Subscript textViscosity, coefficient of thermal expansion, glass transition temperature and dilatometric softening temperature of soda-lime-silicate glass doped with Li2O were investigated by the rotating crucible viscometer and dilatometry, the melting temperature and activation energy for viscous flow of the studied melt were derived on the basis of Arrhenius Equation, in order to reveal the effects of Li2O on the properties of soda-lime-silicate glass. The results showed that the viscosity of soda-lime-silicate glass was effectively decreased and the melting temperature decreased from 1457°C to 1420°C with the increase of Li2O from 0 to 1.0wt%, furthermore, the Tgand Tsreduced 30~40°C. The ΔT responded to the range of viscosity of glass formation (η=103-107Pa•s) increased from 309.84°C to 313.45°C, and the activation energy for viscous flow decreased form 178.47 kJ•mol-1to 168.34 kJ•mol-1. The CTE α(25~400°C)of specimen doped with 0.4% Li2O was 92.048×10-6°C-1and the lowest of the samples.