Abstract
Fabrication of Cd0.5Zn0.5NdxFe2–xO4 nanoparticles, with x = 0.00, 0.01, 0.02, 0.04, 0.06, and 0.08, has been carried out using a wet chemical co-precipitation method. The effect of the rare earth Nd3+ doping on the prepared ferrites was structurally investigated using x-ray diffraction (XRD) along with Rietveld refinement. The results indicate great crystallinity in the FCC Fd3m spinel structure of Cd0.5Zn0.5NdxFe2–xO4 nanoparticles. The lattice parameter increases with the increase of doping concentration from 8.5378 until 8.5432 Å and the crystallite size obtained using Debye-Sherrer, Williamson–Hall, Size-strain plot (SSP), and Halder-Wagner (H-W) methods, decreases until the solubility limit of the materials is at x = 0.04. By using transmission electron microscopy (TEM), the morphological analysis reveals the spherical shape of the samples with minor agglomeration with the aid of using a Polyvinylpyrrolidone (PVP) capping agent. The grain size ranges from 14.37 to 15.24 nm. Raman spectroscopy verifies the incorporation of Nd3+ in the octahedral sites and the decrease in particle size. The elemental composition was verified using x-ray photoelectron spectroscopy (XPS). The magnetic properties were studied using a vibrating sample magnetometer (VSM) and it shows superparamagnetic behavior with a decrease in the saturation magnetization from 2.207 to 1.918 emu g−1 and an increase in coercivity from 7.194 to 14.397 G. The prepared materials were tested as liquefied petroleum gas (LPG) sensors by studying their sensitivity, selectivity, optimum working temperature, response, and recovery times. Nd3+ doping shows a great increase in LPG sensing sensitivity 4 to 20 times than the pure samples. The doping concentration also decreases the response and recovery times.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.