TEM Investigations of Titanium Processed by ECAP Followed by Cold Rolling

Abstract

Conventional coarse grained (CG) commercial pure (CP) Ti Grade 2 was studied after cold rolling (CR) at room temperature, and after equal channel angular pressing (ECAP) at 450° C followed by CR, by transmission electron microscopy (TEM) methods. CR of the CG material leads to a microstructure showing initially twins with (0112) type and later subgrains separated by lowangle grain boundaries. CR carried out after ECAP yields the fragmentation of fine grains (300 – 800 nm) mostly bounded by high-angle boundaries into elongated subgrains (~ 100 nm). It was shown with in-situ annealing experiments in the TEM that this microstructure is thermally stable up to a temperature of 450° C. Tensile tests showed that the combination of ECAP with CR has the potential to produce at the same time high strength (941 MPa) and high ductility (16.7%).