Effects of printing orientation and artificial ageing on martens hardness and indentation modulus of 3D printed restorative resin materials

Abstract

BackgroundThree-dimensional (3D) printing is increasingly used to fabricate dental restorations due to its enhanced precision, consistency and time and cost-saving advantages. The properties of 3D-printed resin materials can be influenced by the chosen printing orientation which can impact the mechanical characteristics of the final products. PurposeThe objective of this study was to evaluate the influence of printing orientation and artificial ageing on the Martens hardness (HM) and indentation modulus (EIT) of 3D-printed definitive and temporary dental restorative resins. MethodsDisk specimens (20 mm diameter × 2 mm height) were additively manufactured in three printing orientations (0°, 45°, 90°) using five 3D-printable resins: VarseoSmile Crownplus (VCP), Crowntec (CT), Nextdent C&B MFH (ND), Dima C&B temp (DT), and GC temp print (GC). The specimens were printed using a DLP 3D-printer (ASIGA MAX UV), while LavaTM Ultimate (LU) and Telio CAD (TC) served as milled control materials. Martens hardness (HM) and indentation modulus (EIT) were tested both before and after storage in distilled water and artificial saliva for 1, 30, and 90 days at 37 °C. Results90° printed specimens exhibited higher HM than the other orientations at certain time points, but no significant differences were observed in HM and EIT between orientations for all 3D-printed materials after 90 days of ageing in both aging media. LU milled control material exhibited the highest HM and EIT among the tested materials, while TC, the other milled control, showed similar values to the 3D printed resins. CT and VCP (definitive resins) and ND displayed higher Martens parameters compared to DT and GC (temporary resins). The hardness of the 3D-printed materials was significantly impacted by artificial ageing compared to the controls, with ND having the least hardness reduction percentage amongst all 3D-printed materials. The hardness reduction percentage in distilled water and artificial saliva was similar for all materials except for TC, where higher reduction was noted in artificial saliva. SignificanceThe used 3D printed resins cannot yet be considered viable alternatives to milled materials intended for definitive restorations but are preferable for use as temporary restorations.