Abstract
Hydrogen production by water electrolysis is one of the techniques for establishment of the economy using hydrogen as an energy source. At the present, platinum group elements are used as the electrode catalyst for both anode and cathode in the acid medium, leading to be high initial cost of the water electrolysis system. We recently found that titanium oxiynitride catalyzed activated carbon (TiON/AC) has a low overpotential for hydrogen production in the acidic electrolyte. The overpotential is around 40 mV, which is very low among the catalyst based on the non-noble metals. In this presentation, we report the preparation of TiON/AC and its hydrogen production ability. TiON/AC is successfully obtained through two-steps as loading of titanium dioxide (TiO2) on activated carbon powder and then the nitridation. At first, deposition of TiO2 on the activated carbon was carried out by a modified liquid-phase deposition (LPD) method, in where H3BO3 and (NH4)2TiF6 aqueous solutions were used. A desired amount of activated carbon powder [specific surface area is 2343 m2/g purchased from Kuraray. Co., Ltd.] was added into H3BO3 aqueous solution. Then, (NH4)2TiF6 aqueous solution was added under stirring. The product was mounted in an alumina boat. Subsequent NH3 nitridation was carried out at 700, 750, 800 and 900°C. The characterization was performed by X-ray diffraction (XRD), field emission scanning electron microscope (FE-SEM) and X-ray photoelectron spectroscopy (XPS). To evaluate hydrogen production ability of TiON/AC, the water electrolysis experiment was demonstrated by using 0.5 mol dm-3 of sulfuric acid solution as the electrolyte. The working electrode (cathode) was prepared by TiON/AC carbon paper. A carbon paper and Ag|AgCl were used as the counter and the reference electrode, respectively. Hydrogen was quantified by a gas chromatography during chronoamperometry. Figure 1 shows the XRD patterns before and after NH3 nitridation at 700, 750, 800 and 900oC. Before the nitridation, the diffraction peaks assigned to both the anatase phase of TiO2 and carbon were recognized. After the nitridation at 700oC, the peaks assigned to TiO2, TiN and TiO were appeared. Furthermore, the peaks assigned to TiN and TiO was obvious and the broad peak of carbon was also recognized when the nitridation temperature was over 750oC. In addition, from the XPS results, the formation of Ti-O-N and O-Ti-N bonding were confirmed. Therefore, we considered that the nitridation of TiO2 to TiON was surely happened over 750oC. Figure 2 shows FE-SEM images of the product after the nitridation of 800oC. The tiny particles as 30 nm were found on AC substrate. These particles were considered the products composed of titanium, nitrogen and oxygen. The hydrogen production rate was estimated from the results of gas chromatography. And, its dependency on the overpotential was shown in Figure 3. Hydrogen production was confirmed at overpotential = 0.1 V for the products after the nitridation of 800 and 900oC. The products obtained at 900oC of the nitridation shows the highest hydrogen production rate. This work was partially supported by the Matching Planner Program from Japan Science and Technology Agency , JST and JSPS KAKENHI Grant Number 16K05940. Figure 1
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.