Abstract
This article presents the results of experimental tests on the stretch-forming ability of 0.21-mm-thick AW-5052-H28 aluminium alloy sheets used in the production of pull-off cups. Erichsen test under various tribological conditions (dry friction, lubrication with graphite lubricant) was used to assess the sheet formability. Punches with a various diameter of the spherical end (8 and 20 mm) were used in the tests. The effect of soaking conditions and varnishing variants on the value of Erichsen indices IE and IE11 was investigated. The sheets were soaked for 13 minutes at various temperatures: 185°C, 190°C and 200°C. In test conditions without lubrication, the lowest value of the IE index = 3.3 mm was observed for sheets in as-received state and for samples after soaking. However, the highest values of the Erichsen index in tests without lubrication were measured for varnished samples and repeatedly soaked. The tests conducted under lubrication conditions with graphite grease revealed usually higher values of the IE index compared to testing conditions without the use of grease. The values of the IE11 index were approximately twice lower than the IE indices. Observation of the bulge surface revealed a smooth surface, which means that the material is characterised by a fine-grained microstructure.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.