Abstract
In this paper, WO3 thin films were implanted by Ar+ ions at 100 keV to the fluences of 1 × 1015 and 1 × 1016 ions/cm2. The electrical conductivity of the implanted samples was measured. Four orders of magnitude increase in the electrical conductivity was observed in the implanted WO3 compared to the pristine WO3. The influence of thermal annealing in vacuum on the electrical conductivity of the implanted samples was also investigated. Thermal annealing further improved the electrical conductivity. X-ray diffraction (XRD), optical image and X-ray photoelectron spectroscopy (XPS) analyses revealed the formation of oxygen vacancy in the implanted sample. It is proposed that the energy levels associated to single charge state of oxygen vacancy serves as donors, improving the electrical conductivity.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.