The study of dehumidifying of carbon monoxide and ammonia adsorption by Iranian natural clinoptilolite zeolite

Abstract

The natural zeolite (clinoptilolite type) was obtained from the Neibagh region of Mianeh, the city in the west of Iran. The raw zeolite was tested for quality and quantity measurements including surface area and volumetric characteristics as well as thermogravimetry analysis. The acid activation process was used to increase the adsorption rate of zeolite and in order to obtain the optimum conditions: the effect of acid concentration, reaction time and the temperature were studied. A surface area measurement test was performed in each stage to get the best results. Thus, efficient condition was selected according to the produced highest surface area. The reaction was first obtained with hydrochloric acid, and then a comparison was made using the sulfuric acid. The hydrochloric reaction proved to be better. The result of activation was 2.5 times the increase in the surface area in relation to the raw sample. The result of elemental analysis conducted once again on the activated sample showed an increase in the ratio of Si/Al (approximately 0.6). Then, using CO, NH 3 and steam, the gas adsorption capacity of both the raw and activated samples was measured and compared. Since CO was not adsorbed at ambient temperature, but steam was adsorbed relatively well, the natural clinoptilolite zeolite of Iran was suggested as a suitable material for adsorbing humidity form carbon monoxide as well as synthesis gas (H 2 and CO mixture).