Abstract
Bioactive glass ceramics (BGC) play a pivotal role in bone tissue engineering, specifically addressing challenges associated with bone repair and regeneration. In this study, we developed silica-based 55S0P and 45S10P spherical BGC nanoparticles (NPs), without and with P2O5 content, using a modified Stöber sol-gel process with base hydrolysis. The fabricated spherical NPs with pronounced textural features effectively contribute to enhanced surface roughness, a desirable parameter for improved biological activity in physiologically relevant solutions and tissue matrices. A comprehensive evaluation of the structural properties of these novel spherical BGC-NPs using diverse characterization techniques revealed distinct nano-textural features in the form of cracks and pores. The HR-TEM confirmed the nanoscale dimensions (170–190 nm) of particles with spherical surface morphology and also systematically analysed via DLS, FE-SEM studies. An augmented surface area with mesopores when phosphate added to the silica glass network was revealed by BET analysis. On the biological front, the study records the formation of an HCA layer on the surfaces of the BGC-NPs, the thickness of which increased with an increase in both phosphate content and immersion time (0, 3, 14 & 28 days) in the SBF solution. The zeta potential values attain a maximum from −22 mV to −23.6 mV for 55S0P and −21.5 mV to −26.4 mV for 45S10P BGC-NPs, and improved with increased immersion time, thereby favouring cellular adhesion for desired biological responses. In vitro, cell culture studies on MG-63 cells, after 24 and 72 h of incubation, demonstrated higher cell adhesion and proliferation, with pronounced biocompatibility. In addition, these BGC-NPs exhibited good hemocompatibility even at the highest test concentration (15 mg/ml) and demonstrated effective antibacterial activity against K. pneumoniae and E. coli. A combinatorial analysis of structural and biological properties revealed that the 45S10P BGC-NPs are more potent than 55S0P BGC-NPs for desired biological performances. In conclusion, the results suggest that the sol-gel fabricated BGC-NPs with enhanced nano-textural features are evidently suitable for applications in bone tissue engineering and regenerative medicine.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.