Investigating the impact of surface treatments on tensile bond strength between pediatric prefabricated zirconia crowns and primary maxillary incisors with various types of luting cement: an in vitro study.

This study aimed to evaluate the effects of two surface treatments on the tensile bond strength of prefabricated zirconia crowns (PZCs) using bioactive and resin cements. Forty extracted human primary maxillary incisors were prepared and divided into four groups based on surface treatment and cement type: (1) sandblast with bioactive cement, (2) sandblast with resin cement, (3) 10-methacryloyloxydecyl dihydrogen phosphate (10-MDP) with bioactive cement, and (4) 10-MDP with resin cement. After 24h of cementation, specimens underwent 5000 thermocycling cycles between 5°C and 55°C. Tensile bond strengths were measured using a universal testing machine. The data were analyzed using two-way ANOVA and Tukey's post hoc test, with significance set at p < 0.05. The mean tensile bond strengths observed were 2.25 ± 1.27MPa for sandblast with bioactive cement, 1.39 ± 0.95MPa for sandblast with resin cement, 2.45 ± 1.15MPa for 10-MDP with bioactive cement, and 1.68 ± 1.03MPa for 10-MDP with resin cement. Significant improvements in bond strength were observed in the bioactive cement group treated with 10-MDP compared to those treated with sandblasting (p < 0.05). The 10-MDP treatment did not enhance bond strength for the resin cement compared to sandblasting. Bioactive cement generally provides a higher tensile bond strength than resin cement. While 10-MDP treatment enhances bond strength when used with bioactive cement, it does not show a similar enhancement when used with resin cement compared to sandblasting, indicating its effectiveness is selective based on the type of cement used.

Comparative cell viability of dentin-bonding adhesive systems on human dental pulp stem cells: time-dependent analysis

BackgroundRestorative materials are in prolonged contact with living tissues such as oral mucosa, dentin, pulp, periodontal, and periapical tissues. Therefore, the potentially harmful effects of these materials and their components on oral tissues should be evaluated before clinical use. This study aimed to compare the cell viability of different adhesive systems (ASs) on human dental pulp stem cells (hDPSCs).MethodsThree ASs that combining methacryloyloxydecyl dihydrogen phosphate (MDP) monomer with new hydrophilic amide monomers [Clearfil Universal Bond Quick(CUBQ), Kuraray Noritake], self-reinforcing 3D monomer [Bond Force II(BFII), Tokuyama)], and dual-cure property [Futurabond DC(FBDC), VOCO] were used. Three (n = 3) samples were prepared for each group. Dental pulp stem cells were isolated from ten patients’ extracted third molar teeth. Samples were incubated in Dulbecco’s modified Eagle’s medium (DMEM) for 24 h (h), 72 h, and 7 days (d) to obtain extracts. For the control group, cells were cultured without DBA samples. Cell viability of ASs extracts was measured using a cell proliferation detection kit (WST-1, Roche). Statistical analysis was performed using two-way ANOVA and post-hoc (Duncan) tests (p < 0.05).ResultsAt 24 and 72 h statistically significant differences were determined between control and BFII, control and FBDC groups (p < 0.05), while no differences between control and CUBQ groups (p > 0.05). On the 7th d, statistically significant differences were found between the control and experimental groups (p < 0.05), while no differences between experimental groups (p > 0.05). A statistically significant difference was detected for the BFII group over the three-time interval (p < 0.05). The lowest cell viability was observed for the FBDC group at 24 h, and the difference was statistically significant when compared with 72 h and 7th d (p < 0.05).ConclusionAll ASs showed different cell viability values at various exposure times. It should be taken into consideration that pH values, as well as the contents of ASs, have a significant effect on the cell viability.

Bottom-Up Assembling Hierarchical Enamel-Like Bulk Materials with Excellent Optical and Mechanical Properties for Tooth Restoration.

Enamel has good optical and mechanical properties because of its multiscale hierarchical structure. Biomimetic construction of enamel-like 3D bulk materials at nano-, micro-, mesh- and macro-levels is a challenge. A novel facile, cost-effective, and easy large-scale bottom-up assembly strategy to align 1D hydroxyapatite (HA) nanowires bundles to 3D hierarchical enamel structure with the nanowires bundles layer-by-layer interweaving orientation, is reported. In the strategy, the surface of oleate templated ultralong HA nanowires with a large aspect ratio is functionalized with amphiphilic 10-methacryloyloxydecyl dihydrogen phosphate (MDP). Furtherly, the MDP functionalized HA nanowire bundles are assembled layer-by-layer with oriented fibers in a single layer and cross-locked between layers at a certain angle at mesoscale and macroscale in the viscous bisphenol A-glycidyl methacrylate (Bis-GMA) ethanol solution by shear force induced by simple agitation and high-speed centrifugation. Finally, the excessive Bis-GMA and ethanol are removed, and (Bis-GMA)-(MDP-HA nanowire bundle) matrix is densely packed under hot pressing and polymerized to form bulk enamel-like materials. The composite has superior optical properties and comparable comprehensive mechanic performances through a combination of strength, hardness, toughness, and friction. This method may open new avenues for controlling the nanowires assembly to develop hierarchical nanomaterials with superior properties for many different applications.

Bond Strength of Milled and Printed Zirconia to 10-Methacryloyloxydecyl Dihydrogen Phosphate (10-MDP) Resin Cement as a Function of Ceramic Conditioning, Disinfection and Ageing.

This study aimed to assess the suitability of printed zirconia (ZrO2) for adhesive cementation compared to milled ZrO2. Surface conditioning protocols and disinfection effects on bond strength were also investigated. ZrO2 discs (n = 14/group) underwent either alumina (Al2O3) airborne particle abrasion (APA; 50 µm, 0.10 MPa) or tribochemical silicatisation (TSC; 110 µm Al2O3, 0.28 MPa and 110 µm silica-modified Al2O3, 0.28 MPa), followed by disinfection (1 min immersion in 70% isopropanol, 15 s water spray, 10 s drying with oil-free air) for half of the discs. A resin cement containing 10-methacryloyloxydecyl dihydrogen phosphate (10-MDP) was used for bonding (for TSC specimens after application of a primer containing silane and 10-MDP). Tensile bond strength was measured after storage for 24 h at 100% relative humidity or after 30 days in water, including 7500 thermocycles. Surface conditioning significantly affected bond strength, with higher values for TSC specimens. Ageing and the interaction of conditioning, disinfection and ageing also impacted bond strength. Disinfection combined with APA mitigated ageing-related bond strength decrease but exacerbated it for TSC specimens. Despite these effects, high bond strengths were maintained even after disinfection and ageing. Adhesive cementation of printed ZrO2 restorations exhibited comparable bond strengths to milled ZrO2, highlighting its feasibility in clinical applications.

Repair of monolithic zirconia restorations with different direct resin composites: effect on the fatigue bonding and mechanical performance

ObjectiveThe study aims to evaluate the shear bond and flexural strength fatigue behavior of yttrium-stabilized zirconia (4YSZ) repaired using different resin composites.Materials and methodsCylindric specimens of 4YSZ were obtained for the bond strength (Ø = 6 mm, 1.5 mm of thickness) and biaxial flexural strength (Ø = 15 mm, 1 mm of thickness) fatigue tests and divided into 3 groups according to the repair resin composite: EVO (nanohybrid), BULK (bulk-fill), and FLOW (flowable). The zirconia surface was air-abraded with alumina particles, a 10-methacryloyloxydecyl dihydrogen phosphate (10-MDP) primer was applied, and the resin composite was build-up over the zirconia. Fatigue shear bond strength and flexural fatigue strength tests were performed (n = 15). One-way ANOVA and Tukey post hoc tests were carried out for both outcomes, besides scanning electron microscopy and finite element analysis.ResultsThe repair material affected the fatigue shear bond strength of zirconia ceramic. The BULK group (18.9 MPa) depicted higher bond strength values than FLOW (14.8 MPa) (p = 0.04), while EVO (18.0 MPa) showed similar results to both groups. No effect was observed for the mechanical behavior (p = 0.53). The stress distribution was similar for all groups.ConclusionThe repair of yttrium-stabilized zirconia (4YSZ) ceramics with bulk-fill resin composites was the best option for high fatigue bond strength. However, the fatigue mechanical performance was similar regardless of the applied repair material.Clinical relevanceThe repair of yttrium-stabilized zirconia (4YSZ) monolithic restorations may be performed with nanohybrid and bulk-fill resin composites in order to promote longevity in the treatment.

Dentin surface modification by MDP to improve dentin bonding stability: Topological enhancement and mineralization of collagen structure in hybrid layers

Decades of research have been conducted on 10-Methacryloyloxydecyl dihydrogen phosphate (MDP) through numerous studies. The mechanisms by which its residual calcium salts benefit dentin bonding remain undetermined. The objective of the research was to investigate the role and process of remaining calcium salts in the priming procedure and their capacity for remineralization. The investigation focused on the variations in topological structure, mechanical properties, and chemical interactions between the main agent and the dentin surface. Two adhesive modes including prime-and-rinse(P&R) and prime-and-nonrinse (P&NR) utilized to evaluate the bonding performance and remineralization ability. The findings indicated that both P&R and P&NR methods could eliminate the smear-layer, uncover dentinal-tubules, and generate a textured/rough surface on the dentin. Collagen fibrils exhibited a greater presence of inorganic minerals in the P&NR mode. Compared to control group, both P&R and P&NR groups improved immediate and aging bond strength significantly (P < 0.05). AFM and 3D-STORM revealed MDP and its residual calcium salts distributed in collagen fibrils and expanded collagen matrix. In the P&NR group, TEM revealed that the dentin collagen matrix experienced some remineralization, and there was also mineralization within the collagen fibrils embedded in the bonding interface. Thus, MDP priming improved dentin bonding stability. Residual calcium salts of P&NR process can enhance topological structure of the collagen matrix and induce intrafibrillar mineralization.

Composite Containing Calcium Phosphate Particles Functionalized with 10-MDP

The phosphate ester monomer 10-methacryloyloxydecyl dihydrogen phosphate (10-MDP) is capable of bonding to hydroxyapatite and, for this reason, is a key component of several self-etch adhesives. In this study, dicalcium phosphate dihydrate particles (DCPD; CaHPO4.2H2O) were functionalized with 10-MDP and used to formulate an experimental composite with 50 vol% inorganic content (3:1 DCPD:silanated barium glass ratio) dispersed in a BisGMA/TEGDMA matrix. The tested hypothesis was that DCPD functionalization would improve the composite’s mechanical performance without compromising Ca2+ release. Composites containing nonfunctionalized DCPD or only reinforcing glass (in both cases, with or without 10-MDP mixed in the resin phase) were used as controls. Materials were tested for degree of conversion (DC; by Fourier transform infrared spectroscopy), water sorption (WS) and solubility (SL; according to ISO 4049), biaxial flexural strength (BFS)/modulus (FM) after 24 h and 5 mo in water, and 28-d Ca2+ release in water (by plasma-coupled optical emission spectroscopy). Data were analyzed using analysis of variance/Tukey test (alpha: 5%). DCPD functionalization did not interfere with DC. The composite containing functionalized DCPD showed significantly lower WS and SL in comparison with the material formulated with nonfunctionalized particles. The presence of 10-MDP (as a functionalizing agent or dispersed in the resin phase) reduced the composite’s initial BFS and FM. After 5 mo in water, the composite with functionalized DCPD and both glass-only composites were able to maintain their mechanical properties at levels statistically similar to what was observed after 24 h. Ca2+ release was significantly reduced in both formulations containing 10-MDP. In conclusion, DCPD functionalization with 10-MDP increased the composite’s resistance to hydrolytic degradation, improving its mechanical stability after prolonged water storage. However, the impaired water transit at the particle-matrix interface led to a reduction in Ca2+ release.

Effect of a 10-Methacryloyloxydecyl Dihydrogen Phosphate- treated Bioceramic Sealer on the Bond Strength of an Endodontic Fiber Post: Multilayer Composite Disk Models and Ultra-highspeed Imaging Analysis

Multiple materials are found in the root canal after fiber-post cementation. The layer of a bioceramic-based (BC) sealer may affect the bond strength (σBS) of the fiber post in the root canal. The purpose of this study was to employ multilayer compos-ite-disk models in diametral compression to investigate whether the bond strength between a fiber post and root dentin can be in-creased by the application of a primer on the BC sealer. The multilayers of materials in the root canal required 3D finite-element (FE) stress analyses (FEA) to pro-vide precise σBS values. First, BC sealer was characterized using x-ray powder diffraction (XRD) to determine when the sealer com-pletely set and the types of crystals formed to select which primer to apply to the sealer. We selected a 10-methacryloyloxydecyl dihydrogen phosphate (10-MDP)-based primer to treat the BC sealer before post cementation. Ultra-highspeed (UHS) imaging was utilized to analyze the crack initiation interface. The obtained failure force was used in FE analysis to calculate σBS. UHS imaging validated the fracture interface at the post-dentin junction as FEA simulations predicted. σBS values of the fiber posts placed with various material combinations in the root canal were 21.1 ± 3.4 (only cement/ post), 22.2 ± 3.4 (BC sealer/cement/post) and 28.6 ± 4.3 MPa (10-MDP primer treated BC sealer/cement/post). The 10-MDP-treated BC sealer exhibited the highest σBS (p < 0.05). The multilayer composite disk model proved reliable with diametral compression testing. The presence of BC sealer in the root canal does not reduce σBS of the fiber post. Conditioning the BC sealer layer with 10-MDP primer before fiber-post cemen-tation increases σBS.

The Effect of Titanium Anodization on the Bond Strength of 10-methacryloyloxydecyl dihydrogen phosphate (10-MDP) Resin Cement.

To examine the effects of anodization and different surface modifications of titanium on bond strength to 10-methacryloyloxydecyl dihydrogen phosphate (10-MDP) resin cement. Grade 5 titanium alloy disks (n = 160) were assigned to one of five prebonding surface treatment study groups (polished; polished and anodized; polished, etched, and anodized; sandblasted; sandblasted and anodized). Disks were adhesively bonded with 10-MDP resin cement (Panavia 21; bonding area: 3.3 mm in diameter) to composite resin cylinders. In each study group, tensile bond strength tests were conducted after 24 ± 1 hours and after 6 months (180 ± 2 days) of water storage (n = 16 specimens per water storage subgroup). Debonded specimens were stereomicroscopically analyzed to determine their fracture mode. Statistics included one-way and multifactorial ANOVA and Tukey post hoc tests (α = .05). Anodization and water storage did not significantly (P ≥ .389) affect tensile bond strength. Although subgroups of polished samples had significantly (P ≤ .031) lower bond strengths (subgroup mean values: 20 to 26 MPa) than etched or sandblasted samples (subgroup mean values: 29 to 33 MPa), they nonetheless exceeded the empirical threshold of 10 MPa used as a criterion for clinical recommendation. The fracture mode of all test specimens was predominantly cohesive. Anodization of titanium surfaces can be performed without weakening the adhesion of 10-MDP-based resin cement to titanium.

10-Methacryloyloxydecyl dihydrogen phosphate in resin-to-zirconia bonding durability: a systematic review and meta-analysis

Objective: To systematically assess the durability of the 10-methacryloyloxydecyl dihydrogen phosphate (10-MDP) pretreated resin-to-zirconia bonding and conducted a meta-analysis to provide clinical guidance on zirconia bonding strategies. Methods: A comprehensive search was conducted on PubMed, Scopus, Web of Science, CNKI, and Wanfang database to identify relevant studies on the resin-to-zirconia bonding after surface pretreatment with 10-MDP. Strict inclusion and exclusion criteria were applied to select appropriate literature and extract essential information and data. The included studies were categorized based on aging methods (water storage, thermocycling, or both), 10-MDP application methods (within primer, adhesive, resin cement, or both), and additional surface treatments (alumina sandblasting, tribochemical silica coating, acid etching, laser etching, and plasma treatment) and were analyzed by Review Manager 5.4. The evaluation indicator was the bonding strength of zirconia after surface pretreatment with 10-MDP. Results: A total of 72 studies were included in the systematic review, with 68 studies eligible for the meta-analysis. The bonding strength of zirconia decreased significantly after aging [P<0.001; mean difference (MD): 5.58; 95%CI: 5.11-6.05]. No significant differences in bonding strength of zirconia were observed after aging when employing various application methods of 10-MDP (all P>0.05). The bonding strength of zirconia was significantly enhanced after aging when 10-MDP was applied in conjunction with additional surface treatments, as compared to the application of 10-MDP alone (P<0.001; MD: 10.17; 95%CI: 8.20-12.14). Conclusions: The bonding strength of zirconia pretreated with 10-MDP exhibited a reduction after undergoing water storage or thermocycling. The application of 10-MDP with additional surface treatments enhanced the bonding strength of zirconia after aging, while the application methods of 10-MDP did not exert an influence.

Comparison of Shear Bond Strength in Novel Calcium Silicate-Based Materials to Composite Resin

The purpose of this study was to evaluate whether the newly introduced calcium silicate-based materials with fast-setting properties could be appropriately used as basement materials in indirect pulp treatment (IPT). This was performed by quantifying the durability of adhesion between the material and composite resin, measured by the shear bond strength (SBS). Five calcium silicate-based materials, TheraCal LC&lt;sup&gt;®&lt;/sup&gt; (TLC), TheraCal PT&lt;sup&gt;®&lt;/sup&gt; (TPT), TheraBase&lt;sup&gt;®&lt;/sup&gt; (TB), Well-Root™ PT (WPT), and Endocem&lt;sup&gt;®&lt;/sup&gt; MTA (EMTA), as well as two glass ionomer-based materials, Fuji II and Fuji II LC, were included. Specimens containing these materials were manufactured and bonded to composite resin with a universal adhesive applied in self-etch mode. The SBS values and failure modes were recorded, and the mean SBSs of the materials were compared. Both TPT and TB exhibited SBS values that were similar to TLC, while both WPT and EMTA appeared to have statistically lower SBS values. Mixed failure was commonly observed in TLC and TPT, while all WPT and EMTA samples showed cohesive failure. In comparison with TLC and TPT, more samples with cohesive failure were observed in TB, implying that this material forms a stronger bond with composite resin. Together with the ability of TB to chemically bind to dentin due to its 10-methacryloyloxydecyl dihydrogen phosphate component, TB seems to be a promising material for IPT within the limitations of this in vitro study.

MDP-salts as an adhesion promoter with MDP-primers and self-adhesive resin cement for zirconia cementation

PurposeTo evaluate the effect of zirconia priming with MDP-Salt before MDP containing primers and self-adhesive cement on the shear bond strength.Materials and methodsFully sintered high translucent zirconia specimens (n = 120) were assigned into 2 groups (n = 60 each): Control (No Pretreatment) and Methacryloyloxydecyl dihydrogen phosphate salt (MDP-Salt) pretreated. Each group was divided into 3 subgroups (n = 20) according to cementation protocol: 1) MDP + Silane primer and conventional resin cement, 2) MDP+ Bisphenyl dimethacrylate (BPDM) primer and conventional resin cement, and 3) MDP containing self-adhesive resin cement. Shear bond strength (SBS) was measured after 10,000 thermocycling. Contact angle was measured for tested groups. Surface topography was assessed using a 3D confocal laser scanning microscope (CLSM). Weibull analysis was performed for SBS and one-way ANOVA for contact angle and surface topography measurements (α = 0.05).ResultsThe use of MDP-Salt significantly improved the SBS (p < .05) for all tested subgroups. Self-adhesive cement showed an insignificant difference with MDP + Silane group for both groups (p > .05). MDP + BPDM showed a significantly lower characteristic strength compared to self-adhesive resin cement when both were pretreated with MDP-Salt. No difference between all tested groups in the surface topographic measurements while MDP-Salt showed the highest contact angle.ConclusionMDP-Salt pretreatment can improve bonding performance between zirconia and MDP containing products.

Alumina and glass-bead blasting effect on bond strength of zirconia using 10-methacryloyloxydecyl dihydrogen phosphate (MDP) containing self-adhesive resin cement and primers

In fact, bonding of zirconia restorations is still a big challenge in clinical situations and many bonding protocols discussed in literature might be still controversial. The aim of this was to study assess the bond strength of zirconia after alumina and glass-bead pre-treatments with two different primers in combination with conventional resin cement and 10-methacryloyloxydecyl dihydrogen phosphate (MDP) containing self-adhesive resin cement without priming. Fully sintered high translucent zirconia samples (n = 160) were assigned into 2 groups of pre-treatments (n = 80): Alumina-sandblasting (AB) and Glass-bead (GB). Then, each group was divided into 4 sub-groups according to priming and cement used (n = 20 each): conventional self-adhesive resin cement, MDP-silane Primer, MDP primer both with conventional self-adhesive resin cement, and MDP contained cement. Shear bond strength (SBS) was measured after thermocycling. Failure mode was analyzed using stereomicroscope. Contact angle and surface topography were investigated using other fully sintered samples (n = 30) constructed for that sole purpose, divided into control (no pre-treatment [unmodified], alumina-, and glass-bead sandblasted groups). Two-way ANOVA was performed for SBS and failure mode was analyzed. The use of Alumina-sandblasting showed higher SBS compared to Glass-bead pre-treatment for MDP-silane primer (p = 0.034) and MDP primer (p < 0.001). While MDP contained cement showed higher but insignificant SBS when pre-treated with glass-beads. Alumina-sandblasting and glass-bead pre-treatments improve bond strength of zirconia combined using primers before cementation with conventional resin cement. Also, self-adhesive MDP contained cement along with surface pre-treatment showed the highest achievable bond strength. It was concluded that both alumina-sandblasting and glass-bead blasting improved SBS combined with MDP containing self-adhesive resin cement reducing the required clinical steps during cementation of zirconia restorations.

Which metal surface treatment improves the bond strength between metal alloys and acrylic resin in removable partial dentures? A systematic review.

The union of the metal removable partial denture framework to the heat polymerized acrylic resin is related to prosthesis longevity. However, methods to enhance this bond are not clear to clinicians and dental laboratory technicians. The purpose of this systematic review was to identify which metal surface treatments best increase the bond strength between heat polymerized acrylic resin and removable partial denture alloys. This review was carried out following the Preferred Reporting Items for Systematic Reviews and Meta-Analyses (PRISMA) guidelines and registered in the International Prospective Registry of Systematic Reviews (PROSPERO) database (CRD42022384926). Electronic searches were carried out independently, by 3 examiners in Medline/PubMed, Scopus, and Web of Science databases, and in the nonpeer-reviewed literature via ProQuest. The electronic searches resulted in 4143 articles, with 4055 after removing duplicates. After reading the titles and abstracts, 37 articles were selected for reading in full-text version, from which 6 articles were included. All studies evaluated materials for conventional acrylic resin denture base (heat polymerized), processed by water bath, bonded to metal. For the metal framework alloys, cobalt chromium (Co-Cr) alloys were used in 2 studies, titanium (Ti) in 2 studies, and Co-Cr and Ti in the other 2 studies. Different metal surface treatments were used as airborne-particle abrasion with aluminum oxide (particle sizes of 50µm, 110µm, and 250µm) followed by the primer application and the isolated use of the primer, compared to the absence of isolated intervention or airborne-particle abrasion of the metal surface. Among the different primers used, those based on 10-methacryloyloxydecyl dihydrogen phosphate (10-MDP) showed the highest acrylic resin-to-metal bond strength values. Airborne-particle abrading the metal with Al2O3 followed by applying a 10-MDP-based primer, increased the bond strength between metal framework alloys and heat polymerized acrylic resin denture base material.

Effect of varying functional monomers in experimental self-adhesive composites: polymerization kinetics, cell metabolism influence and sealing ability

The aim was to evaluate the effects of adding different functional monomers to experimental self-adhesive composites (SACs) on polymerization kinetics, cell metabolic activity, and sealing ability. SACs were formulated using urethane dimethacrylate as the base monomer and triethylene glycol dimethacrylate. Additionally, 10 wt.% of distinct functional monomers were added - 10-methacryloyloxydecyl dihydrogen phosphate, glycerol phosphate dimethacrylate (GPDM), 2-hydroxyethyl methacrylate (HEMA) or hydroxyethyl acrylamide (HEAA). ATR-FTIR was used to determine real-time polymerization kinetics (20 min, n = 3). The final extrapolated conversion and polymerization rates were determined (DC ,max; Rp ,max). The DC ,max values were employed to calculate volumetric shrinkage. The MTT assay was performed on MDPC-23 cells using disc extracts at different concentrations (n = 8). Class V cavities were prepared in 60 sound human molars, assigned to six groups (n = 10), depending on the composite used and aging type (T0 or TC, if thermocycled for 10 000 cycles). One-way ANOVA, two-way, and Kruskal–Wallis tests were employed to treat the data (ɑ = 0.05). Varying the functional monomers had a large impact on DC,max, as confirmed by one-way ANOVA (p<0.001). The highest was obtained for HEMA (64 ± 3%). The HEMA and HEAA formulations were found to be significantly more toxic at concentrations below 100%. For microleakage, having a functional monomer or not did not show any improvement, irrespective of margin or aging period (Mann–Whitney U, p > 0.05). Larger functional monomers MDP and GPDM affected polymerization properties. Conversely, their acidity did not seem to be detrimental to cell metabolic activity. Regarding sealing ability, it seems that the functional monomers did not bring an advantage to the composites. Varying the functional monomer in SACs had a clear impact on the polymerization kinetics as well as on their cytotoxic potential. However, it did not confer better microleakage and sealing. Claiming self-adhesiveness based only on functional monomers seems dubious.

Effects of Different Primers on the Bond Strength to Properly and Excessively Etched Ceramic-coated Zirconia.

To determine the effects of various primers on the immediate and long-term bond strength of ceramic-coated ultratranslucent zirconia that is properly or excessively etched. Ceramic-coated zirconia plates were etched with 9.5% hydrofluoric acid (HF) for 2 or 5 minutes, after which the surface morphology and elemental composition were examined. The etched specimens were treated with different primers including methacryloyloxydecyl dihydrogen phosphate (MDP)-only containing primer, silane-only containing primer, MDP and silane-containing ceramic primer as well as MDP and silane-containing adhesive system. For surface contact angle and shear bond strength (SBS) data, the difference between groups was evaluated by one-way analysis of variance (ANOVA) and three-way ANOVA factorial analysis, respectively. The statistical significance level of 0.05 was set and the Tukey test and the Dunnett-T3 test were used for post-hoc multiple comparisons. Excessive etching (9.5% HF for 5 minutes) led to overconsumption of the glass layer and exposure of zirconia substrate compared to proper etching (9.5% HF for 2 minutes). Among different primers, the surface contact angle of the silane-only containing primer group was the lowest. The silane-only containing primer and MDP and silane-containing ceramic primer produced higher shear bond strength of properly and excessively etched ceramic-coated zirconia, respectively, both before and after thermal aging. The silane-only containing primer and MDP and silane-containing primer can obtain better immediate and long-term shear bond strength for properly and excessively etched ceramic-coated zirconia, respectively.

Effect of the Absence of HEMA on the Bonding Properties of Universal Adhesive Systems Containing 10-MDP: An In Vitro Study.

To evaluate the absence of 2-hydroxyethyl methacrylate (HEMA) on the adhesive properties with enamel and dentin of universal adhesive systems containing 10-methacryloyloxydecyl dihydrogen phosphate (MDP). One hundred and twelve caries-free third molars were used to test adhesion to dentin (n=64) and enamel (n=48). For each substrate, teeth were divided into eight experimental groups: four different adhesives each using two adhesive strategies. The adhesives used were: (1) Scotchbond Universal (SBU, 3M Oral Care, St Paul, MN, USA) as a HEMA-containing universal adhesive; (2) Gluma Bond Universal (GBU, Kulzer, Hanau, Germany); (3) Solare Universal Bond (SUB, GC, Tokyo, Japan); and (4) Zipbond Universal (ZIP, SDI, Victoria, Australia) as HEMA-free universal adhesives. The adhesive strategies used were etch-and-rinse (ER) and self-etch (SE). For dentin tests, the occlusal third of the crown of all teeth was removed and an adhesive protocol was applied. After completing the restoration, specimens were sectioned into bonded sticks (0.8 mm 2) and tested for microtensile bond strength (μTBS), in situ degree of conversion (DC), and nanoleakage (NL) by scanning electron microscopy. For enamel tests, teeth were sectioned into four parts (buccal, lingual, and proximal), and an adhesive protocol was applied. After completing the restoration, the specimens were tested for their microshear bond strength (μSBS). For in situ degree of conversion (DC) and nanoleakage (NL) evaluation of enamel, the specimens were sectioned in slices to be evaluated. The data for each substrate were subjected to two-way ANOVA and Tukey's test (α=0.05) for each property evaluated. The SBU and ZIP adhesives showed the highest μSBS, and DC (dentin and enamel) and lower NL (dentin) values compared to GBU and SUB (p=0.001). However, SBU showed better results in terms of μTBS and μSBS (SE strategy), and DC (dentin and enamel) than ZIP. Strategy ER presented higher values of μTBS and μSBS when compared to strategy SE (p=0.001), except for SBU. The effect of the absence of HEMA in commercial universal adhesive systems on enamel and dentin adhesive properties appears to be material-dependent.

Influence of varying titanium base abutment heights on retention of zirconia restorations: An in vitro study

Implant manufacturers have introduced titanium base (Ti-Base) abutments with increased abutment heights, ostensibly, to increase the retention of the bonded restoration and to improve overall strength. However, evidence regarding the effects of increasing Ti-Base height on improving retention is lacking. The purpose of this in vitro study was to evaluate the effect of different Ti-Base abutment heights on the retention of zirconia implant-supported crowns. Thirty Ti-Base abutments of the same diameter and heights of 3.5mm (n=10), 4.5mm (n=10), and 5.5mm (n=10), were used for testing. Zirconia restorations were cemented onto the Ti-Base abutments with a resin cement after treatment with a 10-methacryloyloxydecyl dihydrogen phosphate primer by a single operator using a positioning device. The zirconia-Ti-Base restorations were tightened to an implant analog embedded in an autopolymerizing resin block. The specimens were placed and tested in a universal testing machine for pull-out testing. Retention was measured by recording the force at load drop. Statistical analysis was performed using 1-way analysis of variance with the Tukey method for pairwise comparisons. The abutment height had a significant effect on retention (P=.010). Ti-Base abutments of 4.5 and 5.5mm had significantly greater retention than Ti-Base abutments of 3.5mm (P=.020, P=.040, respectively). However, Ti-Base abutments of 4.5 and 5.5mm in height were statistically similar (P=.890). An increase in the height of Ti-Base abutments above the standard 3.5mm height significantly improved the retention of the overlying restoration.

Effects of methacryloyloxydecyl dihydrogen phosphate on bonding of tri-n-butylborane-initiated resin to human enamel.

This study investigated the effect of 10-methacryloyloxydecyl dihydrogen phosphate (MDP) in methyl methacrylate (MMA) monomer on the adhesion of tri-n-butylborane (TBB)-initiated resins (MDP/MMA-TBB resins) to human enamel. Enamel surface conditions were either polished only or phosphatized surfaces. The 1.0, 1.7, and 2.0 mol% MDP/MMA-TBB resins, 4-methacryloxyethyl trimellitate anhydride (4-META)/MMA-TBB resin and MMA-TBB resin were prepared as luting materials. The shear bond strength was determined before and after thermocycles, and the results were compared using non-parametric statistical analyses (each, n=15). The MDP/MMA-TBB resins showed significantly better bond durability to enamel than other resins with or without etching. The 1.7 and 2.0 mol% MDP/MMA-TBB resins were suggested to be the optimum MDP concentrations from pre- and post-thermocycling results for the non-etched specimens. The TBB initiator resin including MDP was shown to be effective in bonding to human enamel, and this effect was enhanced in combination with phosphate treatment.

Comparative study of the bond strength of ZirCAD Multi and ZirCAD Prime ceramics with different types of cements

Zirconia ceramic is a modern material used for different types of prosthetic constructions, characterized by high mechanical resistance and aesthetics. The main difficulties in treatment are related to ensuring a stable and durable bond between the ceramic and dentin. This study examined the bonding strength of ZirCAD Multi (3rd generation) and ZirCAD Prime (5th generation) ceramics when using different types of cements before and after sandblasting the surface of zirconia with Al2O3. For this purpose, an experimental setup was created by 3D printing, in which sintered ceramic cylinders were cemented to dentin slices of natural teeth with different types of cements. From the formed ceramic-dentin constructions, test specimens were cut with a microtome and tested for tensile strength. The results showed an increase in the strength of the bond after sandblasting from 1.1 MPa to 2.4 MPa for ZirCAD Multi and from 1.6 MPa to 3.3 MPa for ZirCAD Prime. Zirconia ceramic ZirCAD Prime (5th generation) showed higher adhesion resistance, with the strongest bond being with the Speed Cem Plus and Panavia V5 cements. With ZirCAD Multi, the maximum tensile strength was achieved with the Rely X Luting Plus and Speed Cem Plus cements. Optimal strength and bond resistance were registered between the new fifth-generation zirconia ceramic and composite cements with MDP (10-methacryloyloxydecyl dihydrogen phosphate) primers.