Transport properties and pinning analysis for Co-doped BaFe2As2 thin films on metal tapes

Abstract

We report on the transport properties and pinning analysis of BaFe1.84Co0.16As2 (Ba122:Co) thin films on metal tapes by pulsed laser deposition. The thin films exhibit a large in-plane misorientation of 5.6°, close to that of the buffer layer SrTiO3 (5.9°). Activation energy U0(H) analysis reveals a power law relationship with field, having three different exponents at different field regions, indicative of variation from single-vortex pinning to a collective flux creep regime. The Ba122:Co coated conductors present = 20.2 K and = 19.0 K along with a self-field Jc of 1.14 MA cm−2 and an in-field Jc as high as 0.98 and 0.86 MA cm−2 up to 9 T at 4.2 K for both major crystallographic directions of the applied field, promising for high field applications. Pinning force analysis indicates a significant enhancement compared with similar Ba122:Co coated conductors. By using the anisotropic scaling approach, intrinsic pinning associated with coupling between superconducting blocks can be identified as the pinning source in the vicinity of H//ab, while for H//c random point defects are likely to play a role but correlated defects start to be active at high temperatures.