Commercial Pure Titanium Research Articles

Development of Ti-Zr-Nb-Ta-Ag high entropy alloy for dental implants: In vitro corrosion behavior, antibacterial effect, and surface characteristics

This study presents a new biological high-entropy alloy (Bio-HEA) composed of 35Ti-35Zr-20Nb-5Ta-5Ag (at. %) for potential dental implant applications. The Bio-HEA underwent processing for various durations of mechanical alloying, followed by compaction and sintering. The processed Bio-HEA was tested for corrosion resistance in an artificial saliva medium, antibacterial properties, and surface characteristics. Surface topography and wettability were investigated using atomic force microscopy, surface profilometry, and contact angle measurements. Mechanical alloying, X-ray diffraction, and scanning electron microscopy revealed the formation of a solid-solution Bio-HEA with body-centered cubic crystal structures, with phase variations depending on the processing conditions. The Bio-HEA exhibited significantly higher microhardness values (4.38 GPa and 5.35 GPa) than commercial pure titanium (CPTi) and Ti-6Al-4V alloy, respectively. An increased ball-milling time resulted in higher microhardness for Bio-HEA and enhanced in vitro corrosion resistance in artificial saliva compared to CPTi. This was evidenced by a significant nobler shift of approximately 200 mV in the corrosion potential, with a prominent decrease of approximately two orders of magnitude in the corrosion current density and a higher charge transfer resistance. Additionally, the Bio-HEA demonstrated a lower contact angle compared to that of the Ti-6Al-4V alloy and CPTi. The Bio-HEA achieved antibacterial efficiencies of 91.76 % and 93.0 % compared to Ti-6Al-4V alloy and CPTi, respectively. The enhanced microhardness, antibacterial properties, in vitro corrosion resistance in artificial saliva, and wettability of Bio-HEA compared to commercial Ti-6Al-4V alloy and CPTi makes it a promising candidate for dental bioimplant applications.

Impacts of the alloying elements and thermo-mechanical processing on the phase stability, crystalline structure, microstructure, and selected mechanical properties of Ti-(10-x)Al-xV (x = 0, 2, and 4 wt%) alloys targeted as external prostheses

This study aimed to characterize Ti-Al-V alloys submitted to thermo-mechanical processes and evaluate their impact on the crystalline structure, microstructure, coefficient of thermal expansion (CTE), selected mechanical properties, and cytotoxicity. X-ray diffraction (XRD) analysis revealed a major α phase, with V acting as a β-stabilizer. The cooling rate and the plastic deformation contributed to the formation of minor martensitic αʹ and β phases, with notable variations in cell parameters. The Energy-Dispersive XRD indicated the CTE was dependent on the alloying elements. Ti-10Al and Ti-8Al-2V depicted Widmanstätten laths and basket-weave structures, while Ti-6Al-4V showed typical features of β grain boundaries. Thermodynamic predictions aligned with the observed phase compositions. Vickers micro-hardness tests yielded values surpassing those of commercially pure titanium (CP-Ti), attributed to the synergistic effects of solid solution, phase precipitation, and strain hardening effects. And, elastic modulus approximated that of CP-Ti, largely due to the α phase's predominance. The solution treatment reduced the elastic modulus compared to the hot-rolled samples due to the stress relief and αʹ and β phase precipitation. Preliminary cytotoxicity assays confirmed the non-toxicity of the samples to cell viability. These findings suggest that the solutionized Ti-10Al sample is an economically viable candidate for fabricating external prostheses.

Enhancing Titanium Osteoconductivity by Alkali-Hot Water Treatment.

Titanium and its alloys are essential in orthopedic and dental treatments owing to their high strength, corrosion resistance, and superior biocompatibility compared with those of other metals. However, titanium alloys are bioinert. Previous studies have indicated that alkali treatment (AT) is a straightforward method to create a surface oxidization layer on titanium, thereby improving its bioactivity. Herein, alkali-hot water pretreatment was used to enhance the osteoconductivity of titanium and to identify a simple and efficient means of enhancing the interaction between osteoblasts and implants for clinical applications. Commercial pure titanium plates were ground (CP Ti) and subjected to alkali solution and hot water treatments (AWT). Single-process CP Ti specimens were prepared via either AT or hot water treatment (WT). Network-like structural features were observed in the AT specimens and were further refined and densified in the AWT specimens. Water contact angle testing revealed that the hydrophilicity of the titanium specimen (80° for CP Ti) increased by 19° for the AT specimens but decreased by 59° for the AWT specimens. Mouse preosteoblasts (MC3T3-E1 cells) were used for in vitro evaluation. After 24 h of culturing, the number of attached MC3T3-E1 cells on the AWT specimens was 1.5 times larger than that on the CP Ti specimens, suggesting that the alkali-hot water treatment enhanced the initial cell attachment. Cell proliferation evaluation indicated that fewer cells were detected in the AT and AWT specimens compared with those in the CP Ti or WT specimens. However, osteogenic differentiation evaluation on day 10 revealed a 1.5-fold higher alkaline phosphatase expression in cells cultured on the AWT specimens than in cells cultured on the CP Ti specimens. These findings demonstrate the good cytocompatibility and osteoconductivity of AWT Ti, highlighting its benefits in orthopedics and dental treatments.

Small fatigue crack behavior of CP-Ti in thin-walled cruciform specimens under biaxial loading

This study investigates the small fatigue crack propagation behavior of commercially pure titanium (CP-Ti) using thin-walled cruciform specimens under in-plane biaxial loading, considering the effects of biaxial ratio and phase angle. Increasing phase angle results in more secondary cracks merging with main cracks perpendicular to the rolling direction (RD) and transverse direction (TD), a phenomenon attributed to the rise in shear stress that accelerates main crack growth. Higher loading biaxiality or a lower phase angle leads to decreased crack propagation rates and increased biaxial fatigue life. Electron backscatter diffraction (EBSD) analysis reveals that when the maximum normal stress aligns with the RD, prismatic slip primarily governs crack propagation, thereby accelerating crack propagation rates. Conversely, alignment with the TD reduces prismatic slip activity and crack propagation rates. Under equi-biaxial loading, prismatic slip activity decreases further, and crack propagation is dominated by multiple slip and twinning, consequently resulting in the slowest propagation rates. Additionally, a higher proportion of prismatic slip under high phase angle also accelerates crack propagation. Finally, incorporating Findley equivalent stress into the Chapetti model, which considers the crack length-dependent threshold effect, a highly accurate biaxial small fatigue crack propagation rate model is proposed.

Fabrication of TiN-doped Ti nanocomposites with high strength and ductility by plasma-assisted ball milling and laser powder bed fusion

An efficient method to fabricate titanium nitride (TiN)-doped titanium (Ti) nanocomposites through a combination of plasma milling, plasma spheroidization, and laser powder bed fusion (LPBF) was developed to obtain Ti-based materials with high strength and ductility from commercially pure titanium (CP-Ti). Nitrogen plasma milling and plasma spheroidization were used to fabricate Ti-TiN nanocomposites, which were mixed with CP-Ti powder at a 1:9 ratio and printed by LPBF forming. The resulting materials possessed a dual-scale morphology with both coarse lath-like and fine acicular-like grains. The Ti-TiN nanocomposites possessed higher hardness and tensile strength and lower ductility than those of the control sample without TiN. The mechanical properties of the LPBF-printed Ti-TiN nanocomposites were improved compared with those of LPBF-printed CP-Ti because of the TiN particles and resulting dual-scale structure. Nitrogen plasma milling provides a simple route to fabricate TiN nanophase-reinforced Ti-based nanocomposites suitable for LPBF printing.Graphical

Investigation of mechanical and wettability properties of commercial pure titanium by surface mechanical attrition treatment

The examination of mechanical and wettability properties of commercial pure titanium (CP-Ti) introduced a novel challenge. The microstructure of samples was analyzed by using OM and SEM micro-images. In this study, the hardness of the surface and cross section of samples was evaluated, and the effect of several surface mechanical attrition treatments (SMATed) on samples was examined. Also, the tensile test was done to compare the effect of SMAT duration on mechanical properties of samples. The contact angle method was then employed to investigate the impact of SAMT duration on the wettability trend. According to results, as the treatment time increases, twins become evident in the deeper layers of the samples. In contrast, the near-surface twins are shorter than those found in the deeper material, signifying the presence of finer grains. Moreover, the elevated hardness in SMATed samples can be attributed to several key factors, including cold work, a rise in defects and twins, and grain refinement. The surface hardness increases across the sample series (up to Ti6) due to the substantial energy input. Nevertheless, it is anticipated that further continuation of the process will result in a constant surface hardness. The increased strength observed in SMATed samples can be attributed to factors such as reduction in grain size and the formation of twins. The wettability results show that the treated surfaces exhibited a significant change in wettability compared to the untreated samples, with a 25% reduction in the contact angle. This is attributed to the surface modifications induced by the treatment process, which introduced more hydrophilic functional groups. The results also show that after 4 h of treatment, the contact angle increases, suggesting that the trend may plateau with additional treatment time.

Influence on the properties of TMCs of ceramic and intermetallic composite reinforcements (B4C, TixAly and TixSiy) fabricated by inductive hot pressing

Ambitious and competitive, the aerospace industry continuously demonstrates to be one of the leading engineering sectors either at exigence and new technologies development. As lightning the weight of aircrafts is one of the main targets, the spotlight is usually on material research by which new ones may be produced to pursue this aim and still offer the necessary performances. The combination of the properties of titanium and other materials as reinforcements provides really interesting results as titanium matrix composite materials, also known as TMCs. Various samples of titanium matrix composite materials with different reinforcements have been under study to determine the influence of the reinforcements and their respective proportions on the properties of the material. These samples composed of grade 1 commercially-pure titanium as matrix and B4C, TixAly and TixSiy as reinforcements, have been manufactured through powder metallurgy in the same conditions of temperature and pressure via Inductive Hot Pressing (IHP). A total of eight composite materials have been arranged in several different groups to confront their compositions. Thus, this analysis reports results for the influence of the powder size of the matrix and the ceramic reinforcement, the effect of varying the volumetric composition of B4C, and the selection of different intermetallic reinforcements. These tests and the obtained information serve for a project in which the main goal is to determine which compositions of the studied composite materials reach a high enough specific stiffness for a suitable application in the aerospace industry.

An Experimental and Simulation Study on the Formability of Commercial Pure Titanium Foil.

In order to understand the formability of as-received tempered commercial pure titanium grade 2 foils (CP Ti Gr2) with a thickness of 38 µm, a series of micro limited dome height (µ-LDH) tests were conducted in quasi-static speed (0.01 mm/s) at room temperature without the use of a lubricant. A technique developed at NIU was also used to create micro-circular grids (ϕ50 μm) on the as-received material. The forming limit curve (FLC) of the CP Ti Gr2 foils was obtained through the proposed µ-LDH test. For having mechanical properties of the CP Ti Gr2 foils for LS-Dyna FEA (Finite Element Analysis) simulations, a series of tensile tests in three directions were also conducted at room temperature with the same speed. The obtained FLC has been validated using a micro deep drawing case study in which both FEA simulations and experiments were conducted and compared. It has been proven in this study that the FLC obtained using the proposed µ-LDH test can be used for an extremely thin sheet-metal-forming process by the automotive, aerospace, medical, energy, and electronic industries, etc., right away for product design, forming process development, tool and die designs, and simulations, etc.

Bovine Mineral Grafting Affects the Hydrophilicity of Dental Implant Surfaces: An In Vitro Study.

Wettability is recognized as an important property of implant surfaces for ensuring improved biological responses. However, limited information exists on how bone grafting procedures including materials influence the hydrophilic behavior of implant surfaces. This in vitro study aimed to investigate the influence of two bovine grafting materials after hydration on the wettability of four different disk surfaces: commercially pure titanium (CP-Ti), titanium-zirconium dioxide (TiZrO2-Cerid®), zirconia (SDS®), and niobium. Wettability tests were performed on each of the four implant surfaces with a solution of 0.9% sodium chloride after mixture with W-boneTM (Group A) or Bio-Oss® (Group B) or 0.9% sodium chloride alone (Group C). In total, 360 contact angle measurements were completed with n = 30 per group. Statistical analysis was performed using a one-way analysis with variance (ANOVA) test with a significant mean difference at the 0.05 level. For pure titanium, Group A demonstrated increased hydrophilicity compared to Group B. Both TiZrO2 and zirconia showed significant differences for Groups A, B and C, exhibiting a decrease in hydrophilicity after the use of bovine grafting materials compared to titanium surfaces. Niobium remained consistently hydrophobic. In summary, this study revealed that bovine grafting materials may diminish the hydrophilicity of zirconia surfaces and exert varied effects on titanium and niobium. These findings contribute to the understanding of implant surface interactions with grafting materials, offering insights for optimizing biological responses in implantology.

In-plane biaxial low-cycle dwell fatigue behavior of CP-Ti based on DIC method

This study investigates the biaxial dwell fatigue behavior of commercial pure titanium (CP-Ti) under different load ratios and dwell times. The evolution of mean strain, ratcheting strain, and creep strain was systematically analyzed. The findings reveal that with the decrease of load ratio or the increase of dwell time, both ratcheting and creep strain exhibit an upward trend. The interaction between ratcheting strain and creep strain promotes crack initiation and propagation. The statistical analysis of crack paths by the digital image correlation (DIC) method indicates that crack initiation occurs between 0.7Nf and 0.8Nf, and fatigue failure is governed by the maximum principal strain. Moreover, the electron backscatter diffraction (EBSD) analysis results indicate that as the load ratio increases, the activity of prismatic slip systems decreases, while the activities of other slip systems and twinning modes increases. To enhance predictive accuracy, a modified SWT model by incorporating time-dependent creep damage and anisotropy is proposed for life prediction under biaxial dwell fatigue conditions.

Increase in elastic and hardness anisotropy of titanium with oxygen uptake due to high temperature oxidation: A multimodal framework using high speed nanoindentation mapping

Titanium and its alloys combine an important mechanical anisotropy and a high capacity to dissolve oxygen. The detailed evolution of the elastic compliance of titanium as a function of its oxygen content is only partially known, despite its importance in structural applications. Here, high speed nanoindentation mapping (HSNM) was conducted on a grade 2 commercially pure titanium (CP-Ti) to probe elastic and hardness anisotropy as well as property evolution as a function of the oxygen content within Ti using pre-oxidized specimens. The oxygen concentration investigated ranged from 600 ppm to 20% atomic. Pre-oxidation of the CP-Ti was performed at 700 °C for 100 h under air to create a gradient of oxygen content within the metal, denoted oxygen-rich layer (ORL). Local oxygen content was quantified using microprobe analyses (EPMA) and crystal orientation using electron backscattered diffraction (EBSD). Reduced modulus and hardness maps were obtained on the pre-oxidized sample within the ORL and far from the ORL using large but highly resolved nanoindentation technique in continuous stiffness measurement (CSM) mode. Data merging techniques were used on this multi-modal dataset to statistically link local mechanical properties to chemical and crystal orientation information. Oxygen insertion in the Ti lattice was found to significantly increase the hardness and elastic moduli of titanium and was correlated to orientation of the c-axis of the α-Ti as a function of the nanoindentation loading direction. Using the Vlassak and Nix theory, it was possible to identify the evolution of the Cij terms of the stiffness matrix as a function of the oxygen content up to 20% at. in O.

Development of high hard TiB–TiB2 coatings on Ti implants for bio-tribological applications; applying Box-Behnken design and actual wear analyzing in simulated body fluids

This research focuses on the enhancement of the tribological behavior of commercial pure titanium (Cp-Ti) in a simulated body fluid (SBF) via surface reinforcement by titanium borides. The protective boride coatings were formed through the pack cementation process at two different temperatures (950 and 1050 °C) to create diverse hard compositions of TiB and TiB–TiB2 in the coating, with hardness of 1032 and 1291 Hv, respectively. The roughness and wettability of top surfaces were evaluated before the tribology studies due to their impacts on the tribology behavior. Box-Behnken design (BBD) was applied to investigate the effects of the wear parameters in dry and SBF environments. The duration of the wear tests was 53, 35, and 26 min for low, medium, and high speed. It was found that the abrasion wear type was dominant at the beginning of sliding, and then changed to the plastic deformation in the dry conditions, while there is no sign of the abrasion and adhesion wear features at the surface of the reinforced samples abraded in the SBF solution. Results confirmed a high coincidence between BBD predictions and actual findings. The released debris from the coatings was also investigated to find origins. Results showed that majority of the debris in the SBF solution belonged to the calcium phosphate particles demonstrating the bioactivity of the TiB–TiB2 coatings. According to findings, hard TiB–TiB2 coatings could significantly improve the tribological behavior of the Ti implants, which could in turn result in expanding the biological application of Cp-Ti.

Comparation of non-proportional hardening behavior and microscopic mechanism for CP-Ti under strain-controlled and stress-controlled multiaxial low cycle fatigue

Proportional and non-proportional multiaxial low cycle fatigue tests were performed on commercial pure titanium (CP-Ti), employing both strain-controlled and stress-controlled modes. CP-Ti exhibits a four-stage characteristic under higher applied strain amplitude. For other cases and under stress-controlled mode, the initial hardening dissipated, giving way to a typical three-stage cyclic softening characteristics. Two failure modes, fatigue failure and ratcheting failure, occur depending on the applied stress amplitude. CP-Ti exhibits obvious asymmetric strain response under symmetric stress-controlled mode depending on the loading level. CP-Ti demonstrates non-proportional hardening under both strain-controlled mode and stress-controlled mode with different microscopic mechanisms. The additional hardening due to non-proportional loading results in an increase in the axial response stress with increasing multiaxial strain ratio. Interactions between dislocations with different slip systems hinder the development of stable dislocation structures, leading to pronounced non-proportional hardening of CP-Ti under strain-controlled mode. As for stress-controlled mode, the significant growth of twin content improves the grain boundary strength, leading to the non-proportional hardening of CP-Ti.

Effect of ultrasonic assisted-ECAP processing on the microstructure, mechanical properties, and fluoride-induced corrosion performance of pure titanium

The influence of the ultrasonic assisted equal channel angular pressing (UA-ECAP) process on the microstructural characteristics, mechanical properties, and fluoride-induced corrosion behavior of grade 2 commercially pure titanium (CP-Ti) is investigated. The UA-ECAP process, particularly in the first pass, induces the formation of twins and slip bands. Continued slip band activity leads to non-equilibrium structures and ultrafine grains in subsequent passes. Mechanical properties analyses show hardness progression from 147 HV (annealed state) to 233 HV (3-pass UA-ECAPed) and yield strength increase from 465 MPa to 765 MPa with elongation reduction from 24.6 % to 16.6 %. Fluoride-induced corrosion of various samples in 1 wt% HF solution is investigated through electrochemical and immersion tests. After 28 days of immersion, the 3-pass UA-ECAPed sample exhibits a corrosion rate around half that of the annealed one and lower than other UA-ECAPed samples. Microscopic observations of corroded samples reveal the 3-pass UA-ECAPed sample's film is denser and more uniform, as compared with the other samples. Glow discharge optical emission spectroscopy (GDOES) confirms the corrosion films on all samples consist of an outer region rich in oxygen/fluorine and an inner region rich in oxygen; however, the film exists on the 3-pass UA-ECAPed sample exhibits over twice thicker than other samples and with higher contribution of oxygen in it as well. A proposed physical model is provided to explain the 3-pass ECAP sample's enhanced corrosion resistance.

Damage evolution and ductile fracture of commercially-pure titanium sheets subjected to simple tension and cyclic bending under tension

This paper describes a study into the evolution of damage in commercial-purity titanium (CP–Ti) sheets subjected to cyclic bending under tension (CBT) and uniaxial tension (simple tension, ST). Sections were taken from sheets that were strained to various levels under both methods and were imaged using X-ray computed tomography (XCT) to reveal insights into the size, density, and distribution of microvoids in the sheets. Digital image correlation (DIC) was also used to observe the surface strain of CBT and ST sheets during testing. These results showed that elongation to failure (ETF) for CBT deformation is about 2.5× higher than for ST, local longitudinal strains in the bulk of the CBT sample are around 1.3× higher than the peak strain in the ST necked region, and 1.7× higher in the localized region of CBT failure. It was found that the volume-density of voids in both sheets followed a similar exponential increase with strain, reaching nearly 45× higher in the CBT than the ST sheets before the onset of failure, mainly due to the higher strain levels achieved. A higher volume density of voids developed in the center of sheets at high levels of strain, for both processes, with the density in the sheet center becoming approximately double that found near the edges. Scanning electron microscopy (SEM) was used to examine the fracture surface of CBT and ST sheets after failure. The observations are presented and discussed highlighting the CBT process as effective to delay ductile fracture of the CP-Ti sheets.

A Push-out Bond Strength Study and Interface Analysis of New Porous Titanium Dental Post Luted with Resin Cement

This study aimed to compare the push-out bond strength (PBS) between a new porous titanium post (PTP) and other marketed dental posts cemented with two types of dual-cure resin cement. A total of 96 extracted single-rooted human teeth were recruited. Four types of dental posts (n = 24 each), namely: stainless steel post (SSP), commercially-pure titanium post (CTP), fibre glass post (FGP), and PTP were cemented with two types of resin cements (RelyX U200 and ParaCore) and then sectioned at coronal and middle root levels. The specimens were subjected to a PBS test at a crosshead speed of 0.5 mm/min. The interface analysis was performed using a stereomicroscope and scanning electron microscope. A p-value < 0.05 was considered significant for all statistical tests. PBS recordings showed that the highest PBS mean value in RelyX group was 2.68±1.10 MPa for PTP. The differences in PBS between PTP and SSP and FGP were not significant (p = 0.098 and p = 0.075, respectively). The null hypothesis for RelyX group at both coronal and middle sections of the root was retained (p > 0.05). No failure at the post-cement interface was found in the PTP group, which was founder superior over the other posts (no gap for this interface was observed). The PTP showed similar bonding strength and adhesion to the other tested posts when using RelyX U200 cement. The PTP can be considered a new alternative option for the dental post system.

Artificial neural network enhanced plasticity modeling and ductile fracture characterization of grade-1 commercial pure titanium

This study primarily aims to develop a robust modeling approach to capture the complex material behavior of CP-Ti, appeared by high anisotropy, differential hardening due to anisotropy evolution, and flow behavior sensitive to strain rate and temperature, using artificial neural networks (ANNs). Plasticity is characterized by uniaxial tension and in-plane biaxial tension tests at temperatures of 0 °C and 20 °C with strain rates of 0.001 /s and 0.01 /s, and the results are used to calibrate the non-quadratic anisotropic Yld2000–3d yield function with respect to the plastic work. In order to predict the intricate plastic deformation with the temperature and strain rate effects, two distinct ANN models are developed; one to capture the strain hardening behavior and the other to predict the anisotropic parameters in the chosen yield function. The developed ANN models predict an unseen dataset well, which is intermediate testing conditions at a temperature of 10 °C and strain rate of 0.005 /s. The ANN models, being computationally stable and adhering to conventional constitutive equations, are implemented into a user material subroutine for the ductile fracture characterization of CP-Ti sheet using the hybrid experimental-numerical analysis. The favorable agreement between experimental data and numerical predictions, particularly using the ANN models with evolving anisotropic material parameters for the Yld2000–3d yield function, underscores the significance of the differential hardening effect on the ductile fracture behavior and highlights the capabilities of ANN models to capture the complex plastic behavior of CP-Ti. The key parameters including stress triaxiality, Lode angle parameter, and equivalent plastic strain at the fracture location are extracted from the simulations, enabling the calibration of ductile fracture models, namely Johnson-Cook, Hosford-Coulomb, and Lou-2014, and construction of fracture envelopes.

An Experimental Study on the Frictional Behavior of Ultrathin Metal Sheets at Elevated Temperatures.

Hot forming is an effective approach for improving the formability of ultrathin metal sheets, such as those made of stainless steel and pure titanium. However, the increased friction coefficient between the tool and the high-temperature metal sheet negatively affects material flow during hot forming, potentially resulting in severe local thinning or even cracking. This study explores the frictional behavior of 0.1 mm thick ferritic stainless steel (FSS) and commercially pure titanium (CP-Ti) sheets at elevated temperatures. A friction testing apparatus was developed to measure the friction coefficients of these metal sheets from room temperature (25 °C) up to 600 °C. The friction coefficient of the FSS sheet increased monotonically with temperature, whereas that of the CP-Ti sheet first increased and then decreased. Post-friction testing microscopic examination demonstrated that built-up edges formed on the surfaces of the friction blocks when rubbed against the stainless steel, contributing to the higher friction coefficients. This study provides a foundation for understanding frictional behavior during the hot forming of ultrathin metal sheets.

Characterization of Electrochemical and Biocompatibility of Zinc Oxide Coating Electrodeposited on Commercial Pure Titanium Alloy

This study examines how the duration of electrodeposition affects the morphology and electrochemical characteristics of zinc oxide coatings applied to a pure titanium substrate. The morphology of the coating and the phases present within it are analyzed using a scanning electron microscope and the X‐ray diffraction technique. The coating's resistance to corrosion in a phosphate‐buffered saline solution is evaluated using two electrochemical methods: impedance spectroscopy and potentiodynamic polarization tests. The surface roughness of the coated samples is assessed using interferometry. The results demonstrate that an increase in electrodeposition time, ranging from 150 to 1200 s, leads to an enhanced texture intensity in the (0002) and (010) planes of the ZnO coating. Furthermore, the thickness of the ZnO crystals and surface roughness increases by factors of 3.25 and 2.79, respectively, as the deposition time is extended. This extended duration results in the formation of larger needle‐shaped and flower‐like ZnO crystals, leading to a significantly nonuniform structure. Correspondingly, the corrosion rate also increases as the electrodeposition time is extended from 150 to 1200 s, rising from 0.001951 to 9.117 μm year−1. The lowest corrosion rate (1.654 μm year−1) is achieved in coatings deposited for 300 s using a potential of 3 V.

Improving the uniform elongation of ultrafine-grained pure titanium through judicious allocation of work hardening

Improving uniform elongation in metals typically involves enhancing the work hardening rate, as elevated work hardening can delay necking and fracture. However, our investigation into commercial pure titanium reveals a counterintuitive relationship between these properties. We find that high uniform elongation correlates with low work hardening capability, while a high work hardening rate results in reduced ductility. Two types of ultrafine-grained pure titanium, prepared by rotary swaging, subsequent rolling, and annealing, exhibit different mechanical properties. Microstructural and deformation mechanism analyses reveal that the difference arise from variations in texture. Specifically, extensive activation of <c+a> dislocations in the former sample leads to premature, intense work hardening that is quickly exhausted, while the latter sample shows a steady, uniform work hardening progression that delays necking. Our findings challenge the conventional understanding that high work hardening rates ensure high uniform elongation. Instead, we propose that optimizing ductility requires a strategic allocation of work hardening throughout the tensile deformation to delay necking. This study reveals the intrinsic relationship between work hardening and ductility, offering new strategies for designing stronger and tougher materials.