the banana varieties for salt tolerance was FHIA 1 &gt; Saba &gt; Karpooravalli &gt; Bangrier &gt; Ash Monthan &gt; Veneetu Mannan &gt; Udhayam. A comparative field trial for the 15 banana types showed that Saba, FHIA-1 and Karpooravalli could withstand sodic conditions in the field in terms of bunch characteristics, biochemical parameters, and plant growth. Grand Naine, Rasthali and CO 1 were vulnerable to sodicity stress. Regardless of cultivar, sodicity stress increased the days needed for shooting and harvest.

Structure and Potential Application of Surfactant-Free Microemulsion Consisting of Heptanol, Ethanol and Water

Microemulsions, which are thermodynamically stable and isotropic mixtures of water, oil, and surfactants, attract significant research interest due to their unique physicochemical properties and diverse industrial applications. Traditional surfactant-based microemulsions (SBMEs) stabilize the interface between two typically immiscible liquids, forming various microstructures such as oil-in-water (O/W) droplets, water-in-oil (W/O) droplets, and bicontinuous phases. However, the use of surfactants poses environmental concerns, cost implications, and potential toxicity. Consequently, there is increasing interest in developing surfactant-free microemulsions (SFMEs) that offer similar benefits without the drawbacks associated with surfactants. In this study, we explore the formation and characteristics of a new surfactant-free microemulsion in a ternary system comprising water, ethanol, and heptanol. Advanced techniques are employed to characterize the microstructures and stability of surfactant-free microemulsions. These include electrical conductivity measurements, surface tension analysis, dynamic light scattering (DLS), and Fourier transform infrared spectroscopy (FTIR). These methods have been extensively used in previous research on surfactant-free microemulsions (SFMEs) to reveal the properties and interactions within microemulsion systems. The area of interest is identified using these techniques, where silica nanoparticles are subsequently synthesized and then visualized using transmission electron microscopy (TEM).

Coexistence of multiple magnetic interactions in oxygen-deficient V2O5 nanoparticles

This paper reports on the spin glass-like coexistence of competing magnetic orders in oxygen-deficient V2O5 nanoparticles with a broad size distribution. X-ray photoelectron spectroscopy yields the surface chemical stoichiometry of nearly V2O4.65 due to significant defect density. Temperature-dependent electrical conductivity and thermopower measurements demonstrate a polaronic conduction mechanism with a hopping energy of about 0.112 eV. The V2O5-δ sample exhibits strong field as well as temperature-dependent magnetic behaviour when measured with a SQUID magnetometer, showing positive magnetic susceptibility across the temperature range of 2-350 K. Field-cooled and zero-field-cooled data indicate hysteresis, suggesting glassy behaviour. The formation of small polarons due to oxygen vacancy defects, compensated by V4+ charge defects, results in Magneto-Electronic Phase Separation (MEPS) and various magnetic exchanges, as predicted by first-principle calculations. This is evidenced by the strong hybridisation of V orbitals in the vicinity of vacant oxygen site. An increase in V4+ defects shows an antiferromagnetic (AFM) component. The magnetic diversity in undoped V2O4.9 originates from defect density and their random distribution, leading to MEPS. This involves localised spins in polarons and ferromagnetic (FM) clusters on a paramagnetic (PM) background, while V4+ dimers induce AFM interactions. Electron paramagnetic resonance spectra measured at different temperatures indicate a dominant paramagnetic signal at a g-value of 1.97 due to oxygen defects, with a broad FM resonance-like hump. Both signals diminish with increasing temperature. Neutron diffraction data rules out long-range magnetic ordering, reflecting the composition as V2O4.886. Despite the FM hysteresis, no long-range order is observed in neutron diffraction data, consistent with the polaron cluster-like FM with MEPS nature. This detailed study shall advance the understanding of the diverse magnetic behaviour observed in undoped non-magnetic systems.

Structural and electronic transformations in TiO2 induced by electric current

In-situ diffuse neutron scattering experiments revealed that when electric current is passed through single crystals of rutile TiO2 under conditions conducive to flash sintering, it induces the formation of parallel planes of oxygen vacancies. Specifically, a current perpendicular to the c-axis generates planes normal to the (132) reciprocal lattice vector, whereas currents aligned with the c-axis form planes normal to the (132) and to the (225) vector. The concentration of defects increases with incresing current. The structural modifications are linked to the appearance of signatures of interacting Ti3+ moments in magnetic susceptibility, signifying a structural collapse around the vacancy planes. Electrical conductivity measurements of the modified material reveal several electronic transitions between semiconducting states (via a metal-like intermediate state) with the smallest gap being 27 meV. Pristine TiO2 can be restored by heating followed by slow cooling in air. Our work suggests a novel paradigm for achieving switching of electrical conductivity related to the flash phenomenon.

Electrical conductivity model for reactive porous media under partially saturated conditions with hysteresis effects

The electrical conductivity of a porous medium is strongly controlled by the structure of the medium at the microscale as the pore configuration governs the distribution of the conductive fluid. The pore structure thus plays a key role since different geometries translate in variations of the fluid distribution, causing different behaviors measurable at the macroscale. In this study, we present a new physically-based analytical model derived under the assumption that the pore structure can be represented by a bundle of tortuous capillary tubes with periodic variations of their radius and a fractal distribution of pore sizes. By upscaling the microscale properties of the porous medium, we obtain expressions to estimate the total and relative electrical conductivity. The proposed pore geometry allows us to include the hysteresis phenomenon in the electrical conductivity estimates. The variations on these estimates caused by pore structure changes due to reactive processes are accounted by assuming a uniform dissolution of the pores. Under this hypothesis, we describe the evolution of the electrical conductivity during reactive processes. The expressions of the proposed model have been tested with published data from different soil textures, showing a satisfactory agreement with the experimental data. Hysteretic behavior and mineral dissolution are also successfully addressed. By including hysteresis and mineral dissolution/precipitation in the estimates of the electrical conductivity, this new analytical model presents an improvement as it relates those macroscopic physical phenomena to its origins at the microscale. This opens up exciting possibilities for studies involving electrical conductivity measurements to monitor water movement, and hysteretic and reactive processes in porous media.

Effect of Ca doping at A or B sites on electrochemical performance of La1.9In0.1Ce2O7 proton conductors

Fluorite proton conductors La1.8In0.1Ca0.1Ce2O7-δ and La1.9In0.1Ce1.9Ca0.1O7-δ (LICaC and LICCa) were synthesized by solid state reaction. The effect of Ca doping at A site or B site on La1.9In0.1Ce2O7 was studied by X-ray diffraction (XRD), Inductively Coupled Plasma Mass Spectrometry (ICP), scanning electron microscopy (SEM) and electrical conductivity measurement. XRD shows that the LICaC and LICCa were successfully synthesized, and Ca was doped to the expected sites. The measured mass ratios of each element by ICP were in good agreement with their theoretical values. In addition, SEM also found that the surface of the sample was dense without holes. The conductivities of LICaC and LICCa were studied at 400–800 ℃, and their highest conductivities were 7.28×10−4 and 5.56×10−3 S·cm−1, respectively. The conductivity of LICCa doped at the B site is better than that of LICaC doped at the A site. In the wet air at 800 ℃, the proton transference numbers of LICaC and LICCa are 0.5 and 0.52, respectively. LICaC and LICCa were used as electrolytes to prepare fuel cells and their performance was tested. The electrolyte thickness of LICAC and LICCA was about 0.9 mm. At 700 ℃, the maximum power density of LICaC and LICCa electrolyte-based single cells are 124.51 and 162.26 mW cm−2, respectively. The results show that LICCa has good proton conductivity and has potential as an electrolyte for high-performance fuel cells.

Synthesis and Characterization of Coconut-Derived Graphene Nano Sheet (GNS) and Its Properties in Nickel/GNS and Zinc/GNS Hybrid Electrodes

This study introduces a sustainable method of producing a graphene nano sheet (GNS) from coconut shells and investigates its application in GNS, Ni/GNS, and Zn/GNS electrodes for advanced energy storage devices. The GNS was synthesized in a scalable manner using a pyrolysis and impregnation technique, with its successful synthesis verified by X-ray diffraction (XRD), energy dispersive X-ray spectroscopy (EDX), Raman spectroscopy, and electrical conductivity measurement characterizations. The study highlights the enhanced performance of Zn/GNS electrodes, which outperform both pure GNS and Ni/GNS variants. This superior performance is attributed to the smaller particle size of Zn (mean = 2.356 µm) compared to Ni (mean = 3.09 µm) and Zn’s more favourable electron configuration for electron transfer. These findings demonstrate the potential of bio-derived GNS composites as efficient, high-performance electrodes, paving the way for more sustainable and cost-effective energy storage solutions.

Electrochemical and computational evaluation of hydrazide derivative for mild steel corrosion inhibition and anticancer study

In the present study the authors’ main goal is to avoid the corrosive attack of the chloride ions of 3.5% NaCl solution in saline medium on the mild steel (MS), by addition of small amount of a new derivative of the hydrazide called ligand (HL), as a corrosion inhibitor. This study had been achieved by employing different electrochemical measurements such as, open circuit potential (OCP), electrochemical impedance spectroscopy (EIS) and potentio-dynamic polarization (PDP) methods. The results of the electrochemical test (OCP), showed that, the open circuit potential of the mild steel in saline solution, was guided to more positive direction in presence of the ligand (HL), at its ideal concentration (1 × 10−3 M), compared to the (OCP), of the mild steel in absence of (HL). The results of the electrochemical methods, EIS and PDP presented that, the ligand (HL), was acted as a good corrosion inhibitor for hindering the corrosion process of the mild steel in 3.5% sodium chloride, as it was recorded a good percentage of the inhibition efficiency (77.45%, 53.41%, by EIS and PDP techniques respectively), at its optimum concentration (1 × 10−3 M). Also, the corrosion rate of the mild steel in the saline medium without (HL), was listed about (0.0017 mm/year), while in existence of (HL), was decreased to a value about (0.00061 mm/year). As well, some of electrical properties of (HL), and its derivative [Pd(II), Cr(III), and Ru(III)], complexes were investigated such as; the activation energy (Ea(ac)), which recorded values in the range of 0.02–0.44 (eV) range and electrical conductivity which listed values at room temperature in the range of 10−5–10−8 S.cm−1. The results of the AC and DC electrical conductivity measurements for (HL), and its derivative [Pd(II), Cr(III) and Ru(III)] complexes indicate semiconducting nature which suggests that these compounds could be used in electronic devices. Also, the complexes exhibited higher conductivity values than (HL). Photophysical studies showed good florescence properties of HL that indicated that it can be used to determine most of the drugs with no fluorescence properties by quenching and calculating quantum yield. Moreover, the hydrazide ligand (HL), has shown selectivity as an active anticancer candidate drug for both breast and colon cancer in humans. Density function theory demonstrated that, the frontier molecular orbital HOMOs of the complexes have exhibited similar behavior and the charge density has localized in the metallic region of all the studied complexes. Also, the values of the energy gap of the ligand (HL), and its complexes Pd(II), Cr(III) and Ru(III), had been arranged in this order HL > Cr(III) > Ru(III) > Pd(II). All characterization using different spectroscopic techniques were reported to elucidate the proposed structures such as; thermal analysis, elemental analysis of C, H, and N atoms, spectral analysis using IR, UV, 1H NMR techniques, scanning electron microscopy and energy dispersive X-ray analyses.

Characterizing Flow Dynamics in a Two-dimensional Flow Cell: Developing Methodologies for Enhanced Subsurface Contaminant Remediation Research

This study used a two-dimensional (2-D) flow cell apparatus (25 cm × 25 cm × 1 cm) to characterize water flow and contaminant transport in porous media. The primary objective was to enhance the understanding of flow dynamics and contaminant behavior in controlled 2-D environments, which is crucial for optimizing the application of remediation technologies to treat contaminants in saturated and unsaturated soil conditions. The 2-D cell was designed with transparent walls to simulate subsurface conditions using medium grained sand, allowing for precise control and observation of fluid movement under saturated and quasi-saturated (trapped air) conditions. Visualization techniques and flow measurement tools were employed to capture detailed data on flow patterns, velocities, and dispersion characteristics. Analysis of breakthrough curves for salt tracer tests using electrical conductivity measurements, alongside varying flow rates, flow fractions, and port configurations, provided significant insights into fluid behavior and contaminant transport. The study also explored the effects of varying salt concentrations (and solution densities) on flow dynamics, contributing to a better understanding of the role of contaminant concentration in contaminant plume development and remediation processes. Visual analysis using dyed contaminant complemented the quantitative data, offering real-time observations of flow patterns and contaminant distribution. A custom-built apparatus was used to control the hydraulic head of multiple outlet ports to sample water from different depths. The experiments demonstrated that gravity plays a crucial role in solute (salt) breakthrough, with lower ports showing earlier breakthrough. Flow fields formed vertically, from bottom-to-top, and horizontally, from inlet-to-outlet, with lower portions advancing sooner. However, multi-port configurations, especially involving five ports, disrupted the sequential breakthrough order, possibly due to convection in the clear well that formed the outlet boundary of the flow cell. These findings will support research students in conducting similar experiments with flow and transport that varies with depth, with future insights for professionals in developing and optimizing remediation strategies related to subsurface contaminant flow. Special thanks are extended to Liam Price, Julia-Barnes James, and Brooke Belfall who were helpful during the research and the experimentation process.

Biocontrol of rusted root rot in Panax ginseng by a combination of extracts from Bacillus amyloliquefaciens YY8 crude protein and Enterobacteriaceae YY115 ethyl acetate

BackgroundRusted root rot is one of the most common root diseases in Panax ginseng, and Cylindrocarpon destructans is one of the main pathogenic fungus. The objective of this study was to screen and explore the extracts of biocontrol bacteria isolated from ginseng rhizosphere soil against Cylindrocarpon destructans.ResultsBacterial strains Bacillus amyloliquefaciens YY8 and Enterobacteriacea YY115 were isolated and found to exhibit in vitro antifungal activity against C. destructans. A combination of crude protein extract from B. amyloliquefaciens YY8 and ethyl acetate extract from Enterobacteriacea YY115 in a 6:4 ratio exhibited the strongest antifungal activity against C. destructans. Measurements of electrical conductivity, protein content, and nucleic acid content in suspension cultures of C. destructans treated with a mixture extracts indicated that the extracts disrupted the cell membranes of rusted root rot mycelia, resulting in the leakage of electrolytes, proteins, and nucleic acids from the cells, and ultimately inhibiting the growth of C. destructans. The combined extracts suppressed the infection of ginseng roots discs by C. destructans effectively.ConclusionThe extracts obtained from the two bacterial strains effectively inhibited C. destructans in P. ginseng. It can provide scientific basis for the development of new biological control pesticides, reduce the use of chemical pesticides, and promote the sustainable development of agriculture.

High temperature setup for measurement of Hall coefficient and electrical conductivity of thermoelectric materials.

An experimental setup has been developed for the simultaneous measurement of the Hall coefficient (RH) and electrical conductivity (σ) of thermoelectric (TE) specimens in the temperature range of 300-700K. The van der Pauw geometry is utilized for the RH and σ measurements. The sample holder geometry has been designed for diverse TE specimen dimensions and easy sample mounting. A special feature of the holder geometry is that the same sample can be used for other relevant thermoelectric measurements such as the Seebeck coefficient and thermal diffusivity. This minimizes measurement errors associated with compositional or doping inhomogeneities. In the absence of high temperature standard reference materials for Hall coefficient measurements, silicon samples with different doping concentrations have been used to verify the accuracy of the instrument. Additionally, the electrical conductivity data have been validated by measurements on the same samples in a calibrated setup. Repeat measurements indicate a maximum standard deviation of ±3% and ±0.5% for the RH and σ data in the studied temperature range. Furthermore, comparisons with the calibrated setup indicate deviations within ±3% for the σ data. The suitability of the measurement setup for TE specimens has been demonstrated using measurements on n-type (Mg2Sn) and p-type (Mg3Sb2) specimens with carrier concentrations in the range of 1019-1020cm-3.