Abstract
In the present study, an investigation has been carried out on the friction stir welding (FSW) of two magnesium alloys. Hot-rolled and Die-casting plates of AZ type magnesium alloys were successfully joined by friction stir welding. AZ31B-H24 and AZ91C-F plates with the thickness of 4mm were used, and the microstructural development in stir zone (SZ) was investigated using optical and scanning electron microscopes. Hardness of SZ in AZ31B-H24 alloy has been slightly decreased due to the coarse structure. On the other hand, Hardness of SZ in AZ91C-F alloy has been remarkably increased due to very fine recrystallized grain structure. The result of EPMA showed Al Solid solution hardening by Solid solution of β intermetallic compound to α-Mg. While tensile strength of the FSWelded AZ31B-H24 alloy showed about 80% values compare to Base metal, AZ91C-F showed about 68% values due to strongly affected by formation of the intermetallic compounds, β-Al12Mg17.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.