Wear resistance of 3D-printed denture tooth resin opposing zirconia and metal antagonists

Abstract

Statement of problemAdditive manufacturing technology can be used for denture bases and also denture teeth. Therefore, the mechanical properties of 3D-printed resin denture teeth should be evaluated. PurposeThe purpose of this in vitro study was to compare the wear resistance of 3D-printed denture tooth resin with that of conventionally prefabricated denture teeth. Material and methodsEighty substrate specimens were prepared with 5 kinds of resin denture teeth: 3D-printed denture tooth resin (DENTCA denture tooth resin; DENTCA, Inc), Artic 6 (Kulzer GmbH), Preference (Candulor AG), Premium 6 (Kulzer GmbH), and Surpass (GC Corp). The 3D-printed denture tooth specimens were made of methacrylate-based photopolymerized resin by stereolithography 3D printing. Antagonistic surfaces were made from zirconia by milling and from cobalt-chromium (Co-Cr) alloy by 3D printing and casting. The specimens were loaded at 49 N for 30 000 cycles under thermocycling conditions in a mastication simulator. Wear resistance was measured by calculating the volume of substance lost. Wear surface characteristics were observed by using a scanning electron microscope (SEM). Two-way ANOVA was used to analyze the data (α=.05). ResultsThe influence of the resin denture teeth and the type of antagonist were both statistically significant. The wear volume loss of the 3D-printed denture tooth resin was higher than that of Artic 6 and Preference when opposing the zirconia and the metal antagonists (P<.05). The 3D-printed denture tooth resin did not show a significant difference from Premium 6 with the zirconia and the metal antagonists or Surpass with the zirconia antagonist. From the SEM images, the specimens of the 3D-printed denture tooth resin showed a relatively smooth surface with the zirconia antagonist and exhibited cracks when opposed by the metal antagonist. ConclusionsThe results suggest that 3D-printing by using resin materials provides adequate wear resistance for denture tooth use.