Abstract
Results of studying the thermoluminescent response of undoped ZrO2 + PTFE pellets irradiated with 90Sr/90Y beta particles are presented. Previously, TL characteristics of ZrO2 films doped with rare earths were studied. Phosphor powder was obtained by evaporating a solution of zirconium nitrate in ethanol. In order to stabilise the traps in ZrO2 this phosphor was submitted to different thermal treatments. Optimal thermal treatment consisted in heating at 1100 degrees C for 24 h. With this powder. pressing at room temperature a mixture (2:1) of ZrO2 and polytetrafluoroethylene (PTFE), pellets of 5 mm diameter and 0.8 mm thickness were made. The glow curve of ZrO2 + PTFE pellets exhibited two peaks at 200 and 250 degrees C: its TL response as a function of beta particles dose was linear in the range from 2 to 60 Gy. Repeatability over 10 cycles was 1.8%. Fading at room temperature was 3.8% per month.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.