Biaxial Flexural Strength Research Articles

Effect of femtosecond laser induced surface patterns on the flexural strength of monolithic zirconia.

To investigate how patterns generated by femtosecond (fs) laser and femtosecond laser power affect the surface roughness (Ra) and biaxial flexural strength (BFS) of monolithic zirconia. Eighty disk-shaped zirconia specimens were divided into eight subgroups (n = 10): Control (C), airborne-particle abrasion (APA), 400 mW fs laser (spiral [SP(400)], square [SQ(400)], circular [CI(400)]), and 700 mW fs laser ([SP(700)], [SQ(700)], [CI(700)]). Ra values were calculated by using a surface profilometer. One additional specimen per group was analyzed with scanning electron microscopy and x-ray diffractometry. BFS values were obtained by using the piston-on-3-ball test. One-way ANOVA and either Tukey's HSD (BFS) or Tamhane's T2 (Ra) tests were used to evaluate data (α = 0.05). Regardless of the pattern and power, fs laser groups had higher Ra than C and APA, while SP groups had lower Ra than CI and SQ groups (p ≤ 0.004). For each pattern, Ra increased with higher laser power (p < 0.001), while the laser power did not affect the BFS (p ≥ 0.793). CI and SQ groups had lower BFS than the other groups (p ≤ 0.040), whereas SP groups had similar BFS to C and APA (p ≥ 0.430). Fs laser microstructuring with spiral surface pattern increased the Ra without jeopardizing the BFS of zirconia. Thus, this treatment might be an option to roughen tested zirconia.

The effect of speed sintering and hydrothermal aging on the biaxial flexural strength and microstructure of recent cubic zirconia material

The effect of speed sintering and hydrothermal aging on the biaxial flexural strength and microstructure of recent cubic zirconia material

Nanomechanical properties of ceramic materials from the SiO2–Al2O3-(Na2O)–K2O–MgO system with an addition of SrO

The ceramic materials studied in this paper consist of finely dispersed crystalline phases embedded in a glassy matrix, which is similar to glass-ceramic materials, porcelain, and VC products. The strength depends then not only on the properties of the individual crystalline phases but also on their interactions and the matrix. Differences in mechanical properties for materials with similar chemical compositions are most likely related to diverging microstructures. Crystal orientation, grain-size distribution and shape, the ratio of the glass matrix to the crystalline phase, and homogeneity control the flexural strength of glass-ceramic materials. The subject of the study is whiteware ceramic materials from the SiO2–Al2O3–Na2O–K2O–MgO–SrO system, fired similarly to the regime used for VC products. The effect of the type of alkali oxide and the share of SrO were tested. This paper presents the results of hot-stage microscopy, X-ray diffraction (XRD), scanning electron microscopy with a micro-analyzer (SEM-EDS) and biaxial flexural strength measurements. Additionally, nanoindentation technique was used to access local mechanical properties.

Cyclic fatigue behavior of Y‐TZP nanostructures with non‐homogeneous yttria distribution

AbstractNanostructured Y‐TZP samples with Non‐Homogeneous Yttria Distribution (NNHYD) were prepared by mixing co‐precipitated 3Y‐TZP powder (Tosoh TZ‐3Y) with yttria‐free monoclinic powder (Tosoh TZ‐0), yielding an overall yttria content of 2 mol%. The cyclic fatigue behavior of NNHYD was evaluated by Step‐Stress Accelerated Life Testing (SSALT) and mechanical cycling in a biaxial flexural strength test (BFST) setup and compared to Conventional Submicrometric 3Y‐TZP (CS). Physical, structural, microstructural, and mechanical characterizations of all groups were also evaluated and compared before and after artificial aging in autoclave. NNHYD presented a higher capacity for damage accumulation and maintenance of phase transformation potential than CS, associated with elevated resistance to the propagation of Low‐Temperature Degradation (LTD). A nanostructured 3Y‐TZP surface layer introduced in NNHYD by dip coating (DC‐NNHYD) improved resistance to LTD at the cost of reduced reliability under cyclic fatigue by increasing the stability of the tetragonal phase. This surface alteration highlights the impact of surface properties on mechanical performance. The results of this study present practical possibilities to help achieve the ideal balance between strength, toughness, and LTD resistance to improve the lifetime of zirconia‐based biomaterials.

Impact of the sintering parameters on the grain size, crystal phases, translucency, biaxial flexural strength, and fracture load of zirconia materials

ObjectivesTo investigate the influence of the zirconia and sintering parameters on the optical and mechanical properties. MethodsThree zirconia materials (3/4Y-TZP, 4Y-TZP, 3Y-TZP) were high-speed (HSS), speed (SS) or conventionally (CS) sintered. Disc-shaped specimens nested in 4 vertical layers of the blank were examined for grain size (GS), crystal phases (c/t’/t/m-phase), translucency (T), and biaxial flexural strength. Fracture load (FL) of three-unit fixed dental prostheses was determined initially and after thermomechanical aging. Fracture types were classified, and data statistically analyzed. Results4Y-TZP showed a higher amount of c + t’-phase and lower amount of t-phase, and higher optical and lower mechanical properties than 3Y-TZP. In all materials, T declined from Layer 1 to 4. 3/4Y-TZP showed the highest FL, followed by 3Y-TZP, while 4Y-TZP showed the lowest. In 4Y-TZP, the sintering parameters exercised a direct impact on GS and T, while mechanical properties were largely unaffected. The sintering parameters showed a varying influence on 3Y-TZP. Thermomechanical aging resulted in comparable or higher FL. Conclusion3/4Y-TZP presenting the highest FL underscores the principle of using strength-gradient multi-layer blanks to profit from high optical properties in the incisal area, while ensuring high mechanical properties in the lower areas subject to tensile forces. With all groups exceeding maximum bite forces, the examined three-unit FDPs showed promising long-term mechanical properties.

Flexural Strength of Different Monolithic Computer-Assisted Design and Computer-Assisted Manufacturing Ceramic Materials Upon Accelerated Aging.

The durability of ceramic is crucial, which is probably influenced by aging. This study evaluated the effect of aging on flexural strength of different ceramics. One-hundred twenty ceramic discs (Ø 12 mm, 1.5 mm thickness) were prepared from zirconia-reinforced lithium silicate (ZLS, C), lithium disilicate (LS2, E), precolored yttria-stabilized tetragonal zirconia polycrystalline (Y-TZP, Ip), and customized color Y-TZP (Ic). Samples were randomly divided into two groups for accelerated aging (A) between 5 and 55°C water baths, 30-second immersing time each, for 10,000 cycles, and nonaged group (N), serving as control. Biaxial flexural strength (σ) was evaluated utilizing the piston-on-three-balls at 0.5 mm/min speed. Analysis of variance and Tukey comparisons were determined for significant differences (α = 0.05). Weibull analysis was applied for survival probability, Weibull modulus (m), and characteristic strength (σo). Microstructures were evaluated with scanning electron microscopy and X-ray diffraction (XRD). The highest σ and σo were seen for IcN, followed by IcA, IpN, IpA, EN, CA, CN, and EA, respectively. CN showed the highest m, while EA showed the lowest m. Significant differences of σ for each ceramic were indicated (p < 0.05). Aging caused a significant difference in σ (p < 0.05). XRD showed t→m phase transformation of Ip and Ic after aging. Aging affected strength of ceramics. Comparable strength between LS2 and ZLS was evidenced, but both were less strength than Y-TZP either aging or non-aging. Comparable strength between precolored Y-TZP and customized color Y-TZP was indicated. Better resisting aging deterioration of Y-TZP than LS2 and ZLS is suggested for fabrication restorative reconstruction.

Mechanical Properties of High- and Low-Fusing Zirconia Veneering Ceramics Fired on Different Trays and Substrates.

This study aimed to evaluate the effect of ceramic type, firing tray, and firing substrate on the density, shrinkage, biaxial flexural strength, Martens' hardness, and elastic indentation modulus of zirconia veneering ceramics. Disk-shaped specimens were fabricated from a high-fusing (HFZ) and a low-fusing (STR) zirconia veneering ceramic. These specimens were then divided into 10 groups according to firing trays (round, small honeycomb-shaped, cordierite [RSC]; round, large honeycomb-shaped, aluminum oxide [RLA]; rectangular, plane, silicon nitride [RCPS]; round, plane, silicon nitride [RPS]; and rectangular, plane, calcium silicate [RCPC]) and firing substrates (firing cotton and platinum foil) used (n = 12). The density, shrinkage, biaxial flexural strength, Martens' hardness, and indentation modulus were measured, and analyzed with generalized linear model analysis (α = 0.05). The interaction between the ceramic type and firing substrate affected density (p < 0.001), and the other outcomes were affected by the interaction among all main factors (p ≤ 0.045). Higher density was observed with HFZ or platinum foil (p ≤ 0.007). RSC and RLA led to a higher density than RCPS within HFZ and led to the lowest density within STR (p ≤ 0.046). STR had a higher shrinkage (p < 0.001). RSC mostly led to a lower shrinkage of HFZ (p ≤ 0.045). The effect of ceramic type and firing substrates on the biaxial flexural strength, Martens' hardness, and indentation modulus was minimal while there was no clear trend on the effect of firing tray on these properties. Ceramic type, firing tray, and firing substrate affected the mechanical properties of the tested zirconia veneering ceramics. Firing the tested zirconia veneering ceramics over a round and small honeycomb-shaped cordierite firing tray with firing cotton mostly led to improved mechanical properties.

Bovine hydroxyapatite/3Y-TZP bioceramic: Aligning 3Y-TZP content with sintering parameters

This study aimed to produces and characterize bovine hydroxyapatite (HA) bioceramic with 3Y-TZP addition and analyze different sintering curves. HA was extracted from bovine bones and nanoparticulated. HA discs (0, 1, 5 and 10 wt% 3Y-TZP) were subjected to uniaxial and isostatic pressing. Dilatometry analysis was performed and the groups were sintered using 3 different firing curves (conventional, 1300 °C; 2-step, 1292 °C; 2-step, 1420 °C). The samples were analyzed by X-ray diffraction (XRD), biaxial flexural strength (BFS), Vickers microhardness (VH) and Field emission scanning electron microscopy (FE-SEM). The dilatometry results signaled the need for sintering optimization in groups added with 3Y-TZP. XRD demonstrated the characteristic crystallographic peaks of HA in the pure groups and with 1% 3Y-TZP, and decomposition of HA into β-TCP and formation of calcium zirconate in the groups with 5 and 10% 3Y-TZP. Considering each composition, the groups of pure HA (131.3 ± 13.5 MPa; 401 ± 12.7 GPa) sintered by the conventional curve and HA+1%3Y-TZP (145 ± 8.6 MPa; 507 ± 47.9 GPa), HA+5%3Y-TZP (68.1 ± 14.2 MPa; 183 ± 9.8 GPa) and HA+10%3Y-TZP (55.6 ± 5.1 MPa; 96.1 ± 7.64 GPa) sintered by the 2-step curve at 1420 °C, combined the best BFS and VH results. The addition of 1 wt% 3Y-TZP and optimization in the sintering process improved the mechanical and microstructural properties of HA bioceramics and maintenance of its crystalline characteristics. Refinement in material processing is necessary for the future use of this bioceramic in dentistry.

Dielectric probing of low-temperature degradation resistance of commercial zirconia bio-ceramics

ObjectivesTo investigate the effect of the stability of oxygen vacancies on the low-temperature degradation (LTD) resistance of two kinds of commercial zirconia-based materials (3Y-TZP ceramics and Ce-TZP/Al2O3 composites) via the dielectric probing methods. MethodsThe commercial 3Y-TZP ceramics and Ce-TZP/Al2O3 composites were prepared via conventional solid-state methods. Density, phase content, microstructure, strain, and biaxial flexural strength (BFS) of two materials were investigated using Archimedes method, XRD, SEM, strain-electric field (S-E) loops and ball-on-ring methods, respectively. The concentration of oxygen vacancies before and after LTD of two materials were evaluated using dielectric probing and XPS methods. ResultsThe XRD analysis revealed that compared to the 3Y-TZP ceramics, the Ce-TZP/Al2O3 composites showed better LTD resistance, without clear LTD. The greater LTD resistance for Ce-TZP/Al2O3 composites was associated with their stability of oxygen vacancies, by higher activation energy based on the dielectric measurements and XPS results. For the 3Y-TZP ceramics that underwent the tetragonal to the monoclinic phase transition during the LTD treatment, the concentration of their oxygen vacancies decreased after LTD. In addition, the Ce-TZP/Al2O3 composites exhibited higher flexural strength and potential fracture toughness based on the BFS testing and strain vs electric field measurement results, indicating a great potential for use in fixed restorative dental applications. SignificanceThis work suggested the stability of oxygen vacancies played a key role in the resistance to LTD. Optimizing the stability of the oxygen vacancies is key to the development of more reliable zirconia- based dental biomaterials with greater resistance to LTD.

Biaxial flexural strength of hydrothermally aged resin-based materials

PurposeThe strength of temporary restorations plays a vital role in full-mouth reconstruction, and it can be impacted by the aging process. The aim of this in vitro study was to evaluate the biaxial flexural strength and fractographic features of different resin-based materials submitted to thermal aging. Material and methodsOne hundred and ninety-two resin disc-shaped specimens (6.5 mm in diameter and 0.5 mm in thickness) were fabricated and divided into six experimental groups according to the resin-based materials (Filtek Bulk-Fill flowable resin; J-Temp temporary resin; and Fuji Lining glass ionomer cement) and aging process (before and after thermal cycling). Biaxial flexural strength test was performed using a universal testing machine at a crosshead speed of 0.5 mm/min before and after thermal cycling (5 °C and 55 °C, 5760 cycles, 30 s). The mechanical properties were assessed using Weibull parameters (characteristic strength and Weibull modulus) (n = 30). Fractured specimens were examined under a polarized light stereomicroscope to identify crack origin and propagation direction. The surface microstructure of the resin-based materials was assessed by scanning electron microscopy (n = 2). The Weibull modulus (m), characteristic strength, and reliability properties were calculated, and a contour plot was used to detect differences among groups (95% confidence interval). ResultsThe Weibull modulus (m), characteristic strength, and reliability of the resin-based compounds were influenced by material type and thermal aging (p < 0.05). Weibull modulus (m) revealed no differences when comparing the materials and aging process (p > 0.05), except for the preceding aging period where Filtek Bulk-Fill exhibited higher values compared to J-Temp (p < 0.05). Filtek Bulk-Fill demonstrated superior characteristic strength and reliability compared to J-Temp and Fuji Lining before and after thermal cycling (p < 0.05). Fractography of the resin-based materials showed fractures originating from surface defects exposed to tensile side and their propagation toward the compressive side. Generally, no differences in surface microstructure were observed on micrographs before and after thermal aging for Filtek Bulk-Fill and Fuji Lining. However, the aging process developed flaws in J-Temp. ConclusionResin-based material composition resulted in different flexural strength performance, impacting the Weibull modulus (m), characteristic strength, and reliability of the resin-based restorations.

Effect of curing mode of resin composite cements on water sorption, color stability, and biaxial flexural strength

ObjectivesTo determine whether water sorption and solubility of a recently introduced self-adhesive cement is comparable to two clinically tested resin composite cements after thermal aging, and if this is affected by the curing mode. Whether water sorption is correlated with color difference and biaxial flexural strength was also investigated. MethodsWater sorption and solubility of three resin composite cements {RelyX Universal (RUV), (Panavia V5 (PV5), Panavia SA plus (PSA)} were measured after thermal aging. Disk-shaped specimens were either light-cured or autopolymerized (n = 15 per group). Color difference ΔE00 and biaxial flexural strength were also obtained. ResultsSorption was highest for RUV (auto: 54.9 ± 9.0 µg/mm3, light: 49.7 ± 4.9 µg/mm3), followed by PSA (auto: 37.7 ± 1.4 µg/mm3, light: 34.5 ± 1.1 µg/mm3) and PV5 (auto: 21.7 ± 0.7 µg/mm3, light: 22.1 ± 0.4 µg/mm3). Light-curing reduced solubility values, particularly for RUV (from 60.7 ± 20.8 µg/mm3 to 6.4 ± 0.8 µg/mm3). Color differences of ΔE00 > 1.8 (considered clinically not acceptable) were noted after aging for RUV and PSA. Sorption and ΔE00 values after aging were correlated linearly (R2 = 0.970). Biaxial flexural strength values were highest for PV5 (light: 153.4 ± 15.9 MPa; auto: 133.2 ± 18.0 MPa) and lowest for RUV (light: 99.3 ± 12.8 MPa; auto: 35.1 ± 8.3 MPa). SignificanceLight-curing has beneficial effects on sorption, color stability, and biaxial flexural strength of resin composite cements. Cements containing 2-hydroxymethacrylate such as RUV and PSA are more prone to water sorption and color changes.

Denture base materials: An in vitro evaluation of the mechanical and color properties

ObjectivesThis study aimed to compare the physical and mechanical properties of four denture base materials: Polyan IC (PA), milled polymethylmethacrylate (PMMA), three-dimensional (3D)-printed resin (3DP), and SR Ivocap (SR). MethodsNinety-six samples were prepared and divided into four groups as follows. Group A consisted of 3DP (Asiga DentaBASE, Asiga) fabricated using a manufacturer-recommended 3D printer (Asiga Pro 4k, Asiga). Group B comprised milled PMMA (MP) (Ivotion Base, Ivoclar Vivadent). Group C included PA (BredentSenden), meanwhile, group D involved SR (Ivoclar VivadentSchaan). Cuboid samples (65 mm x 10 mm x 2.5 mm) were used for biaxial flexure strength testing in a universal testing machine (UTM). Cylindrical samples of 20 mm x 40 mm were used for compressive strength testing in a UTM. Additionally, cuboid samples (65 mm x 10 mm x 2.5 mm) were used for Vickers surface hardness testing in a microhardness tester. disk samples (10 mm x 2.5 mm) were employed for color stability testing both in a coffee solution and Coca-Cola, using a digital spectrophotometer. Statistical analyses were performed using one-way analysis of variance and Tukey's post hoc analysis (α=0.05). ResultsMP demonstrated superior compressive strength (p = 0.002) and color stability compared to that exhibited by 3DP (p < 0.001) while displaying similar flexure strength (p = 0.336) and hardness (p = 0.708). MP and PA displayed similar compressive strength (p = 0.081), flexure strength (p = 0.159), and color stability in coke (p = 0.071). However, MP had reduced hardness (p < 0.001) and color stability in coffee (p < 0.001). Moreover, MP demonstrated a higher compressive strength (p < 0.001) than that displayed by SR. However, the flexure strength, hardness, and color stability were similar (p > 0.05). Furthermore, 3DP exhibited comparable compressive strength (p = 0.334) to that of PA but demonstrated significantly lower flexure strength (p = 0.005), hardness (p < 0.001), and color stability (p < 0.001) compared to PA. In comparison to SR, PA had a higher compressive strength (p < 0.001), hardness (p = 0.001), and color stability in coffee (p < 0.001), although they demonstrated similar (p > 0.05) flexure strength and color stability in coke. ConclusionsThe MP and PA demonstrated superior compressive strength than that exhibited by the other materials tested. The tested materials had similar flexure strengths, except for PA which demonstrated superiority over the 3DP. Among all tested materials, PA exhibited the highest hardness, while the 3DP was the least color-stable. Clinical SignificanceConsidering the mechanical properties and color stability, Polyan and milled polymethylmethacrylate are preferred for complete denture fabrication. However, the limited repairability and complex handling of Polyan should be considered.

Development of ZTA (80% Al2O3/20% ZrO2) pre-sintered blocks for milling in CAD/CAM systems

The present work aims to develop a production method of pre-sintered zirconia-toughened-alumina (ZTA) composite blocks for machining in a computer-aided design and computer-aided manufacturing (CAD-CAM) system. The ZTA composite comprised of 80% Al2O3 and 20% ZrO2 was synthesized, uniaxially and isostatically pressed to generate machinable CAD-CAM blocks. Fourteen green-body blocks were prepared and pre-sintered at 1000 °C. After cooling and holder gluing, a stereolithography (STL) file was designed and uploaded to manufacture disk-shaped specimens projected to comply with ISO 6872:2015. Seventy specimens were produced through machining of the blocks, samples were sintered at 1600 °C and two-sided polished. Half of the samples were subjected to accelerated autoclave hydrothermal aging (20h at 134 °C and 2.2 bar). Immediate and aged samples were characterized by scanning electron microscopy (SEM) and X-ray diffraction (XRD). Optical and mechanical properties were assessed by reflectance tests and by biaxial flexural strength test, Vickers indentation and fracture toughness, respectively. Samples produced by machining presented high density and smooth surfaces at SEM evaluation with few microstructural defects. XRD evaluation depicted characteristic peaks of alpha alumina and tetragonal zirconia and autoclave aging had no effect on the crystalline spectra of the composite. Optical and mechanical evaluations demonstrated a high masking ability for the composite and a characteristic strength of 464 MPa and Weibull modulus of 17, with no significant alterations after aging. The milled composite exhibited a hardness of 17.61 GPa and fracture toughness of 5.63 MPa m1/2, which remained unaltered after aging. The synthesis of ZTA blocks for CAD-CAM was successful and allowed for the milling of disk-shaped specimens using the grinding method of the CAD-CAM system. ZTA composite properties were unaffected by hydrothermal autoclave aging and present a promising alternative for the manufacture of infrastructures of fixed dental prostheses.

Color- and strength-graded zirconia: Strength, light transmission, and composition

Statement of problemNatural teeth are graded in terms of translucency and strength. Graded zirconia materials are now available with a higher yttria content on the top or in the enamel zone to increase surface translucency and a lower yttria content on the bottom or in the dentin zone to increase strength. Such materials could provide multiple advantages over uniform materials and reduce the need for porcelain veneering in anterior artificial crowns; however, studies on the properties of these materials are lacking. PurposeThe purpose of this in vitro study was to measure and compare the biaxial flexural strength, percentage light transmission, elemental content, and phase content of zones within and among color graded zirconia blocks and color- and strength-graded zirconia blocks. Material and methodsDisks of a color graded material (Katana STML) and a strength- and color-graded material (IPS e.max ZirCAD Prime) were fabricated (Zircom Furnace). Biaxial flexural strength was measured using a piston-on-3-ball test in a universal testing machine (n=10). Absolute light transmission was measured with a spectrophotometer. Elemental compositions were quantified for 3 zones in each of the 2 zirconia materials using X-ray fluorescence analysis. Zirconia phase fractions were quantified for 3 zones using X-ray diffraction analysis (XRD). Where appropriate, 2-way ANOVA, 1-way ANOVA, and Tukey multiple pairwise comparison testing were used to determine which of the 6 zones differed from one another (α=.05). ResultsThe color-graded zirconia exhibited gradients in light transmission and differences in phase content in the 3 zones measured. The color- and strength-graded zirconia exhibited gradients in light transmission, biaxial flexural strength, elemental composition, and phase content in the 3 zones measured. The bottom, dentin, or intaglio layer of a strength graded zirconia material was substantially stronger than all other zones of either material (P<.05). The top, enamel, zones of both materials possessed high light transmissibility (P<.05). The 2 materials differed with respect to biaxial strength (P<.001), light transmission (P<.02), elemental composition, and phase composition overall, as well as in most zone-by zone comparisons (P<.05). The performance and composition of the color graded material was consistent with it being a 5Y material throughout. The performance and composition of the color and strength graded material was consistent with it having a 3Y bottom zone and a 5Y top zone. ConclusionsA strength-graded and color-graded zirconia material offers potential advantages in both strength and translucency.

Influence Of Low-Temperature Degradation On Phase Transformation And Biaxial Flexural Strength On Different High-Translucent 4Y-PSZ, 5Y-PSZ, 6Y-PSZ Monolithic Zirconia

Objective: This study aimed to investigate the effect of low-temperature degradation (LTD) in phase transformation and biaxial flexural strength of high-translucent yttria partially stabilized zirconia (Y-PSZ) and yttria tetragonal zirconia polycrystalline (3-YTZP).&#x0D; Methods: A total of 120 new high-translucent 3-YTZP (NMS) and Y – PSZ (KST, KUT, NQ3MS) zirconia disc specimens were manufactured according to ISO 6872 for biaxial flexural strength (14 mm., 1.2 ± 0.02 mm). The specimens from each type of material were divided into 3 subgroups (n:30) according to the LTD in an autoclave at 134 C0 at 2 bar (n:10) (at 5, 20 hour (h)). Specimens without LTD served as the control. Data of the monoclinic phase changes (Xm) and flexural strength were analyzed using two-way ANOVA followed by post hoc MannWhitney U test. Weibull statistics were used to analyze strength reliability.&#x0D; Results: LTD increased the monoclinic content significantly for NMS and slightly for the KST group. A monoclinic phase was not detected for KUT and NQ3MS groups. The biaxial flexural strength of the NMS group was affected significantly and decreased with an increase in the 20 h aging. For flexural strength values, there was no significant difference in aging times for each of the KST, KUT, and NQ3MS groups. Weibull analysis showed the highest characteristic strength for NMS (1412.9), KST (750.1), NQ3MS(790.5) and KUT (615.2) groups. The Weibull modulus (m) increased in the NMS, KUT, and NQ3MS groups compared with the control group and decreased in the KST group.&#x0D; Conclusion: LTD caused a significant decrease in the biaxial flexural strength results of the NMS group but did not significantly affect the KST, KUT, and NQ3MS groups’ values.

Topographical and crystalline change on surface by sandblasting improve flexural and shear bond strength of niobia-modified yttria-stabilized tetragonal zirconia polycrystal.

This study aimed to investigate the effects of sandblasting on the physical properties and bond strength of two types of translucent zirconia: niobium-oxide-containing yttria-stabilized tetragonal zirconia polycrystals ((Y, Nb)-TZP) and 5 mol% yttria-partially stabilized zirconia (5Y-PSZ). Fully sintered disc specimens were either sandblasted with 125 µm alumina particles or left as-sintered. Surface roughness, crystal phase compositions, and surface morphology were explored. Biaxial flexural strength (n=10) and shear bond strength (SBS) (n=12) were evaluated, including thermocycling conditions. Results indicated a decrease in flexural strength of 5Y-PSZ from 601 to 303 MPa upon sandblasting, while (Y, Nb)-TZP improved from 458 to 544 MPa. Both materials significantly increased SBS after sandblasting (p<0.001). After thermocycling, (Y, Nb)-TZP maintained superior SBS (14.3 MPa) compared to 5Y-PSZ (11.3 MPa) (p<0.001). The study concludes that (Y, Nb)-TZP is preferable for sandblasting applications, particularly for achieving durable bonding without compromising flexural strength.

Fracture strength of porcelain veneer on surface-treated zirconia.

In this study, we investigated the effects of surface treatment on the fracture strength of porcelain-veneered zirconia. Highly translucent 4 mol% yttria-stabilized zirconia disks (KATANA HT, Kuraray Noritake Dental) were divided into three surface-treatment groups: 1)as-sintered, 2) alumina sandblasted, and 3) ground. Crystallographic and surface-roughness analyses were conducted for each group. Veneering ceramics (Cerabien ZR, Kuraray Noritake Dental) were applied to the zirconia surfaces. The fracture strengths of the porcelain-veneered zirconia disks were measured using biaxial flexural-strength tests. Crystallographic analysis revealed that grinding and sandblasting increased the fractions of the monoclinic and rhombohedral zirconia phases. The ground specimens had a higher surface roughness than the sandblasted specimens. Weibull analysis showed no significant differences in biaxial flexural strength among the three groups. The results suggest that these surface treatments do not affect the fracture strength of porcelain-veneered zirconia.

Effects of multiple firings on the translucency, crystalline phase, and mechanical strength of highly translucent zirconia.

This study aimed to clarify the effects of multiple firings on the translucency, crystal structure, and mechanical strength of highly translucent zirconia. Four types of highly translucent zirconia (LAVA Esthetic, LAVA Plus, KATANA Zirconia STML, and KATANA Zirconia HTML) were fired three times at three different temperatures, and the translucency, crystal structure, and flexural strength were evaluated before and after firing. The translucency was statistically compared using repeated-measures analysis of variance; the zirconia phase composition was assessed using X-ray diffraction followed by Rietveld analysis; and the biaxial flexural strength was assessed using Weibull analysis. The translucency of LAVA Esthetic and KATANA Zirconia HTML decreased significantly after firing, and the crystal composition of LAVA Plus and KATANA Zirconia HTML changed after multiple firings, whereas multiple firings did not affect the biaxial flexural strength of any samples. Thus, multiple firings may affect the optical properties of highly translucent zirconia.

Effect of thermocycling on the mechanical properties of permanent composite-based CAD-CAM restorative materials produced by additive and subtractive manufacturing techniques

BackgroundThe aim of the study was to determine and compare the biaxial flexural strength (BFS) and Vickers hardness (VHN) of additive and subtractive manufactured permanent composite-based restorative materials, before and after thermal aging.MethodsA total of 200 specimens were prepared; 100 disc-shaped specimens (diameter 13 × 1.2 mm) for the BFS test and 100 square specimens (14 × 14 × 2 mm) for the VHN test. The specimens were made from various materials: two subtractive composite-based blocks (Cerasmart 270 [CS], Vita Enamic [VE]), two additive composite-based resins used for two different vat polymerization methods (digital light processing [DLP]; Saremco Print Crowntec [SC] and stereolithography [SLA]; Formlabs Permanent Crown Resin [FP]), and one feldspathic glass-matrix ceramic block (Vita Mark II [VM]) as the control group. Specimens of each material were divided into two subgroups: thermal cycled or non-thermal cycled (n = 10). BFS and VHN tests were performed on all groups. Data were analyzed with two-way ANOVA and post hoc Tukey test (α = 0.05).ResultsThe type of restorative material used for the specimen had a statistically significant influence on both BFS and VHN values. However, thermal cycling did not affect the BFS and VHN values. After thermal cycling, the results of the BFS test were ranked from best to worst as follows: CS, FP, SC, VE, then VM. For the VHN values, the order from best to worst was as follows: VM, VE, CS, FP, then SC.Conclusions3D printed and milled composite groups showed higher BFS than feldspathic ceramics. When the VHN results were examined, it was seen that the 3D resin groups had the lowest VHN values. Furthermore, it was observed that the thermal cycle had no effect on BFS or VHN.

Correction: Smirnov et al. Experimental and Statistical Modeling for Effect of Nozzle Diameter, Filling Pattern, and Layer Height of FDM-Printed Ceramic–Polymer Green Body on Biaxial Flexural Strength of Sintered Alumina Ceramic. J. Compos. Sci. 2023, 7, 381

The authors would like to highlight the following correction to their published paper [...]