Abstract
The paper reports successful fabrication of CdS/CdTe and ZnS/CdTe heterojunctions by a combination of two different deposition techniques viz. successive ionic layer adsorption and reaction (SILAR) and conventional vacuum deposition. The SILAR deposited CdS and ZnS layers formed well adherent and stable heterojunctions with the vacuum deposited CdTe. The electrical characteristics of the heterojunctions were analyzed by thermionic emission model and Cheung's model. The ideality factor, series resistance, barrier height, space charge density and thickness of the depletion region were determined by rigorous I–V, J-V and C–V characterization. The barrier heights of the devices were found to be in the range of 0.8 eV–0.9 eV. The thickness of the depletion region was found to be 5.2 nm and 7.1 nm while the space charge density was found to be 3.6 × 1022 m−3 and 1.59 × 1021 m-3, respectively, for CdS/CdTe and ZnS/CdTe heterojunctions.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.