Abstract
This paper presents the results of the investigation into the electrical conductivity of thin films based on tin dioxide (SnO2) nanoparticles, a film consisting of copper phthalocyanine-3,4′,4″,4‴-tetrasulfonic acid tetrasodium salt (CuPc–4SO3Na) molecules, and a composite film based on a mixture of equal parts by volume of the two materials upon adsorption of ammonia. The adsorption experiments have been carried out in a vacuum at room temperature with an increase in the ammonia pressure to 3 × 103 Pa from the residual gas base pressure of 5 × 10–1 Pa. It has been found that, in the case of a single-component film based on SnO2 nanoparticles, an increase in the electrical conductivity reaches 100% and is not completely reversible at room temperature after evacuation of the gas. For the single-component CuPc–4SO3Na film and the composite CuPc–4SO3Na/SnO2 film, the electrical conductivities increase by a factor of 400 and 150, respectively. Upon evacuation of ammonia to the base pressure, the electrical conductivity decreases to the initial values for 1 s. The mechanism of the influence of adsorbed ammonia molecules on the electrical conductivity of the composite material under investigation has been discussed using the model of the formation of the composite sample, according to which the organic component is located in voids between the SnO2 nanoparticles.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.