Abstract
A facile top-down strategy of preparing mesoporous materials directly from natural minerals by selective-etching was proposed. Kaolinite (Al2O3·2SiO2·2H2O), a cheap and abundant clay mineral, was chosen and processed into mesoporous materials with well-defined mesopores (2–6nm) and high specific surface areas (170–430m2/g). In the process, kaolinite was activated by heat-treatment, and then etched by an acid or alkali solution according to its chemical and crystalline features. The activated amorphous alumina or silica component was selectively etched by acid or alkali, respectively, and nanopores were generated in-situ as a result. The pore sizes and specific surface areas can be controlled by the calcination and etching conditions. The as-prepared mesoporous silica and alumina materials showed favorable adsorption abilities towards methylene blue with the monolayer adsorption capacity up to 362mg/g. The template-free preparation of mesoporous materials directly from natural clay minerals may help to promote not only the development of clay products but also the wide application of mesoporous materials with encouraging economic and environmental benefits.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.