Abstract
The reduction behavior of a leach residue containing hematite (Fe2O3), nickel ferrite (NiFe2O4) and a small amount of siliceous gangue was studied using thermogravimetric (TG) and differential thermal analysis (DTA) techniques. Carbon monoxide and graphite were used as reductants and a wide range of temperatures were covered. Both non-isothermal reduction (15°C/min) and isothermal reduction tests with continuous measurement of the CO and CO2 evolution were performed to evaluate the temperature dependence of the reduction kinetics. In order to further elucidate the reduction mechanisms, the reduced products were subject to various analyses, i.e. SEM/EDS, XRD, and EPMA. Results show that the reduction rate increased with the increase of temperature when using CO as the reductant. Change of the rate-controlling mechanism from the gaseous diffusion in the pores of the sample bed to the diffusion in the metallic product layer was found to have taken place in the isothermal tests, resulting in the variation of apparent activation energies from 6.7kJ/mol to 41.1kJ/mol with the progress of reduction. The siliceous gangue melted at 1200°C, inhibiting the reduction of the oxides. Effective reduction by graphite only occurred above around 1000°C. Reduction of the molten silicate took place above 1200°C resulting in the formation of Fe–Ni–Si alloys.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.