Abstract
The development of lead-free solders has been an essential task in the electronics industry because of the restriction of lead use by legislation. Among the candidates, Sn-Ag-Cu group of solder alloys have great advantages to replace the conventional Sn-Pb solder. In this study, the wetting and intermetallic study between Sn-3.5Ag-1.0Cu-xZn lead-free solder reacting on copper substrate were investigated under different soldering conditions. The addition of 0.7wt% of Zn improved the wettability on Cu substrate since it has the highest spreading area at 310°C. The Cu6Sn5 and Cu3Sn phases are the main interface intermetallic formed and these intermetallics increased in thickness with time and temperature. At 270°C, the addition of 0.7wt% Zn retarded the growth of Cu3Sn intermetallic until 10 min of the soldering time. Generally the addition of Zn was beneficial in retarding the total intermetallic thickness.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.