Abstract
Titanium nitride (TiN) films have been used as gate electrodes in metal-oxide-semiconductor (MOS) capacitors, which were fabricated with SiO2 layer as gate dielectric, and as upper electrodes in Schottky diodes on Si substrates. The TiN layer has presented the electrical resistivity of [email protected]@Wcm and poly crystalline structure (Ti2N and TiN phase formation), which were extracted by four probe testing, and, X-ray diffraction and Raman spectroscopy, respectively. To get both MOS and Schottky devices on the same substrate, with TiN/SiO2/Si/Al and TiN/Si/Al structures, respectively, 300nm thick TiN layer was simultaneously deposited by DC sputtering process on SiO2/Si and on Si on the same n-type substrate. The MOS capacitors and Schottky diodes were sintered in conventional furnace in forming gas at 450^oC for different annealing times between 5 and 30min. These devices were electrical characterized by capacitance-voltage (C-V) and current-voltage (I-V) measurements, respectively. With both measurements from capacitors and diodes fabricated on the same substrate, the TiN work function values were extracted, resulting in values between 4.5 and 4.2eV. These values agree with results from literature. Our TiN work function extraction method presents higher accuracy, due to two different measurements were carried out to extract the same parameter, and lower defect incorporation on semiconductor surface can occur, because both devices were fabricated on the same substrate at the same conditions. Furthermore, the distortion in MOS capacitor C-V curve is reduced at 10min of sintering process, indicating that the charge density at TiN/SiO2/Si/Al structures is reduced to one level of 1010cm^-^2. From the I-V curves of Schottky diodes, the ideality factor between 1.0 and 1.5 was extracted. And, these excellent results, such as low charge density of 1010cm^-^2, the ideality factor of 1.0, and work function of 4.2eV, indicates that TiN electrodes can be used for MOS technology and Schottky diode.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.