The Domain of Portevin-Le Chatelier Effect in Al-3Mg Alloy

Abstract

An Al-3Mg (wt. %) alloy was studied after equal channel angular pressing and subsequent cold rolling. The mechanical behavior of the alloy in the temperature range from 223 K to 373 K (from –50°C to 125°C) at strain rates 2.1×10–1 – 5.2×10–5 s–1 was investigated. The analysis of stress-strain curves was performed to determine the conditions of manifestation of the Portevin – Le Chatelier (PLC) effect in investigated alloy. The deformation curve at a temperature of 298 K (25°C) and a strain rate of 1×10–3 s–1 is characterized by instability of plastic flow in contrast to the deformation curves obtained under other studied strain rate/temperature conditions. Stress oscillations at the necking stage were observed at high temperatures (>323 K (50°C)) and lower strain rates (1×10–4 s–1 and 5.2×10–5 s–1) forming the left border of the PLC effect domain. In general, deformation curves are characterized by the absence of stress serrations during the uniform elongation.